- W2034233574 abstract "Electrical, structural, and optical properties of a free-standing 200 μm thick n-type GaN template grown by hydride vapor phase epitaxy have been investigated. Hall mobilities of 1100 and 6800 cm2/V s have been obtained at room temperature and 50 K, respectively. Quantitative analysis of acceptor concentration, donor concentration and donor activation energy has been conducted through simultaneous fitting of the temperature dependent Hall mobility and carrier concentration data which led to a donor concentration of 2.10×1016 cm−3 and an acceptor concentration of 4.9×1015 cm−3. The resultant donor activation energy is 18 meV. The analysis indicates that the dominant scattering mechanism at low temperatures is by ionized impurities. The extended defect concentrations on Ga- and N-faces were about 5×105 cm−2 for the former and about 1×107 cm−2 for the latter, as revealed by a chemical etch. The full width at half maximum of the symmetric (0 0 0 2) X-ray diffraction peak was 69″ and 160″ for the Ga- and N-faces, respectively. That for the asymmetric (10–14) peak was 103″ and 140″ for Ga- and N-faces, respectively. The donor bound exciton linewidth as measured on the Ga- and N-face (after a chemical etch to remove the damage) is about 1 meV each at 10 K. Instead of the commonly observed yellow band, this sample displayed a green band, which is centered at about 2.45 eV." @default.
- W2034233574 created "2016-06-24" @default.
- W2034233574 creator A5012506211 @default.
- W2034233574 creator A5020992935 @default.
- W2034233574 creator A5045908766 @default.
- W2034233574 creator A5051466308 @default.
- W2034233574 creator A5063146358 @default.
- W2034233574 creator A5065838439 @default.
- W2034233574 creator A5066812245 @default.
- W2034233574 date "2000-12-01" @default.
- W2034233574 modified "2023-10-09" @default.
- W2034233574 title "Electrical, structural, and optical characterization of free-standing GaN template grown by hydride vapor phase epitaxy" @default.
- W2034233574 cites W1745854265 @default.
- W2034233574 cites W1964716706 @default.
- W2034233574 cites W1970731037 @default.
- W2034233574 cites W1974011962 @default.
- W2034233574 cites W1977197537 @default.
- W2034233574 cites W1989491415 @default.
- W2034233574 cites W1992577211 @default.
- W2034233574 cites W2004150821 @default.
- W2034233574 cites W2010045670 @default.
- W2034233574 cites W2015993055 @default.
- W2034233574 cites W2016187903 @default.
- W2034233574 cites W2021714295 @default.
- W2034233574 cites W2038422902 @default.
- W2034233574 cites W2041520141 @default.
- W2034233574 cites W2048454557 @default.
- W2034233574 cites W2053711982 @default.
- W2034233574 cites W2058849736 @default.
- W2034233574 cites W2059310165 @default.
- W2034233574 cites W2060985203 @default.
- W2034233574 cites W2064581761 @default.
- W2034233574 cites W2067743273 @default.
- W2034233574 cites W2073775034 @default.
- W2034233574 cites W2086948262 @default.
- W2034233574 cites W2086965817 @default.
- W2034233574 cites W2089732291 @default.
- W2034233574 cites W2090195395 @default.
- W2034233574 cites W2091768670 @default.
- W2034233574 cites W2109759939 @default.
- W2034233574 cites W2119392370 @default.
- W2034233574 cites W2148945027 @default.
- W2034233574 cites W2162785093 @default.
- W2034233574 cites W2319413014 @default.
- W2034233574 cites W2945667631 @default.
- W2034233574 doi "https://doi.org/10.1016/s0038-1101(00)00202-1" @default.
- W2034233574 hasPublicationYear "2000" @default.
- W2034233574 type Work @default.
- W2034233574 sameAs 2034233574 @default.
- W2034233574 citedByCount "34" @default.
- W2034233574 countsByYear W20342335742013 @default.
- W2034233574 countsByYear W20342335742017 @default.
- W2034233574 countsByYear W20342335742020 @default.
- W2034233574 crossrefType "journal-article" @default.
- W2034233574 hasAuthorship W2034233574A5012506211 @default.
- W2034233574 hasAuthorship W2034233574A5020992935 @default.
- W2034233574 hasAuthorship W2034233574A5045908766 @default.
- W2034233574 hasAuthorship W2034233574A5051466308 @default.
- W2034233574 hasAuthorship W2034233574A5063146358 @default.
- W2034233574 hasAuthorship W2034233574A5065838439 @default.
- W2034233574 hasAuthorship W2034233574A5066812245 @default.
- W2034233574 hasConcept C106782819 @default.
- W2034233574 hasConcept C110738630 @default.
- W2034233574 hasConcept C113196181 @default.
- W2034233574 hasConcept C119599485 @default.
- W2034233574 hasConcept C121332964 @default.
- W2034233574 hasConcept C127413603 @default.
- W2034233574 hasConcept C134112204 @default.
- W2034233574 hasConcept C147789679 @default.
- W2034233574 hasConcept C171250308 @default.
- W2034233574 hasConcept C17729963 @default.
- W2034233574 hasConcept C178790620 @default.
- W2034233574 hasConcept C185592680 @default.
- W2034233574 hasConcept C191897082 @default.
- W2034233574 hasConcept C192562407 @default.
- W2034233574 hasConcept C26873012 @default.
- W2034233574 hasConcept C2777961443 @default.
- W2034233574 hasConcept C2779227376 @default.
- W2034233574 hasConcept C2779892579 @default.
- W2034233574 hasConcept C43617362 @default.
- W2034233574 hasConcept C49040817 @default.
- W2034233574 hasConcept C544153396 @default.
- W2034233574 hasConcept C69990965 @default.
- W2034233574 hasConcept C71987851 @default.
- W2034233574 hasConcept C95121573 @default.
- W2034233574 hasConceptScore W2034233574C106782819 @default.
- W2034233574 hasConceptScore W2034233574C110738630 @default.
- W2034233574 hasConceptScore W2034233574C113196181 @default.
- W2034233574 hasConceptScore W2034233574C119599485 @default.
- W2034233574 hasConceptScore W2034233574C121332964 @default.
- W2034233574 hasConceptScore W2034233574C127413603 @default.
- W2034233574 hasConceptScore W2034233574C134112204 @default.
- W2034233574 hasConceptScore W2034233574C147789679 @default.
- W2034233574 hasConceptScore W2034233574C171250308 @default.
- W2034233574 hasConceptScore W2034233574C17729963 @default.
- W2034233574 hasConceptScore W2034233574C178790620 @default.
- W2034233574 hasConceptScore W2034233574C185592680 @default.
- W2034233574 hasConceptScore W2034233574C191897082 @default.