- W2031137421 abstract "In order to safely use precipitation strengthening type A286 stainless steel in high cycles, the fundamental fatigue strength characteristics were investigated using fatigue tests at room temperature. During the fatigue test, the author paid attention to the behaviour of small fatigue cracks in order to clarify the fatigue strength properties in more detail than the usual fatigue test. As a result of the fatigue test, the fatigue strength characteristic of the A286 steel became clarified as shown below. The fatigue strength ratio of the A286 steel is lower than 0.5 which is the ratio value of most steels. The cracks propagate which result in a failure even after 107 cycles. It was found that there are two crack mechanisms propagation of the A286 steel; i.e., in a high load-stress, the cracks monotonously propagate and result in failure. Under a low load-stress, the cracks intermittently propagate even after 107 cycles. The non-propagating cracks coalesce with a new crack which initiates near the crack tip and it becomes longer, finally resulting in a failure. This is the reason why the fatigue failures occur even after 107 cycles." @default.
- W2031137421 created "2016-06-24" @default.
- W2031137421 creator A5044845081 @default.
- W2031137421 creator A5053884387 @default.
- W2031137421 creator A5059439606 @default.
- W2031137421 date "2011-01-01" @default.
- W2031137421 modified "2023-09-26" @default.
- W2031137421 title "Fatigue strength properties of precipitation strengthening stainless steel A286 focused attention on small fatigue crack behaviour" @default.
- W2031137421 cites W2012814637 @default.
- W2031137421 cites W2013107117 @default.
- W2031137421 cites W2038937427 @default.
- W2031137421 cites W2076613441 @default.
- W2031137421 cites W2117608490 @default.
- W2031137421 cites W2156955737 @default.
- W2031137421 doi "https://doi.org/10.1016/j.proeng.2011.04.327" @default.
- W2031137421 hasPublicationYear "2011" @default.
- W2031137421 type Work @default.
- W2031137421 sameAs 2031137421 @default.
- W2031137421 citedByCount "7" @default.
- W2031137421 countsByYear W20311374212012 @default.
- W2031137421 countsByYear W20311374212013 @default.
- W2031137421 countsByYear W20311374212018 @default.
- W2031137421 countsByYear W20311374212023 @default.
- W2031137421 crossrefType "journal-article" @default.
- W2031137421 hasAuthorship W2031137421A5044845081 @default.
- W2031137421 hasAuthorship W2031137421A5053884387 @default.
- W2031137421 hasAuthorship W2031137421A5059439606 @default.
- W2031137421 hasBestOaLocation W20311374211 @default.
- W2031137421 hasConcept C1147972 @default.
- W2031137421 hasConcept C127413603 @default.
- W2031137421 hasConcept C131850400 @default.
- W2031137421 hasConcept C138885662 @default.
- W2031137421 hasConcept C159985019 @default.
- W2031137421 hasConcept C192562407 @default.
- W2031137421 hasConcept C21036866 @default.
- W2031137421 hasConcept C28539199 @default.
- W2031137421 hasConcept C2985278600 @default.
- W2031137421 hasConcept C41895202 @default.
- W2031137421 hasConcept C59085676 @default.
- W2031137421 hasConcept C66938386 @default.
- W2031137421 hasConcept C75512024 @default.
- W2031137421 hasConceptScore W2031137421C1147972 @default.
- W2031137421 hasConceptScore W2031137421C127413603 @default.
- W2031137421 hasConceptScore W2031137421C131850400 @default.
- W2031137421 hasConceptScore W2031137421C138885662 @default.
- W2031137421 hasConceptScore W2031137421C159985019 @default.
- W2031137421 hasConceptScore W2031137421C192562407 @default.
- W2031137421 hasConceptScore W2031137421C21036866 @default.
- W2031137421 hasConceptScore W2031137421C28539199 @default.
- W2031137421 hasConceptScore W2031137421C2985278600 @default.
- W2031137421 hasConceptScore W2031137421C41895202 @default.
- W2031137421 hasConceptScore W2031137421C59085676 @default.
- W2031137421 hasConceptScore W2031137421C66938386 @default.
- W2031137421 hasConceptScore W2031137421C75512024 @default.
- W2031137421 hasLocation W20311374211 @default.
- W2031137421 hasOpenAccess W2031137421 @default.
- W2031137421 hasPrimaryLocation W20311374211 @default.
- W2031137421 hasRelatedWork W164291226 @default.
- W2031137421 hasRelatedWork W1993495133 @default.
- W2031137421 hasRelatedWork W2031927898 @default.
- W2031137421 hasRelatedWork W2069894571 @default.
- W2031137421 hasRelatedWork W2333337162 @default.
- W2031137421 hasRelatedWork W2365436309 @default.
- W2031137421 hasRelatedWork W2528637474 @default.
- W2031137421 hasRelatedWork W592764403 @default.
- W2031137421 hasRelatedWork W639842310 @default.
- W2031137421 hasRelatedWork W1929586317 @default.
- W2031137421 hasVolume "10" @default.
- W2031137421 isParatext "false" @default.
- W2031137421 isRetracted "false" @default.
- W2031137421 magId "2031137421" @default.
- W2031137421 workType "article" @default.