- W2034876051 endingPage "262" @default.
- W2034876051 startingPage "257" @default.
- W2034876051 abstract "Alloys were produced by casting of Cu-Al-Fe-Be and Cu-Al-Fe-Ni aluminum bronzes and aged. The microstructures and mechanical properties were evaluated. The results indicated that solution and aging treatment can significantly improve the plasticity of Cu-Al-Fe-Be and Cu-Al-Fe-Ni, while the strength and hardness remained in the quenched level. Extending the aging time can effectively enhance the mechanical properties of alloys, and the longer the aging time, the higher the electric resistance of alloys. According to the results, the mechanical properties of the Cu-Al-Fe-Be alloy can be improved remarkably by solution treatment for 120 min at 950°C, followed by aging treatment for 120 min at 350°C, and quenched. While the most suitable heat treatment for the Cu-Al-Fe-Ni alloy was solution treatment 120 min at 950°C, followed by aging for 120 min at 450°C, and quenched. The experimental result also suggested that the Cu-Al-Fe-Be alloy possessed higher hardness and tensile strength compared to the Cu-Al-Fe-Ni alloy." @default.
- W2034876051 created "2016-06-24" @default.
- W2034876051 creator A5024830878 @default.
- W2034876051 creator A5050047118 @default.
- W2034876051 creator A5066815669 @default.
- W2034876051 date "2011-02-01" @default.
- W2034876051 modified "2023-09-28" @default.
- W2034876051 title "The Effect of Aging Heat Treatment on the Mechanical Properties of Cu-Al-Fe-(x) Alloys" @default.
- W2034876051 cites W1978149070 @default.
- W2034876051 cites W2020479792 @default.
- W2034876051 cites W2029892587 @default.
- W2034876051 cites W2130528691 @default.
- W2034876051 cites W2935748481 @default.
- W2034876051 doi "https://doi.org/10.4028/www.scientific.net/kem.467-469.257" @default.
- W2034876051 hasPublicationYear "2011" @default.
- W2034876051 type Work @default.
- W2034876051 sameAs 2034876051 @default.
- W2034876051 citedByCount "1" @default.
- W2034876051 countsByYear W20348760512022 @default.
- W2034876051 crossrefType "journal-article" @default.
- W2034876051 hasAuthorship W2034876051A5024830878 @default.
- W2034876051 hasAuthorship W2034876051A5050047118 @default.
- W2034876051 hasAuthorship W2034876051A5066815669 @default.
- W2034876051 hasConcept C112950240 @default.
- W2034876051 hasConcept C16635281 @default.
- W2034876051 hasConcept C191897082 @default.
- W2034876051 hasConcept C192562407 @default.
- W2034876051 hasConcept C2780026712 @default.
- W2034876051 hasConcept C513153333 @default.
- W2034876051 hasConcept C87976508 @default.
- W2034876051 hasConceptScore W2034876051C112950240 @default.
- W2034876051 hasConceptScore W2034876051C16635281 @default.
- W2034876051 hasConceptScore W2034876051C191897082 @default.
- W2034876051 hasConceptScore W2034876051C192562407 @default.
- W2034876051 hasConceptScore W2034876051C2780026712 @default.
- W2034876051 hasConceptScore W2034876051C513153333 @default.
- W2034876051 hasConceptScore W2034876051C87976508 @default.
- W2034876051 hasLocation W20348760511 @default.
- W2034876051 hasOpenAccess W2034876051 @default.
- W2034876051 hasPrimaryLocation W20348760511 @default.
- W2034876051 hasRelatedWork W1982015266 @default.
- W2034876051 hasRelatedWork W1984021872 @default.
- W2034876051 hasRelatedWork W1987487801 @default.
- W2034876051 hasRelatedWork W2362720846 @default.
- W2034876051 hasRelatedWork W2364995748 @default.
- W2034876051 hasRelatedWork W2373405944 @default.
- W2034876051 hasRelatedWork W2377876279 @default.
- W2034876051 hasRelatedWork W2388650043 @default.
- W2034876051 hasRelatedWork W2389587133 @default.
- W2034876051 hasRelatedWork W3047228083 @default.
- W2034876051 hasVolume "467-469" @default.
- W2034876051 isParatext "false" @default.
- W2034876051 isRetracted "false" @default.
- W2034876051 magId "2034876051" @default.
- W2034876051 workType "article" @default.