- W2032636761 abstract "Pre-exposure tests on unstressed specimens of IMI 125 (low-oxygen, commercially pure titanium) in MeOH/HCl solutions revealed that intergranular anodic dissolution was occurring. In addition it was also observed that for pre-exposure times of 25 h or more, absorbed hydrogen was responsible for an intergranular strain-rate dependent embrittlement when specimens were tested in air, in the strain rate range 5.56 × 10−4-5.56 × 10−6s−1 immediately upon removal from the test environment. If an ageing period of 20 h at 150°C was inserted in between removing the specimens from the environment and testing, then the embrittlement effect could be eliminated. Constant crosshead speed stress corrosion tests were also performed in MeOH/HCl in the range of crosshead speeds 166.67 μm s−1 to 1.67 nm s−1. The mode of cracking was observed to be predominantly intergranular, with small regions of transgranular cleavage evident. Crack velocities of in excess of 1.2 mm h−1 were observed for the intergranular SCC. Additions of selenium, a cathodic poison, to the test environment produced a significant increase in the observed crack velocity, whilst additions of platinum were observed significantly to reduce crack propagation rates and, in some instances, cause complete crack arrest. Significantly less intergranular fracture was evident in specimens tested in platinum-containing solutions compared with those tested in platinum-free solutions. The above observations supported the argument that hydrogen embrittlement is the mechanism responsible for the intergranular SCC of titanium in MeOH/HCl solutions." @default.
- W2032636761 created "2016-06-24" @default.
- W2032636761 creator A5004119703 @default.
- W2032636761 creator A5012486395 @default.
- W2032636761 date "1993-05-01" @default.
- W2032636761 modified "2023-10-09" @default.
- W2032636761 title "The stress corrosion cracking and hydrogen embrittlement of titanium in methanol-hydrochloric acid solutions" @default.
- W2032636761 cites W1986685376 @default.
- W2032636761 cites W1992783996 @default.
- W2032636761 cites W2017512026 @default.
- W2032636761 cites W2043706785 @default.
- W2032636761 cites W2048037245 @default.
- W2032636761 cites W2064107280 @default.
- W2032636761 cites W2090870718 @default.
- W2032636761 cites W2329125548 @default.
- W2032636761 doi "https://doi.org/10.1016/0010-938x(93)90102-m" @default.
- W2032636761 hasPublicationYear "1993" @default.
- W2032636761 type Work @default.
- W2032636761 sameAs 2032636761 @default.
- W2032636761 citedByCount "32" @default.
- W2032636761 countsByYear W20326367612012 @default.
- W2032636761 countsByYear W20326367612013 @default.
- W2032636761 countsByYear W20326367612014 @default.
- W2032636761 countsByYear W20326367612016 @default.
- W2032636761 countsByYear W20326367612017 @default.
- W2032636761 countsByYear W20326367612022 @default.
- W2032636761 crossrefType "journal-article" @default.
- W2032636761 hasAuthorship W2032636761A5004119703 @default.
- W2032636761 hasAuthorship W2032636761A5012486395 @default.
- W2032636761 hasConcept C142282041 @default.
- W2032636761 hasConcept C149342994 @default.
- W2032636761 hasConcept C169043833 @default.
- W2032636761 hasConcept C178790620 @default.
- W2032636761 hasConcept C184102282 @default.
- W2032636761 hasConcept C185592680 @default.
- W2032636761 hasConcept C191897082 @default.
- W2032636761 hasConcept C192562407 @default.
- W2032636761 hasConcept C20625102 @default.
- W2032636761 hasConcept C2778760603 @default.
- W2032636761 hasConcept C512968161 @default.
- W2032636761 hasConcept C92621854 @default.
- W2032636761 hasConceptScore W2032636761C142282041 @default.
- W2032636761 hasConceptScore W2032636761C149342994 @default.
- W2032636761 hasConceptScore W2032636761C169043833 @default.
- W2032636761 hasConceptScore W2032636761C178790620 @default.
- W2032636761 hasConceptScore W2032636761C184102282 @default.
- W2032636761 hasConceptScore W2032636761C185592680 @default.
- W2032636761 hasConceptScore W2032636761C191897082 @default.
- W2032636761 hasConceptScore W2032636761C192562407 @default.
- W2032636761 hasConceptScore W2032636761C20625102 @default.
- W2032636761 hasConceptScore W2032636761C2778760603 @default.
- W2032636761 hasConceptScore W2032636761C512968161 @default.
- W2032636761 hasConceptScore W2032636761C92621854 @default.
- W2032636761 hasIssue "5" @default.
- W2032636761 hasLocation W20326367611 @default.
- W2032636761 hasOpenAccess W2032636761 @default.
- W2032636761 hasPrimaryLocation W20326367611 @default.
- W2032636761 hasRelatedWork W132565280 @default.
- W2032636761 hasRelatedWork W2012997152 @default.
- W2032636761 hasRelatedWork W2041097107 @default.
- W2032636761 hasRelatedWork W2062700662 @default.
- W2032636761 hasRelatedWork W2230276082 @default.
- W2032636761 hasRelatedWork W2507498813 @default.
- W2032636761 hasRelatedWork W2609467133 @default.
- W2032636761 hasRelatedWork W4241719453 @default.
- W2032636761 hasRelatedWork W815299756 @default.
- W2032636761 hasRelatedWork W1571280065 @default.
- W2032636761 hasVolume "34" @default.
- W2032636761 isParatext "false" @default.
- W2032636761 isRetracted "false" @default.
- W2032636761 magId "2032636761" @default.
- W2032636761 workType "article" @default.