- W2031609599 abstract "Amorphous AlN films deposited by sputtering using electron cyclotron resonance (ECR) plasma were used to form AlN/n-InP metal–insulator–semiconductor diodes. The AlN films were deposited without substrate heating. Capacitance–voltage ( C – V ) measurements showed a small hysteresis window of ∼35 mV for a 2-nm-thick AlN film, and frequency dispersion was much improved by post-deposition annealing at 200°C in an H 2 gas atmosphere. We estimated the interface-trap density to be 3×10 12 cm -2 eV -1 by comparing 10-kHz and 1-MHz C – V curves. Small leakage currents of less than 2 mA/cm 2 at a bias voltage of 1 V were obtained for the 2-nm-thick film. To clarify the effect of the deposition methods, AlN films were deposited by conventional magnetron sputtering. ECR sputtering provided better C – V and current-voltage characteristics than magnetron sputtering for as-deposited AlN films, showing that good metal–insulator–semiconductor (MIS) properties arise because of the suitable deposition method and the good combination of materials. An analysis of surface atoms on the InP substrate by secondary ion mass spectrometry showed a large oxygen concentration on the order of 10 22 cm -3 , which is not preferable for MIS diode properties. Surface cleaning using dilute HF reduced oxygen and carbon concentrations to less than half." @default.
- W2031609599 created "2016-06-24" @default.
- W2031609599 creator A5010122688 @default.
- W2031609599 creator A5044752584 @default.
- W2031609599 creator A5071525464 @default.
- W2031609599 creator A5074657713 @default.
- W2031609599 creator A5077280543 @default.
- W2031609599 date "2005-01-01" @default.
- W2031609599 modified "2023-09-24" @default.
- W2031609599 title "Al/AlN/InP Metal-Insulator-Semiconductor-Diode Characteristics with Amorphous AlN Films Deposited by Electron-Cyclotron-Resonance Sputtering" @default.
- W2031609599 cites W1669819412 @default.
- W2031609599 cites W2000146482 @default.
- W2031609599 cites W2001573824 @default.
- W2031609599 cites W2003772790 @default.
- W2031609599 cites W2005018318 @default.
- W2031609599 cites W2023091914 @default.
- W2031609599 cites W2026688714 @default.
- W2031609599 cites W2042556875 @default.
- W2031609599 cites W2047559449 @default.
- W2031609599 cites W2060784350 @default.
- W2031609599 cites W2094485367 @default.
- W2031609599 cites W2106619646 @default.
- W2031609599 doi "https://doi.org/10.1143/jjap.44.334" @default.
- W2031609599 hasPublicationYear "2005" @default.
- W2031609599 type Work @default.
- W2031609599 sameAs 2031609599 @default.
- W2031609599 citedByCount "12" @default.
- W2031609599 countsByYear W20316095992012 @default.
- W2031609599 countsByYear W20316095992018 @default.
- W2031609599 crossrefType "journal-article" @default.
- W2031609599 hasAuthorship W2031609599A5010122688 @default.
- W2031609599 hasAuthorship W2031609599A5044752584 @default.
- W2031609599 hasAuthorship W2031609599A5071525464 @default.
- W2031609599 hasAuthorship W2031609599A5074657713 @default.
- W2031609599 hasAuthorship W2031609599A5077280543 @default.
- W2031609599 hasConcept C113196181 @default.
- W2031609599 hasConcept C145148216 @default.
- W2031609599 hasConcept C171250308 @default.
- W2031609599 hasConcept C175361016 @default.
- W2031609599 hasConcept C178790620 @default.
- W2031609599 hasConcept C185592680 @default.
- W2031609599 hasConcept C19067145 @default.
- W2031609599 hasConcept C192562407 @default.
- W2031609599 hasConcept C22423302 @default.
- W2031609599 hasConcept C43617362 @default.
- W2031609599 hasConcept C49040817 @default.
- W2031609599 hasConcept C56052488 @default.
- W2031609599 hasConcept C61427134 @default.
- W2031609599 hasConcept C78434282 @default.
- W2031609599 hasConceptScore W2031609599C113196181 @default.
- W2031609599 hasConceptScore W2031609599C145148216 @default.
- W2031609599 hasConceptScore W2031609599C171250308 @default.
- W2031609599 hasConceptScore W2031609599C175361016 @default.
- W2031609599 hasConceptScore W2031609599C178790620 @default.
- W2031609599 hasConceptScore W2031609599C185592680 @default.
- W2031609599 hasConceptScore W2031609599C19067145 @default.
- W2031609599 hasConceptScore W2031609599C192562407 @default.
- W2031609599 hasConceptScore W2031609599C22423302 @default.
- W2031609599 hasConceptScore W2031609599C43617362 @default.
- W2031609599 hasConceptScore W2031609599C49040817 @default.
- W2031609599 hasConceptScore W2031609599C56052488 @default.
- W2031609599 hasConceptScore W2031609599C61427134 @default.
- W2031609599 hasConceptScore W2031609599C78434282 @default.
- W2031609599 hasIssue "1R" @default.
- W2031609599 hasLocation W20316095991 @default.
- W2031609599 hasOpenAccess W2031609599 @default.
- W2031609599 hasPrimaryLocation W20316095991 @default.
- W2031609599 hasRelatedWork W154104228 @default.
- W2031609599 hasRelatedWork W1963504437 @default.
- W2031609599 hasRelatedWork W1968373997 @default.
- W2031609599 hasRelatedWork W1976243357 @default.
- W2031609599 hasRelatedWork W1986989277 @default.
- W2031609599 hasRelatedWork W2086744665 @default.
- W2031609599 hasRelatedWork W2384986301 @default.
- W2031609599 hasRelatedWork W2571385234 @default.
- W2031609599 hasRelatedWork W2735408399 @default.
- W2031609599 hasRelatedWork W137487168 @default.
- W2031609599 hasVolume "44" @default.
- W2031609599 isParatext "false" @default.
- W2031609599 isRetracted "false" @default.
- W2031609599 magId "2031609599" @default.
- W2031609599 workType "article" @default.