• W2030403962 abstract "Ti–47Al–2Nb–2Cr–0.15B (at%) alloy was brazed with an amorphous Ti–25.65Zr–13.3Cu–12.35Ni–3Co–2Mo (wt%) alloy foil in vacuum furnace. The effects of brazing temperature and testing temperature on the interfacial microstructure and mechanical property of the TiAl joints were investigated in detail. Sound TiAl brazed joints are obtained at brazing temperature of 925–1050 °C for 5 min. The joint is mainly composed of two zones, and the intermetallic phases in the joint are (Ti, Zr)2, (Cu, Ni) and Ti3Al. The brazing temperature has a significant effect on the interfacial microstructure of the TiAl joint. The room temperature shear strength of the joint first increases and then decreases with the brazing temperature. The highest room temperature shear strength of the joint is 211 MPa when the TiAl alloys were brazed at 1000 °C for 5 min. The shear strength decreases with the testing temperature and maintains above 155 MPa at a temperature below 700 °C. However, solid-state diffusion and serious oxidation in the central brazed layer II lead to the sharp reduction of the joint shear strength when the testing temperature exceeds 700 °C. All the failures of the joints occur in the central brazed layer II and the (Ti, Zr)2 (Cu, Ni) intermetallic compounds occupy most of the fracture surfaces." @default.
• W2030403962 created "2016-06-24" @default.
• W2030403962 creator A5014335750 @default.
• W2030403962 creator A5017215030 @default.
• W2030403962 creator A5024933708 @default.
• W2030403962 creator A5027475930 @default.
• W2030403962 creator A5067379174 @default.
• W2030403962 creator A5088467528 @default.
• W2030403962 date "2015-05-01" @default.
• W2030403962 modified "2023-09-30" @default.
• W2030403962 title "Effects of brazing temperature and testing temperature on the microstructure and shear strength of γ-TiAl joints" @default.
• W2030403962 cites W1676101252 @default.
• W2030403962 cites W1965148666 @default.
• W2030403962 cites W1965199165 @default.
• W2030403962 cites W1965806307 @default.
• W2030403962 cites W1973951752 @default.
• W2030403962 cites W1986825520 @default.
• W2030403962 cites W1994702250 @default.
• W2030403962 cites W1995000115 @default.
• W2030403962 cites W1995359807 @default.
• W2030403962 cites W1995617469 @default.
• W2030403962 cites W2007706311 @default.
• W2030403962 cites W2026533324 @default.
• W2030403962 cites W2030216430 @default.
• W2030403962 cites W2048079133 @default.
• W2030403962 cites W2048543240 @default.
• W2030403962 cites W2050635176 @default.
• W2030403962 cites W2059346919 @default.
• W2030403962 cites W2067210438 @default.
• W2030403962 cites W2068507082 @default.
• W2030403962 cites W2069066973 @default.
• W2030403962 cites W2071257342 @default.
• W2030403962 cites W2071659350 @default.
• W2030403962 cites W2091187115 @default.
• W2030403962 cites W2092034473 @default.
• W2030403962 cites W2094804014 @default.
• W2030403962 cites W2099246830 @default.
• W2030403962 cites W2106619382 @default.
• W2030403962 cites W2114682068 @default.
• W2030403962 cites W2120399389 @default.
• W2030403962 doi "https://doi.org/10.1016/j.msea.2015.03.039" @default.
• W2030403962 hasPublicationYear "2015" @default.
• W2030403962 type Work @default.
• W2030403962 sameAs 2030403962 @default.
• W2030403962 citedByCount "29" @default.
• W2030403962 countsByYear W20304039622015 @default.
• W2030403962 countsByYear W20304039622016 @default.
• W2030403962 countsByYear W20304039622017 @default.
• W2030403962 countsByYear W20304039622018 @default.
• W2030403962 countsByYear W20304039622019 @default.
• W2030403962 countsByYear W20304039622020 @default.
• W2030403962 countsByYear W20304039622021 @default.
• W2030403962 countsByYear W20304039622022 @default.
• W2030403962 countsByYear W20304039622023 @default.
• W2030403962 crossrefType "journal-article" @default.
• W2030403962 hasAuthorship W2030403962A5014335750 @default.
• W2030403962 hasAuthorship W2030403962A5017215030 @default.
• W2030403962 hasAuthorship W2030403962A5024933708 @default.
• W2030403962 hasAuthorship W2030403962A5027475930 @default.
• W2030403962 hasAuthorship W2030403962A5067379174 @default.
• W2030403962 hasAuthorship W2030403962A5088467528 @default.
• W2030403962 hasConcept C127413603 @default.
• W2030403962 hasConcept C127893833 @default.
• W2030403962 hasConcept C159390177 @default.
• W2030403962 hasConcept C159750122 @default.
• W2030403962 hasConcept C159985019 @default.
• W2030403962 hasConcept C170154142 @default.
• W2030403962 hasConcept C18555067 @default.
• W2030403962 hasConcept C191897082 @default.
• W2030403962 hasConcept C192562407 @default.
• W2030403962 hasConcept C27501479 @default.
• W2030403962 hasConcept C2780026712 @default.
• W2030403962 hasConcept C39432304 @default.
• W2030403962 hasConcept C41151612 @default.
• W2030403962 hasConcept C7363328 @default.
• W2030403962 hasConcept C86171150 @default.
• W2030403962 hasConcept C87976508 @default.
• W2030403962 hasConcept C96035792 @default.
• W2030403962 hasConceptScore W2030403962C127413603 @default.
• W2030403962 hasConceptScore W2030403962C127893833 @default.
• W2030403962 hasConceptScore W2030403962C159390177 @default.
• W2030403962 hasConceptScore W2030403962C159750122 @default.
• W2030403962 hasConceptScore W2030403962C159985019 @default.
• W2030403962 hasConceptScore W2030403962C170154142 @default.
• W2030403962 hasConceptScore W2030403962C18555067 @default.
• W2030403962 hasConceptScore W2030403962C191897082 @default.
• W2030403962 hasConceptScore W2030403962C192562407 @default.
• W2030403962 hasConceptScore W2030403962C27501479 @default.
• W2030403962 hasConceptScore W2030403962C2780026712 @default.
• W2030403962 hasConceptScore W2030403962C39432304 @default.
• W2030403962 hasConceptScore W2030403962C41151612 @default.
• W2030403962 hasConceptScore W2030403962C7363328 @default.
• W2030403962 hasConceptScore W2030403962C86171150 @default.
• W2030403962 hasConceptScore W2030403962C87976508 @default.
• W2030403962 hasConceptScore W2030403962C96035792 @default.
• W2030403962 hasLocation W20304039621 @default.
• W2030403962 hasOpenAccess W2030403962 @default.
• W2030403962 hasPrimaryLocation W20304039621 @default.

• next