- W2024574894 endingPage "419" @default.
- W2024574894 startingPage "409" @default.
- W2024574894 abstract "In this study, 5083 aluminum alloys modified with grain refiner, 0.25% Zr and 0.46% Mn, were processed by reciprocating extrusion to yield high-strain-rate superplasticity above 400 °C and superior room-temperature mechanical properties. Without any prior homogenization treatment, 10 extrusion passes could give the cast billets an equiaxed grain structure with a grain size of about 4.5 μm and a subgrain size about 0.2 μm, and a uniform distribution of fine inclusions and dispersoids in the matrix. The fine-grained structure was stable up to 525 °C, giving the alloy a high-strain-rate and low-stress superplasticity over a wide operating temperature of 400–500 °C. In the tensile test at 500 °C, a maximum elongation of 1013% and a low flow stress of 7.7 MPa at 5 × 10−2 s−1 were achieved. The apparent and true activation energies for low temperatures (300–400 °C) without high-strain-rate superplasticity were 220.6 and 208 kJ/mol, respectively, whereas those at high temperatures (400–500 °C) were 88.4 and 98.7 kJ/mol, respectively. Further analysis confirms that grain boundary sliding is the dominant mechanism over the high-strain-rate region from 1 × 10−2 to 5 × 10−1 s−1 at 500 °C, and power-law breakdown mechanism occurs over the strain rate from 5 × 10−4 to 1 × 10−2 s−1 at 300 °C. The high-strain-rate superplasticity was more strongly enhanced by Zr addition than addition of Cr and Mn. Two enhancing mechanisms for the maximum superplastic elongation and the optimum strain rate are proposed. This study concludes that the effectiveness of Zr is caused by the fineness and the coherency of Zr-rich dispersoids in the matrix." @default.
- W2024574894 created "2016-06-24" @default.
- W2024574894 creator A5026954516 @default.
- W2024574894 creator A5054844975 @default.
- W2024574894 date "2007-07-01" @default.
- W2024574894 modified "2023-10-18" @default.
- W2024574894 title "Superplasticity of 5083 alloys with Zr and Mn additions produced by reciprocating extrusion" @default.
- W2024574894 cites W1964265685 @default.
- W2024574894 cites W1965032870 @default.
- W2024574894 cites W1966026336 @default.
- W2024574894 cites W1968575581 @default.
- W2024574894 cites W1972296274 @default.
- W2024574894 cites W1974141446 @default.
- W2024574894 cites W1976129345 @default.
- W2024574894 cites W1980298054 @default.
- W2024574894 cites W1985151083 @default.
- W2024574894 cites W1987472637 @default.
- W2024574894 cites W1990940932 @default.
- W2024574894 cites W1991296081 @default.
- W2024574894 cites W1993982126 @default.
- W2024574894 cites W1998006889 @default.
- W2024574894 cites W1999690443 @default.
- W2024574894 cites W2003377729 @default.
- W2024574894 cites W2004347014 @default.
- W2024574894 cites W2016891789 @default.
- W2024574894 cites W2019207484 @default.
- W2024574894 cites W2019687214 @default.
- W2024574894 cites W2021029258 @default.
- W2024574894 cites W2021150702 @default.
- W2024574894 cites W2026087097 @default.
- W2024574894 cites W2029990139 @default.
- W2024574894 cites W2032274717 @default.
- W2024574894 cites W2036113416 @default.
- W2024574894 cites W2036479805 @default.
- W2024574894 cites W2038370018 @default.
- W2024574894 cites W2040198847 @default.
- W2024574894 cites W2050097038 @default.
- W2024574894 cites W2059875354 @default.
- W2024574894 cites W2072432731 @default.
- W2024574894 cites W2072890145 @default.
- W2024574894 cites W2080470682 @default.
- W2024574894 cites W2082932193 @default.
- W2024574894 cites W2084037957 @default.
- W2024574894 cites W2084551700 @default.
- W2024574894 cites W2088052871 @default.
- W2024574894 cites W2088764470 @default.
- W2024574894 cites W2091198844 @default.
- W2024574894 cites W2116978976 @default.
- W2024574894 cites W2121350967 @default.
- W2024574894 cites W2143522249 @default.
- W2024574894 cites W2148352013 @default.
- W2024574894 cites W2149120080 @default.
- W2024574894 cites W2167906031 @default.
- W2024574894 cites W49994748 @default.
- W2024574894 doi "https://doi.org/10.1016/j.msea.2007.01.121" @default.
- W2024574894 hasPublicationYear "2007" @default.
- W2024574894 type Work @default.
- W2024574894 sameAs 2024574894 @default.
- W2024574894 citedByCount "33" @default.
- W2024574894 countsByYear W20245748942012 @default.
- W2024574894 countsByYear W20245748942013 @default.
- W2024574894 countsByYear W20245748942014 @default.
- W2024574894 countsByYear W20245748942015 @default.
- W2024574894 countsByYear W20245748942016 @default.
- W2024574894 countsByYear W20245748942017 @default.
- W2024574894 countsByYear W20245748942018 @default.
- W2024574894 countsByYear W20245748942019 @default.
- W2024574894 countsByYear W20245748942020 @default.
- W2024574894 countsByYear W20245748942021 @default.
- W2024574894 countsByYear W20245748942022 @default.
- W2024574894 countsByYear W20245748942023 @default.
- W2024574894 crossrefType "journal-article" @default.
- W2024574894 hasAuthorship W2024574894A5026954516 @default.
- W2024574894 hasAuthorship W2024574894A5054844975 @default.
- W2024574894 hasConcept C112950240 @default.
- W2024574894 hasConcept C149342994 @default.
- W2024574894 hasConcept C162611839 @default.
- W2024574894 hasConcept C175997439 @default.
- W2024574894 hasConcept C191897082 @default.
- W2024574894 hasConcept C192191005 @default.
- W2024574894 hasConcept C192562407 @default.
- W2024574894 hasConcept C2776812455 @default.
- W2024574894 hasConcept C2778958987 @default.
- W2024574894 hasConcept C33947775 @default.
- W2024574894 hasConcept C47908070 @default.
- W2024574894 hasConcept C81710450 @default.
- W2024574894 hasConcept C87976508 @default.
- W2024574894 hasConceptScore W2024574894C112950240 @default.
- W2024574894 hasConceptScore W2024574894C149342994 @default.
- W2024574894 hasConceptScore W2024574894C162611839 @default.
- W2024574894 hasConceptScore W2024574894C175997439 @default.
- W2024574894 hasConceptScore W2024574894C191897082 @default.
- W2024574894 hasConceptScore W2024574894C192191005 @default.
- W2024574894 hasConceptScore W2024574894C192562407 @default.
- W2024574894 hasConceptScore W2024574894C2776812455 @default.
- W2024574894 hasConceptScore W2024574894C2778958987 @default.
- W2024574894 hasConceptScore W2024574894C33947775 @default.
- W2024574894 hasConceptScore W2024574894C47908070 @default.