- W2034155194 abstract "Synthesis of CeMO3 (M=Al,Ga) was attempted by the arc-melting method. In the case of M=Al, the arc-melted sample consisted typically of three regions CeAlO3, CeO2 and eutectic, mainly Al2O3. A similar texture was also observed for the case of M=Ga. Both CeAlO3 and CeGaO3 are crystallized in a tetragonal system (space group:P4/mmm). Lattice parameters of the tetragonal cell for CeAlO3 and CeGaO3 are a=0.37669(9) nm, c=0.37967(7) nm and a=0.3873(1) nm, c=0.3880(1) nm, respectively. According to thermal analysis, decomposition of 2CeMO3+12O2→2CeO2+M2O3 occurs for CeAlO3 and CeGaO3 at about 1275°C and 833°C, respectively. The TG curve shows that the onset-temperature of oxidation for CeAlO3 is at 1170°C and for CeGaO3 is at 720°C. After TG-DTA measurement, both compounds are completely decomposed to starting materials. The value of the micro-Vickers hardness for the CeAlO3 and CeGaO3 is 9.0 (±0.2) GPa and 7.2 (±0.4) GPa, respectively." @default.
- W2034155194 created "2016-06-24" @default.
- W2034155194 creator A5017563166 @default.
- W2034155194 creator A5019561119 @default.
- W2034155194 creator A5029532681 @default.
- W2034155194 creator A5047441463 @default.
- W2034155194 creator A5059431785 @default.
- W2034155194 creator A5062196470 @default.
- W2034155194 creator A5078970228 @default.
- W2034155194 date "1997-09-01" @default.
- W2034155194 modified "2023-10-16" @default.
- W2034155194 title "Microstructure, thermal properties and hardness of the CeMO3 (M=Al,Ga) synthesized by arc-melting method" @default.
- W2034155194 cites W1965917276 @default.
- W2034155194 cites W1975974640 @default.
- W2034155194 cites W1982416681 @default.
- W2034155194 cites W2007194236 @default.
- W2034155194 cites W2014044436 @default.
- W2034155194 cites W2016131690 @default.
- W2034155194 cites W2030189424 @default.
- W2034155194 cites W2059664144 @default.
- W2034155194 cites W2081636377 @default.
- W2034155194 cites W2089827332 @default.
- W2034155194 cites W2094688538 @default.
- W2034155194 doi "https://doi.org/10.1016/s0925-8388(97)00141-2" @default.
- W2034155194 hasPublicationYear "1997" @default.
- W2034155194 type Work @default.
- W2034155194 sameAs 2034155194 @default.
- W2034155194 citedByCount "19" @default.
- W2034155194 countsByYear W20341551942012 @default.
- W2034155194 countsByYear W20341551942015 @default.
- W2034155194 countsByYear W20341551942016 @default.
- W2034155194 countsByYear W20341551942017 @default.
- W2034155194 countsByYear W20341551942018 @default.
- W2034155194 countsByYear W20341551942019 @default.
- W2034155194 countsByYear W20341551942020 @default.
- W2034155194 countsByYear W20341551942021 @default.
- W2034155194 countsByYear W20341551942023 @default.
- W2034155194 crossrefType "journal-article" @default.
- W2034155194 hasAuthorship W2034155194A5017563166 @default.
- W2034155194 hasAuthorship W2034155194A5019561119 @default.
- W2034155194 hasAuthorship W2034155194A5029532681 @default.
- W2034155194 hasAuthorship W2034155194A5047441463 @default.
- W2034155194 hasAuthorship W2034155194A5059431785 @default.
- W2034155194 hasAuthorship W2034155194A5062196470 @default.
- W2034155194 hasAuthorship W2034155194A5078970228 @default.
- W2034155194 hasConcept C121332964 @default.
- W2034155194 hasConcept C165720898 @default.
- W2034155194 hasConcept C191897082 @default.
- W2034155194 hasConcept C192562407 @default.
- W2034155194 hasConcept C204530211 @default.
- W2034155194 hasConcept C2524010 @default.
- W2034155194 hasConcept C2994069645 @default.
- W2034155194 hasConcept C33923547 @default.
- W2034155194 hasConcept C83415579 @default.
- W2034155194 hasConcept C87976508 @default.
- W2034155194 hasConcept C97355855 @default.
- W2034155194 hasConceptScore W2034155194C121332964 @default.
- W2034155194 hasConceptScore W2034155194C165720898 @default.
- W2034155194 hasConceptScore W2034155194C191897082 @default.
- W2034155194 hasConceptScore W2034155194C192562407 @default.
- W2034155194 hasConceptScore W2034155194C204530211 @default.
- W2034155194 hasConceptScore W2034155194C2524010 @default.
- W2034155194 hasConceptScore W2034155194C2994069645 @default.
- W2034155194 hasConceptScore W2034155194C33923547 @default.
- W2034155194 hasConceptScore W2034155194C83415579 @default.
- W2034155194 hasConceptScore W2034155194C87976508 @default.
- W2034155194 hasConceptScore W2034155194C97355855 @default.
- W2034155194 hasFunder F4320320912 @default.
- W2034155194 hasIssue "1-2" @default.
- W2034155194 hasLocation W20341551941 @default.
- W2034155194 hasOpenAccess W2034155194 @default.
- W2034155194 hasPrimaryLocation W20341551941 @default.
- W2034155194 hasRelatedWork W2010582503 @default.
- W2034155194 hasRelatedWork W2020660716 @default.
- W2034155194 hasRelatedWork W2063388647 @default.
- W2034155194 hasRelatedWork W2066753314 @default.
- W2034155194 hasRelatedWork W2083437883 @default.
- W2034155194 hasRelatedWork W2145920364 @default.
- W2034155194 hasRelatedWork W2354299464 @default.
- W2034155194 hasRelatedWork W2597184736 @default.
- W2034155194 hasRelatedWork W3118359290 @default.
- W2034155194 hasRelatedWork W3157307459 @default.
- W2034155194 hasVolume "260" @default.
- W2034155194 isParatext "false" @default.
- W2034155194 isRetracted "false" @default.
- W2034155194 magId "2034155194" @default.
- W2034155194 workType "article" @default.