- W2034175182 abstract "Abstract Zn x Cd 1-x S thin films at low zinc content have been deposited on bare soda lime glass substrates using RF magnetron co-sputtering of CdS and ZnS for the first time to investigate annealing effect on the structural and optical properties of the thin films. The as-deposited films were annealed in O 2 /N 2 ambient at annealing temperature ranging 200-500 °C. The composition of the films was controlled by varying RF power of CdS and ZnS in such a ratio so that zinc content in the thin films was low. The composition, structural, optical and surface morphological properties of the films was investigated using EDX, XRD, UV-Vis spectrophotometer and FESEM. The annealed films were observed hexagonal wurtzite structure with strong preferential orientation along (002) diffraction peak. Crystallinity of the films increased with increasing annealing temperature below 400 °C whereas beyond 400 °C new peaks were observed along with decreasing trend of (002) diffraction peak. Optical absorption and transmission spectra were recorded within the range 300-900 nm. With increasing annealing temperature, the band gap of the annealed films once decreased and then abruptly increased at around 400 °C. The decreased bandgap may have been due to possible increase in the crystalline nature of the material. From SEM, it was observed that the thin films were formed by different clusters of grains which later changed to isolated grains as the annealing temperature increased. This work confirms that annealing temperature has overbearing influence on the Zn x Cd 1-x S thin film properties deposited by RF magnetron co-sputtering." @default.
- W2034175182 created "2016-06-24" @default.
- W2034175182 creator A5015240056 @default.
- W2034175182 creator A5045738528 @default.
- W2034175182 creator A5048409881 @default.
- W2034175182 creator A5050350023 @default.
- W2034175182 creator A5058851203 @default.
- W2034175182 creator A5069724940 @default.
- W2034175182 creator A5086894323 @default.
- W2034175182 date "2013-01-01" @default.
- W2034175182 modified "2023-10-18" @default.
- W2034175182 title "Effect of Annealing on the Properties of ZnxCd1-xS Thin Film Growth by RF Magnetron Co-sputtering" @default.
- W2034175182 cites W1988238480 @default.
- W2034175182 cites W2012508662 @default.
- W2034175182 cites W2023357982 @default.
- W2034175182 cites W2035651091 @default.
- W2034175182 cites W2058064137 @default.
- W2034175182 cites W2059922132 @default.
- W2034175182 cites W2067584333 @default.
- W2034175182 cites W2068926205 @default.
- W2034175182 cites W2072373289 @default.
- W2034175182 cites W2077125702 @default.
- W2034175182 cites W2078551140 @default.
- W2034175182 cites W2084561590 @default.
- W2034175182 cites W2087610644 @default.
- W2034175182 cites W2147803264 @default.
- W2034175182 cites W2149462900 @default.
- W2034175182 doi "https://doi.org/10.1016/j.egypro.2013.05.060" @default.
- W2034175182 hasPublicationYear "2013" @default.
- W2034175182 type Work @default.
- W2034175182 sameAs 2034175182 @default.
- W2034175182 citedByCount "24" @default.
- W2034175182 countsByYear W20341751822014 @default.
- W2034175182 countsByYear W20341751822015 @default.
- W2034175182 countsByYear W20341751822016 @default.
- W2034175182 countsByYear W20341751822017 @default.
- W2034175182 countsByYear W20341751822018 @default.
- W2034175182 countsByYear W20341751822019 @default.
- W2034175182 countsByYear W20341751822020 @default.
- W2034175182 countsByYear W20341751822021 @default.
- W2034175182 countsByYear W20341751822022 @default.
- W2034175182 countsByYear W20341751822023 @default.
- W2034175182 crossrefType "journal-article" @default.
- W2034175182 hasAuthorship W2034175182A5015240056 @default.
- W2034175182 hasAuthorship W2034175182A5045738528 @default.
- W2034175182 hasAuthorship W2034175182A5048409881 @default.
- W2034175182 hasAuthorship W2034175182A5050350023 @default.
- W2034175182 hasAuthorship W2034175182A5058851203 @default.
- W2034175182 hasAuthorship W2034175182A5069724940 @default.
- W2034175182 hasAuthorship W2034175182A5086894323 @default.
- W2034175182 hasBestOaLocation W20341751821 @default.
- W2034175182 hasConcept C123408415 @default.
- W2034175182 hasConcept C127413603 @default.
- W2034175182 hasConcept C171250308 @default.
- W2034175182 hasConcept C19067145 @default.
- W2034175182 hasConcept C191897082 @default.
- W2034175182 hasConcept C192562407 @default.
- W2034175182 hasConcept C22423302 @default.
- W2034175182 hasConcept C2777855556 @default.
- W2034175182 hasConcept C49040817 @default.
- W2034175182 hasConcept C61427134 @default.
- W2034175182 hasConcept C61696701 @default.
- W2034175182 hasConcept C97892325 @default.
- W2034175182 hasConceptScore W2034175182C123408415 @default.
- W2034175182 hasConceptScore W2034175182C127413603 @default.
- W2034175182 hasConceptScore W2034175182C171250308 @default.
- W2034175182 hasConceptScore W2034175182C19067145 @default.
- W2034175182 hasConceptScore W2034175182C191897082 @default.
- W2034175182 hasConceptScore W2034175182C192562407 @default.
- W2034175182 hasConceptScore W2034175182C22423302 @default.
- W2034175182 hasConceptScore W2034175182C2777855556 @default.
- W2034175182 hasConceptScore W2034175182C49040817 @default.
- W2034175182 hasConceptScore W2034175182C61427134 @default.
- W2034175182 hasConceptScore W2034175182C61696701 @default.
- W2034175182 hasConceptScore W2034175182C97892325 @default.
- W2034175182 hasLocation W20341751821 @default.
- W2034175182 hasOpenAccess W2034175182 @default.
- W2034175182 hasPrimaryLocation W20341751821 @default.
- W2034175182 hasRelatedWork W1968373997 @default.
- W2034175182 hasRelatedWork W2001415651 @default.
- W2034175182 hasRelatedWork W2025548647 @default.
- W2034175182 hasRelatedWork W2067838394 @default.
- W2034175182 hasRelatedWork W2255166385 @default.
- W2034175182 hasRelatedWork W2356622808 @default.
- W2034175182 hasRelatedWork W2366815809 @default.
- W2034175182 hasRelatedWork W2367979151 @default.
- W2034175182 hasRelatedWork W2387657166 @default.
- W2034175182 hasRelatedWork W2393308622 @default.
- W2034175182 hasVolume "33" @default.
- W2034175182 isParatext "false" @default.
- W2034175182 isRetracted "false" @default.
- W2034175182 magId "2034175182" @default.
- W2034175182 workType "article" @default.