- W2035440708 abstract "A new synthesis and processing route for SiO<SUB>2</SUB> glass like micropatterns with heights up to 30 micrometer by gel embossing and thermal densification has been developed. For this reason an organically modified nanoparticulate sol prepared by acid catalysis of methyl- and phenyl- triethoxysilane and tetraethyl orthosilicate in combination with colloidal silica sol was used. Sol coatings with thicknesses up to 15 micrometer are obtained by dipping of float glass substrates. After a predrying step of about 60 s micropatterns are obtained using a pressure of only 2.5 mN/mm<SUP>2</SUP>. Due to this low pressure, flexible and low cost silicon rubber stampers can be used. The gelation time of the sol can be extended from 5 d to 16 days and the working time for embossing can be extended from 60 s up to 100 s by a partial replacement of methyl silane by phenyl silane from 0 to 20 mole %. After embossing and drying at 50 degrees Celsius the patterned layer was densified at temperatures up to 500 degrees Celsius to 95% density as indicated by refractive index measurements. It is assumed that the densification process is strongly promoted by the used colloidal silica nano particles. The linear shrinkage of the micropatterns is limited to about 25% due to the high solid content of the sol and the high green density of the layers. Since the structures are densified at temperatures far below T<SUB>g</SUB> sharp edged patterns can be obtained as shown by high resolution secondary electron microscopy. The capability of this technique is demonstrated by the fabrication of light trapping structures with pyramides of 7 micrometer in height and 10 micrometer in width on an area of 20 multiplied by 20 mm<SUP>2</SUP> and micro lens arrays of lenses with 30 micrometer in height and 600 micrometer in diameter on an area of 20 multiplied by 30 mm<SUP>2</SUP>." @default.
- W2035440708 created "2016-06-24" @default.
- W2035440708 creator A5003191112 @default.
- W2035440708 creator A5021444629 @default.
- W2035440708 creator A5023440782 @default.
- W2035440708 creator A5081130938 @default.
- W2035440708 date "1997-10-02" @default.
- W2035440708 modified "2023-09-27" @default.
- W2035440708 title "<title>Preparation of micropatterns with profile heights up to 30 microns from silica sols</title>" @default.
- W2035440708 doi "https://doi.org/10.1117/12.284142" @default.
- W2035440708 hasPublicationYear "1997" @default.
- W2035440708 type Work @default.
- W2035440708 sameAs 2035440708 @default.
- W2035440708 citedByCount "3" @default.
- W2035440708 countsByYear W20354407082016 @default.
- W2035440708 countsByYear W20354407082018 @default.
- W2035440708 crossrefType "proceedings-article" @default.
- W2035440708 hasAuthorship W2035440708A5003191112 @default.
- W2035440708 hasAuthorship W2035440708A5021444629 @default.
- W2035440708 hasAuthorship W2035440708A5023440782 @default.
- W2035440708 hasAuthorship W2035440708A5081130938 @default.
- W2035440708 hasConcept C120665830 @default.
- W2035440708 hasConcept C121332964 @default.
- W2035440708 hasConcept C127413603 @default.
- W2035440708 hasConcept C159985019 @default.
- W2035440708 hasConcept C171250308 @default.
- W2035440708 hasConcept C171635847 @default.
- W2035440708 hasConcept C192562407 @default.
- W2035440708 hasConcept C2776392700 @default.
- W2035440708 hasConcept C2777432599 @default.
- W2035440708 hasConcept C2777691222 @default.
- W2035440708 hasConcept C2778024142 @default.
- W2035440708 hasConcept C2778024649 @default.
- W2035440708 hasConcept C2781448156 @default.
- W2035440708 hasConcept C38398224 @default.
- W2035440708 hasConcept C42360764 @default.
- W2035440708 hasConcept C49040817 @default.
- W2035440708 hasConcept C544956773 @default.
- W2035440708 hasConceptScore W2035440708C120665830 @default.
- W2035440708 hasConceptScore W2035440708C121332964 @default.
- W2035440708 hasConceptScore W2035440708C127413603 @default.
- W2035440708 hasConceptScore W2035440708C159985019 @default.
- W2035440708 hasConceptScore W2035440708C171250308 @default.
- W2035440708 hasConceptScore W2035440708C171635847 @default.
- W2035440708 hasConceptScore W2035440708C192562407 @default.
- W2035440708 hasConceptScore W2035440708C2776392700 @default.
- W2035440708 hasConceptScore W2035440708C2777432599 @default.
- W2035440708 hasConceptScore W2035440708C2777691222 @default.
- W2035440708 hasConceptScore W2035440708C2778024142 @default.
- W2035440708 hasConceptScore W2035440708C2778024649 @default.
- W2035440708 hasConceptScore W2035440708C2781448156 @default.
- W2035440708 hasConceptScore W2035440708C38398224 @default.
- W2035440708 hasConceptScore W2035440708C42360764 @default.
- W2035440708 hasConceptScore W2035440708C49040817 @default.
- W2035440708 hasConceptScore W2035440708C544956773 @default.
- W2035440708 hasLocation W20354407081 @default.
- W2035440708 hasOpenAccess W2035440708 @default.
- W2035440708 hasPrimaryLocation W20354407081 @default.
- W2035440708 hasRelatedWork W2006512054 @default.
- W2035440708 hasRelatedWork W2030372205 @default.
- W2035440708 hasRelatedWork W2033182285 @default.
- W2035440708 hasRelatedWork W2035440708 @default.
- W2035440708 hasRelatedWork W2075585776 @default.
- W2035440708 hasRelatedWork W2354929567 @default.
- W2035440708 hasRelatedWork W2374726142 @default.
- W2035440708 hasRelatedWork W3036062738 @default.
- W2035440708 hasRelatedWork W3092945548 @default.
- W2035440708 hasRelatedWork W4378376734 @default.
- W2035440708 isParatext "false" @default.
- W2035440708 isRetracted "false" @default.
- W2035440708 magId "2035440708" @default.
- W2035440708 workType "article" @default.