• W2035257508 abstract "Effects of the gel size on the thermal behavior and the shrinking profile of a chemically cross-linked poly(N-isopropylacrylamide) (NIPA) gel in water were investigated by differential scanning calorimetry (DSC) and the volume measurement at the same heating rate as used for the DSC. The DSC thermogram of NIPA gel depended on the shrinking process at the transition. The DSC thermogram of the NIPA gel of the smallest size (0.3-mm diameter at the preparation) gave double endothermic peaks, and the gel underwent a discontinuous volume shrinkage (i.e. a volume transition) at about 34.5 °C in the DSC run with a heating rate of 0.1 °C/min. This suggests that the two-step cooperative dehydration of NIPA chains takes places in the volume shrinkage. It was proposed that the peak at the low temperature (peak 1) originated from the dehydration of NIPA chains without the volume transition while the peak at the high temperature (peak 2) was associated with the discontinuous volume shrinkage. A single broad endothermic peak was observed for the NIPA gel of the largest size (3-mm diameter at the preparation) that shrank only slightly during the DSC run. For the largest gel, the volume transition cannot occur within the time scale of the DSC run due to the slow volume shrinkage while dehydration of the polymer chains takes place locally. The peak of the largest gel and peak 1 were suggested to be due to the dehydration of NIPA chains coupled with the spinodal decomposition without the volume transition." @default.
• W2035257508 created "2016-06-24" @default.
• W2035257508 creator A5021550995 @default.
• W2035257508 creator A5040429486 @default.
• W2035257508 creator A5065694778 @default.
• W2035257508 date "1998-01-27" @default.
• W2035257508 modified "2023-09-27" @default.
• W2035257508 title "Effects of the Gel Size on the Volume Phase Transition of Poly(<i>N</i>-isopropylacrylamide) Gels: A Calorimetric Study" @default.
• W2035257508 cites W1969606439 @default.
• W2035257508 cites W1976529631 @default.
• W2035257508 cites W1982218431 @default.
• W2035257508 cites W1993447953 @default.
• W2035257508 cites W2003034707 @default.
• W2035257508 cites W2020105489 @default.
• W2035257508 cites W2028561555 @default.
• W2035257508 cites W2035548368 @default.
• W2035257508 cites W2038202658 @default.
• W2035257508 cites W2040509978 @default.
• W2035257508 cites W2059611393 @default.
• W2035257508 cites W2060573038 @default.
• W2035257508 cites W2061628043 @default.
• W2035257508 cites W2063934271 @default.
• W2035257508 cites W2066567158 @default.
• W2035257508 cites W2069253483 @default.
• W2035257508 cites W2079611104 @default.
• W2035257508 cites W2086710884 @default.
• W2035257508 cites W2087874940 @default.
• W2035257508 cites W2090420532 @default.
• W2035257508 cites W2091007535 @default.
• W2035257508 cites W2110069860 @default.
• W2035257508 doi "https://doi.org/10.1021/la970886t" @default.
• W2035257508 hasPublicationYear "1998" @default.
• W2035257508 type Work @default.
• W2035257508 sameAs 2035257508 @default.
• W2035257508 citedByCount "31" @default.
• W2035257508 countsByYear W20352575082012 @default.
• W2035257508 countsByYear W20352575082014 @default.
• W2035257508 countsByYear W20352575082015 @default.
• W2035257508 countsByYear W20352575082016 @default.
• W2035257508 countsByYear W20352575082018 @default.
• W2035257508 countsByYear W20352575082019 @default.
• W2035257508 countsByYear W20352575082020 @default.
• W2035257508 countsByYear W20352575082021 @default.
• W2035257508 countsByYear W20352575082023 @default.
• W2035257508 crossrefType "journal-article" @default.
• W2035257508 hasAuthorship W2035257508A5021550995 @default.
• W2035257508 hasAuthorship W2035257508A5040429486 @default.
• W2035257508 hasAuthorship W2035257508A5065694778 @default.
• W2035257508 hasConcept C113196181 @default.
• W2035257508 hasConcept C121332964 @default.
• W2035257508 hasConcept C127413603 @default.
• W2035257508 hasConcept C149288129 @default.
• W2035257508 hasConcept C150394285 @default.
• W2035257508 hasConcept C159985019 @default.
• W2035257508 hasConcept C178790620 @default.
• W2035257508 hasConcept C180145272 @default.
• W2035257508 hasConcept C185592680 @default.
• W2035257508 hasConcept C188027245 @default.
• W2035257508 hasConcept C192562407 @default.
• W2035257508 hasConcept C20556612 @default.
• W2035257508 hasConcept C20976626 @default.
• W2035257508 hasConcept C2778769901 @default.
• W2035257508 hasConcept C39519442 @default.
• W2035257508 hasConcept C42360764 @default.
• W2035257508 hasConcept C43617362 @default.
• W2035257508 hasConcept C55493867 @default.
• W2035257508 hasConcept C97355855 @default.
• W2035257508 hasConceptScore W2035257508C113196181 @default.
• W2035257508 hasConceptScore W2035257508C121332964 @default.
• W2035257508 hasConceptScore W2035257508C127413603 @default.
• W2035257508 hasConceptScore W2035257508C149288129 @default.
• W2035257508 hasConceptScore W2035257508C150394285 @default.
• W2035257508 hasConceptScore W2035257508C159985019 @default.
• W2035257508 hasConceptScore W2035257508C178790620 @default.
• W2035257508 hasConceptScore W2035257508C180145272 @default.
• W2035257508 hasConceptScore W2035257508C185592680 @default.
• W2035257508 hasConceptScore W2035257508C188027245 @default.
• W2035257508 hasConceptScore W2035257508C192562407 @default.
• W2035257508 hasConceptScore W2035257508C20556612 @default.
• W2035257508 hasConceptScore W2035257508C20976626 @default.
• W2035257508 hasConceptScore W2035257508C2778769901 @default.
• W2035257508 hasConceptScore W2035257508C39519442 @default.
• W2035257508 hasConceptScore W2035257508C42360764 @default.
• W2035257508 hasConceptScore W2035257508C43617362 @default.
• W2035257508 hasConceptScore W2035257508C55493867 @default.
• W2035257508 hasConceptScore W2035257508C97355855 @default.
• W2035257508 hasIssue "4" @default.
• W2035257508 hasLocation W20352575081 @default.
• W2035257508 hasOpenAccess W2035257508 @default.
• W2035257508 hasPrimaryLocation W20352575081 @default.
• W2035257508 hasRelatedWork W1973937055 @default.
• W2035257508 hasRelatedWork W1986555257 @default.
• W2035257508 hasRelatedWork W2052317294 @default.
• W2035257508 hasRelatedWork W2076061040 @default.
• W2035257508 hasRelatedWork W2102001917 @default.
• W2035257508 hasRelatedWork W2112990587 @default.
• W2035257508 hasRelatedWork W2118238442 @default.
• W2035257508 hasRelatedWork W2325472790 @default.

• next