- W2032074920 abstract "High-purity niobium and tantalum single crystals having orientations in the central part of the stereographic triangle and a residual resistance ratio RRR of better than 5500:1 are deformed in tension, compression, and by cyclic deformation at temperatures below ambient. The deformation behaviour is studied by observation of the slip-line morphology, Laue X-ray backreflection, X-ray topography, and transmission electon microscopy (TEM). Anomalous (011) slip is observed at temperatures below about 200 K for the niobium crystals and at liquid nitrogen temperatures for the tantalum crystals, respectively. The influence of the specimen purity on the appearance of the anomalous slip is investigated by etching experiments: for example, etching in an acid solution subsequently suppresses anomalous slip in the tantalum specimens owing to the influence of hydrogen interstitials. Prestraining of the specimens has different effects on the appearance of the anomalous slip, depending on the temperature and the mode of the predeformation: anomalous slip is generally suppressed by prestraining unless the specimens are predeformed into stage I of the three-stage work-hardening curve at the appropriate temperatures. The TEM investigations reveal that the dislocation arrangement consists of regular networks of screw dislocations with primary and conjugate Burgers vectors, lying in the anomalous slip plane. The X-ray topography investigations demonstrate that twist walls of alternating signs are built up during anomalous slip. The separation of two adjacent twist walls of alternating signs corresponds to the separation of the anomalous slip lines on the crystal surfaces. From the angle of twist the density of the excess dislocations in the twist walls is estimated to be about 3% of the total dislocation density. Hochreine, mittelorientierte Niob- und Tantaleinkristalle mit einem Restwiderstandsverhältnis von besser als 5500:1 werden im Zugversuch, Druckversuch und durch Wechselverformung bei Temperaturen unterhalb von Raumtemperatur verformt. Das Verformungsverhalten wird mit Hilfe von Gleitlinienbeobachtungen, Laue-Rückstrahlaufnahmen, Berg-Barrett Röntgentopographie und Durch-strahlungselektronenmikroskopie untersucht. Bei den Niobeinkristallen wird bei Verformungstemperaturen kleiner als etwa 200 K die sogenannte anomale Gleitung auf (011) Ebenen gefunden. Dagegen tritt sie bei den Tantaleinkristallen erst nach Verformung bei Stickstofftemperatur auf. Der Einfluß der Probenreinheit auf das Auftreten von anomaler Gleitung wird mit Hilfe von Ätzexperimenten untersucht. Infolge des Einflusses von Wasserstoff-Zwischengitteratomen wird die anomale Gleitung bei Tantal nach Ätzen in einer Säurelösung unterdrückt. Vorverformen von Proben wirkt sich auf verschiedene Weise auf das Auftreten der anomalen Gleitung aus, abhängig von der Temperatur und der Art des Verformens. Im allgemeinen wird die anomale Gleitung bei vorverformten Kristallen unterdrückt, sofern die Proben nicht bei der „richtigen”︁ Temperatur bis in Stufe I der Verfestigungskurve vorverformt wurden. Die Untersuchungen mittels Durchstrahlungselek tronenmik roskopie ergeben, daß die Versetzungsanordnung aus regelmäßigen Netzwerken von Schraubenversetzungen mit primären und konjugierten Burgers-Vektoren besteht, die in anomalen (011) Ebenen liegen. Die Berg-Barrett-Röntgentopographie-Untersuchungen zeigen, daß während der anomalen Gleitung Drillwände mit alternierenden Vorzeichen aufgebaut werden. Dabei entspricht der Abstand zweier benachbarter Drillwände dem Abstand der anomalen Gleitlinien auf der Kristalloberfläche. Aus der Größe des Drillwinkels wird die Dichte der überschüssigen Versetzungen in den Drillwänden auf etwa 3% der Gesamtversetzungsdichte geschätzt." @default.
- W2032074920 created "2016-06-24" @default.
- W2032074920 creator A5090763210 @default.
- W2032074920 date "1995-02-16" @default.
- W2032074920 modified "2023-09-23" @default.
- W2032074920 title "Anomalous Slip in High-Purity Niobium and Tantalum Single Crystals" @default.
- W2032074920 cites W1664898154 @default.
- W2032074920 cites W1967499752 @default.
- W2032074920 cites W1968619906 @default.
- W2032074920 cites W1968949501 @default.
- W2032074920 cites W1977092816 @default.
- W2032074920 cites W1980391527 @default.
- W2032074920 cites W1991293310 @default.
- W2032074920 cites W1991833339 @default.
- W2032074920 cites W1994970542 @default.
- W2032074920 cites W1998321185 @default.
- W2032074920 cites W1999252130 @default.
- W2032074920 cites W2002308253 @default.
- W2032074920 cites W2002717217 @default.
- W2032074920 cites W2005974625 @default.
- W2032074920 cites W2006419907 @default.
- W2032074920 cites W2011486289 @default.
- W2032074920 cites W2013080649 @default.
- W2032074920 cites W2013629000 @default.
- W2032074920 cites W2013901374 @default.
- W2032074920 cites W2018335159 @default.
- W2032074920 cites W2018424517 @default.
- W2032074920 cites W2018431230 @default.
- W2032074920 cites W2023236330 @default.
- W2032074920 cites W2029541269 @default.
- W2032074920 cites W2036463198 @default.
- W2032074920 cites W2043790020 @default.
- W2032074920 cites W2046238277 @default.
- W2032074920 cites W2052483652 @default.
- W2032074920 cites W2056126413 @default.
- W2032074920 cites W2056809074 @default.
- W2032074920 cites W2057785574 @default.
- W2032074920 cites W2067905412 @default.
- W2032074920 cites W2074327980 @default.
- W2032074920 cites W2077453740 @default.
- W2032074920 cites W2077685593 @default.
- W2032074920 cites W2079852689 @default.
- W2032074920 cites W2080157473 @default.
- W2032074920 cites W2083275377 @default.
- W2032074920 cites W2083721011 @default.
- W2032074920 cites W2127707569 @default.
- W2032074920 cites W2135623627 @default.
- W2032074920 cites W3162678295 @default.
- W2032074920 doi "https://doi.org/10.1002/pssa.2211470213" @default.
- W2032074920 hasPublicationYear "1995" @default.
- W2032074920 type Work @default.
- W2032074920 sameAs 2032074920 @default.
- W2032074920 citedByCount "29" @default.
- W2032074920 countsByYear W20320749202012 @default.
- W2032074920 countsByYear W20320749202013 @default.
- W2032074920 countsByYear W20320749202014 @default.
- W2032074920 countsByYear W20320749202018 @default.
- W2032074920 countsByYear W20320749202019 @default.
- W2032074920 countsByYear W20320749202020 @default.
- W2032074920 countsByYear W20320749202021 @default.
- W2032074920 countsByYear W20320749202022 @default.
- W2032074920 countsByYear W20320749202023 @default.
- W2032074920 crossrefType "journal-article" @default.
- W2032074920 hasAuthorship W2032074920A5090763210 @default.
- W2032074920 hasConcept C121332964 @default.
- W2032074920 hasConcept C159122135 @default.
- W2032074920 hasConcept C159985019 @default.
- W2032074920 hasConcept C185592680 @default.
- W2032074920 hasConcept C191897082 @default.
- W2032074920 hasConcept C192562407 @default.
- W2032074920 hasConcept C195268267 @default.
- W2032074920 hasConcept C2524010 @default.
- W2032074920 hasConcept C26873012 @default.
- W2032074920 hasConcept C2776196297 @default.
- W2032074920 hasConcept C33923547 @default.
- W2032074920 hasConcept C507968137 @default.
- W2032074920 hasConcept C514619126 @default.
- W2032074920 hasConcept C8010536 @default.
- W2032074920 hasConcept C97355855 @default.
- W2032074920 hasConceptScore W2032074920C121332964 @default.
- W2032074920 hasConceptScore W2032074920C159122135 @default.
- W2032074920 hasConceptScore W2032074920C159985019 @default.
- W2032074920 hasConceptScore W2032074920C185592680 @default.
- W2032074920 hasConceptScore W2032074920C191897082 @default.
- W2032074920 hasConceptScore W2032074920C192562407 @default.
- W2032074920 hasConceptScore W2032074920C195268267 @default.
- W2032074920 hasConceptScore W2032074920C2524010 @default.
- W2032074920 hasConceptScore W2032074920C26873012 @default.
- W2032074920 hasConceptScore W2032074920C2776196297 @default.
- W2032074920 hasConceptScore W2032074920C33923547 @default.
- W2032074920 hasConceptScore W2032074920C507968137 @default.
- W2032074920 hasConceptScore W2032074920C514619126 @default.
- W2032074920 hasConceptScore W2032074920C8010536 @default.
- W2032074920 hasConceptScore W2032074920C97355855 @default.
- W2032074920 hasIssue "2" @default.
- W2032074920 hasLocation W20320749201 @default.
- W2032074920 hasOpenAccess W2032074920 @default.
- W2032074920 hasPrimaryLocation W20320749201 @default.