- W2031684470 abstract "Silicate gels were prepared by mixing K2O•3.9SiO2 (0.3 mol/L) and Al(NO3)3•9H2O (1 mol/L) solutions in various ratios, using potassium hydroxide solution (1 mol/L) to regulate the pH. Nine gel samples were thus prepared at a range of pH conditions, filtered, washed and air-dried. About 1 mol% of potassium was incorporated into the gels at low pH, but up to 20 mol% was incorporated under high pH conditions. On heating, characteristic DTA exotherms were observed at higher temperatures, possibly providing an indication of the degree of polymerization of the gels. The low-potassium gels exhibited a sharp exothermic peak at about 1000°C corresponding to mullite formation, whereas the high-potassium gels exhibited a small, gentle exotherm at about 1000-1100°C corresponding to the formation of KAlSiO4 (PAS, considered to be one of the modifications of kalsilite) and/or KAlSi2O6 (leucite), depending on the gel composition. The 29Si and 27Al MAS-NMR spectra showed that the potassium-poor gels contain predominantly tetrahedral Si(1-2Al) and Q1 silicate units, and both tetrahedral and octahedral Al3+, whereas the potassium-rich gels contain predominantly Si(4Al) units and solely tetrahedral Al3+. The implications of these results for the formation of potassium geopolymers are discussed." @default.
- W2031684470 created "2016-06-24" @default.
- W2031684470 creator A5001716856 @default.
- W2031684470 creator A5025193101 @default.
- W2031684470 creator A5035998684 @default.
- W2031684470 creator A5039244389 @default.
- W2031684470 creator A5063493600 @default.
- W2031684470 creator A5063947162 @default.
- W2031684470 creator A5065113472 @default.
- W2031684470 date "2006-01-01" @default.
- W2031684470 modified "2023-10-16" @default.
- W2031684470 title "Effect of Synthesis pH on the Preparation and Properties of K-Al-Bearing Silicate Gels from Solution" @default.
- W2031684470 cites W1966457008 @default.
- W2031684470 cites W1982870960 @default.
- W2031684470 cites W1992469583 @default.
- W2031684470 cites W2014519729 @default.
- W2031684470 cites W2041687619 @default.
- W2031684470 cites W2043164424 @default.
- W2031684470 cites W2090380346 @default.
- W2031684470 cites W2114711884 @default.
- W2031684470 cites W2131291757 @default.
- W2031684470 cites W2334926235 @default.
- W2031684470 doi "https://doi.org/10.2109/jcersj.114.624" @default.
- W2031684470 hasPublicationYear "2006" @default.
- W2031684470 type Work @default.
- W2031684470 sameAs 2031684470 @default.
- W2031684470 citedByCount "15" @default.
- W2031684470 countsByYear W20316844702013 @default.
- W2031684470 countsByYear W20316844702016 @default.
- W2031684470 countsByYear W20316844702018 @default.
- W2031684470 countsByYear W20316844702021 @default.
- W2031684470 crossrefType "journal-article" @default.
- W2031684470 hasAuthorship W2031684470A5001716856 @default.
- W2031684470 hasAuthorship W2031684470A5025193101 @default.
- W2031684470 hasAuthorship W2031684470A5035998684 @default.
- W2031684470 hasAuthorship W2031684470A5039244389 @default.
- W2031684470 hasAuthorship W2031684470A5063493600 @default.
- W2031684470 hasAuthorship W2031684470A5063947162 @default.
- W2031684470 hasAuthorship W2031684470A5065113472 @default.
- W2031684470 hasBestOaLocation W20316844701 @default.
- W2031684470 hasConcept C134132462 @default.
- W2031684470 hasConcept C13965031 @default.
- W2031684470 hasConcept C178790620 @default.
- W2031684470 hasConcept C179104552 @default.
- W2031684470 hasConcept C185592680 @default.
- W2031684470 hasConcept C2776685566 @default.
- W2031684470 hasConcept C2777335606 @default.
- W2031684470 hasConcept C2779439175 @default.
- W2031684470 hasConcept C2780049689 @default.
- W2031684470 hasConcept C2781436864 @default.
- W2031684470 hasConcept C44228677 @default.
- W2031684470 hasConcept C517785266 @default.
- W2031684470 hasConcept C521977710 @default.
- W2031684470 hasConceptScore W2031684470C134132462 @default.
- W2031684470 hasConceptScore W2031684470C13965031 @default.
- W2031684470 hasConceptScore W2031684470C178790620 @default.
- W2031684470 hasConceptScore W2031684470C179104552 @default.
- W2031684470 hasConceptScore W2031684470C185592680 @default.
- W2031684470 hasConceptScore W2031684470C2776685566 @default.
- W2031684470 hasConceptScore W2031684470C2777335606 @default.
- W2031684470 hasConceptScore W2031684470C2779439175 @default.
- W2031684470 hasConceptScore W2031684470C2780049689 @default.
- W2031684470 hasConceptScore W2031684470C2781436864 @default.
- W2031684470 hasConceptScore W2031684470C44228677 @default.
- W2031684470 hasConceptScore W2031684470C517785266 @default.
- W2031684470 hasConceptScore W2031684470C521977710 @default.
- W2031684470 hasIssue "1331" @default.
- W2031684470 hasLocation W20316844701 @default.
- W2031684470 hasOpenAccess W2031684470 @default.
- W2031684470 hasPrimaryLocation W20316844701 @default.
- W2031684470 hasRelatedWork W145761977 @default.
- W2031684470 hasRelatedWork W1998760060 @default.
- W2031684470 hasRelatedWork W2026391925 @default.
- W2031684470 hasRelatedWork W2033707383 @default.
- W2031684470 hasRelatedWork W2041328207 @default.
- W2031684470 hasRelatedWork W2167582997 @default.
- W2031684470 hasRelatedWork W2371380694 @default.
- W2031684470 hasRelatedWork W2391858193 @default.
- W2031684470 hasRelatedWork W2966337655 @default.
- W2031684470 hasRelatedWork W3173728004 @default.
- W2031684470 hasVolume "114" @default.
- W2031684470 isParatext "false" @default.
- W2031684470 isRetracted "false" @default.
- W2031684470 magId "2031684470" @default.
- W2031684470 workType "article" @default.