- W2035002372 abstract "Introduction .—The bismuth rods used for the experiments were of circular cross section, the diameter being about 1 mm. and the length varying from 1 to 2 cm. The rods were prepared in the usual way by extrusion of the metal, and afterwards grown into crystals of the desired orientation by the method described by the author in a previous paper. Except where specially stated, the bismuth used was obtained from Hilger and was 99·993 per cent, pure, and was the same as that used for the experiments on magnetisation described in Part II of this paper. The rods of bismuth were fixed in the apparatus as shown in fig. 2. The two globes which held the rod were made of low melting point Newton alloy; the length of the rod was measured by a travelling microscope. The rods when placed in the extensometer were submitted to a stress produced by the weight of the piston 9, fig. 1, and by different connecting links. The force due to the weight of these parts amounted to 127 gm. which produced a stress of about 15 kg. per square centimetre on the specimen under examination. Later it will be seen that the phenomena observed are actually independent of the stress. The experimental results are represented by curves. The relative increase of length Δ l / l multiplied by 10 6 is taken for the ordinates, and the abscissæ as before, represent the field in kilogauss. In weak magnetic fields, for all orientations of the crystal, we found th at the increase in length followed the square law, and in this case the experimental results could be expressed by the moduli of magnetostriction as defined in Part III, expression (50). The magnetostriction effect was very large and the possible stray effects were small in comparison and could be regarded as negligible." @default.
- W2035002372 created "2016-06-24" @default.
- W2035002372 date "1932-04-01" @default.
- W2035002372 modified "2023-09-25" @default.
- W2035002372 title "The study of the magnetic properties of matter in strong magnetic fields. Part V.— Experiments on magnetostriction in dia- and para-magnetic substances" @default.
- W2035002372 doi "https://doi.org/10.1098/rspa.1932.0054" @default.
- W2035002372 hasPublicationYear "1932" @default.
- W2035002372 type Work @default.
- W2035002372 sameAs 2035002372 @default.
- W2035002372 citedByCount "19" @default.
- W2035002372 countsByYear W20350023722013 @default.
- W2035002372 countsByYear W20350023722015 @default.
- W2035002372 countsByYear W20350023722021 @default.
- W2035002372 crossrefType "journal-article" @default.
- W2035002372 hasConcept C115260700 @default.
- W2035002372 hasConcept C120665830 @default.
- W2035002372 hasConcept C121332964 @default.
- W2035002372 hasConcept C138885662 @default.
- W2035002372 hasConcept C142724271 @default.
- W2035002372 hasConcept C159985019 @default.
- W2035002372 hasConcept C162184086 @default.
- W2035002372 hasConcept C185885794 @default.
- W2035002372 hasConcept C191897082 @default.
- W2035002372 hasConcept C192562407 @default.
- W2035002372 hasConcept C199360897 @default.
- W2035002372 hasConcept C204787440 @default.
- W2035002372 hasConcept C21036866 @default.
- W2035002372 hasConcept C26873012 @default.
- W2035002372 hasConcept C2781285689 @default.
- W2035002372 hasConcept C41008148 @default.
- W2035002372 hasConcept C41895202 @default.
- W2035002372 hasConcept C533668322 @default.
- W2035002372 hasConcept C62520636 @default.
- W2035002372 hasConcept C71924100 @default.
- W2035002372 hasConcept C72852350 @default.
- W2035002372 hasConceptScore W2035002372C115260700 @default.
- W2035002372 hasConceptScore W2035002372C120665830 @default.
- W2035002372 hasConceptScore W2035002372C121332964 @default.
- W2035002372 hasConceptScore W2035002372C138885662 @default.
- W2035002372 hasConceptScore W2035002372C142724271 @default.
- W2035002372 hasConceptScore W2035002372C159985019 @default.
- W2035002372 hasConceptScore W2035002372C162184086 @default.
- W2035002372 hasConceptScore W2035002372C185885794 @default.
- W2035002372 hasConceptScore W2035002372C191897082 @default.
- W2035002372 hasConceptScore W2035002372C192562407 @default.
- W2035002372 hasConceptScore W2035002372C199360897 @default.
- W2035002372 hasConceptScore W2035002372C204787440 @default.
- W2035002372 hasConceptScore W2035002372C21036866 @default.
- W2035002372 hasConceptScore W2035002372C26873012 @default.
- W2035002372 hasConceptScore W2035002372C2781285689 @default.
- W2035002372 hasConceptScore W2035002372C41008148 @default.
- W2035002372 hasConceptScore W2035002372C41895202 @default.
- W2035002372 hasConceptScore W2035002372C533668322 @default.
- W2035002372 hasConceptScore W2035002372C62520636 @default.
- W2035002372 hasConceptScore W2035002372C71924100 @default.
- W2035002372 hasConceptScore W2035002372C72852350 @default.
- W2035002372 hasIssue "828" @default.
- W2035002372 hasLocation W20350023721 @default.
- W2035002372 hasOpenAccess W2035002372 @default.
- W2035002372 hasPrimaryLocation W20350023721 @default.
- W2035002372 hasRelatedWork W1137582763 @default.
- W2035002372 hasRelatedWork W1975768762 @default.
- W2035002372 hasRelatedWork W1995497260 @default.
- W2035002372 hasRelatedWork W2035002372 @default.
- W2035002372 hasRelatedWork W2056354259 @default.
- W2035002372 hasRelatedWork W2072032634 @default.
- W2035002372 hasRelatedWork W2137753052 @default.
- W2035002372 hasRelatedWork W2283679062 @default.
- W2035002372 hasRelatedWork W2371211881 @default.
- W2035002372 hasRelatedWork W2582325703 @default.
- W2035002372 hasVolume "135" @default.
- W2035002372 isParatext "false" @default.
- W2035002372 isRetracted "false" @default.
- W2035002372 magId "2035002372" @default.
- W2035002372 workType "article" @default.