- W2026703105 abstract "Porous alumina ceramics with unidirectionally-oriented pores were prepared by extrusion. Carbon fibers of 14 μm diameter and 600 μm length to be used as the pore-forming agent were kneaded with alumina, binder and dispersing agent. The resulting paste was extruded, dried at 110 °C, degreased at 1000 °C and fired at 1600 °C for 2 h. SEM showed a microstructure of dispersed highly oriented pores in a dense alumina matrix. The pore area in the cross section was 25.3% with about 1700 pores/mm2. The pore size distribution of the fired body measured by Hg porosimetry showed a sharp peak corresponding to the diameter of the burnt-out carbon fibers. The resulting porous alumina ceramics with 38% total porosity showed a fracture strength of 171 MPa and a Young's modulus of 132 GPa. This strength is significantly higher than the reported value for other porous alumina ceramics even though the present pore size is much larger." @default.
- W2026703105 created "2016-06-24" @default.
- W2026703105 creator A5054746271 @default.
- W2026703105 creator A5072950026 @default.
- W2026703105 creator A5079298506 @default.
- W2026703105 creator A5086405055 @default.
- W2026703105 creator A5090765558 @default.
- W2026703105 date "2006-01-01" @default.
- W2026703105 modified "2023-10-17" @default.
- W2026703105 title "Preparation and properties of porous alumina ceramics with oriented cylindrical pores produced by an extrusion method" @default.
- W2026703105 cites W1968657302 @default.
- W2026703105 cites W1970643541 @default.
- W2026703105 cites W1972865181 @default.
- W2026703105 cites W1976421564 @default.
- W2026703105 cites W2017899903 @default.
- W2026703105 cites W2020994776 @default.
- W2026703105 cites W2031750630 @default.
- W2026703105 cites W204058272 @default.
- W2026703105 cites W2078720778 @default.
- W2026703105 cites W2110260233 @default.
- W2026703105 cites W2125336698 @default.
- W2026703105 cites W2140632415 @default.
- W2026703105 cites W2141141511 @default.
- W2026703105 cites W2156789104 @default.
- W2026703105 cites W2158210438 @default.
- W2026703105 cites W2323845995 @default.
- W2026703105 cites W2325605436 @default.
- W2026703105 cites W2326169427 @default.
- W2026703105 doi "https://doi.org/10.1016/j.jeurceramsoc.2004.11.015" @default.
- W2026703105 hasPublicationYear "2006" @default.
- W2026703105 type Work @default.
- W2026703105 sameAs 2026703105 @default.
- W2026703105 citedByCount "94" @default.
- W2026703105 countsByYear W20267031052012 @default.
- W2026703105 countsByYear W20267031052013 @default.
- W2026703105 countsByYear W20267031052014 @default.
- W2026703105 countsByYear W20267031052015 @default.
- W2026703105 countsByYear W20267031052016 @default.
- W2026703105 countsByYear W20267031052017 @default.
- W2026703105 countsByYear W20267031052018 @default.
- W2026703105 countsByYear W20267031052019 @default.
- W2026703105 countsByYear W20267031052020 @default.
- W2026703105 countsByYear W20267031052021 @default.
- W2026703105 countsByYear W20267031052022 @default.
- W2026703105 countsByYear W20267031052023 @default.
- W2026703105 crossrefType "journal-article" @default.
- W2026703105 hasAuthorship W2026703105A5054746271 @default.
- W2026703105 hasAuthorship W2026703105A5072950026 @default.
- W2026703105 hasAuthorship W2026703105A5079298506 @default.
- W2026703105 hasAuthorship W2026703105A5086405055 @default.
- W2026703105 hasAuthorship W2026703105A5090765558 @default.
- W2026703105 hasConcept C105569014 @default.
- W2026703105 hasConcept C114873805 @default.
- W2026703105 hasConcept C134132462 @default.
- W2026703105 hasConcept C159985019 @default.
- W2026703105 hasConcept C192562407 @default.
- W2026703105 hasConcept C193867417 @default.
- W2026703105 hasConcept C2778958987 @default.
- W2026703105 hasConcept C3019071265 @default.
- W2026703105 hasConcept C6648577 @default.
- W2026703105 hasConcept C87976508 @default.
- W2026703105 hasConceptScore W2026703105C105569014 @default.
- W2026703105 hasConceptScore W2026703105C114873805 @default.
- W2026703105 hasConceptScore W2026703105C134132462 @default.
- W2026703105 hasConceptScore W2026703105C159985019 @default.
- W2026703105 hasConceptScore W2026703105C192562407 @default.
- W2026703105 hasConceptScore W2026703105C193867417 @default.
- W2026703105 hasConceptScore W2026703105C2778958987 @default.
- W2026703105 hasConceptScore W2026703105C3019071265 @default.
- W2026703105 hasConceptScore W2026703105C6648577 @default.
- W2026703105 hasConceptScore W2026703105C87976508 @default.
- W2026703105 hasIssue "6" @default.
- W2026703105 hasLocation W20267031051 @default.
- W2026703105 hasOpenAccess W2026703105 @default.
- W2026703105 hasPrimaryLocation W20267031051 @default.
- W2026703105 hasRelatedWork W1568987576 @default.
- W2026703105 hasRelatedWork W1588506368 @default.
- W2026703105 hasRelatedWork W179177257 @default.
- W2026703105 hasRelatedWork W2084035109 @default.
- W2026703105 hasRelatedWork W2343807156 @default.
- W2026703105 hasRelatedWork W2358796993 @default.
- W2026703105 hasRelatedWork W2496922396 @default.
- W2026703105 hasRelatedWork W3042576019 @default.
- W2026703105 hasRelatedWork W4318950781 @default.
- W2026703105 hasRelatedWork W1596514690 @default.
- W2026703105 hasVolume "26" @default.
- W2026703105 isParatext "false" @default.
- W2026703105 isRetracted "false" @default.
- W2026703105 magId "2026703105" @default.
- W2026703105 workType "article" @default.