- W2036701473 abstract "Extensive failure analysis was performed on identical, isothermally cycled wafer-level chip scale packages with Sn3.8wt%0.7wt%Ag (SAC387) solder joints. Packages were periodically removed during the cycling process to observe crack front progression. The packages were dipped in liquid nitrogen to reduce solder ductility and then pried apart. The crack areas were observed under an optical microscope. The average crack areas on the corner and mid-edge joints of the package were measured using an image processing software. 50 packages were characterized from 240 to 7200 cycles at every 240 cycles. An average of 20 solder joints per cycle was observed to estimate the crack length and area. A finite element model of this package was constructed in ABAQUS. The solder interconnects of the model were given full plastic and creep properties. Using the failure analysis data and the finite element model, the material constant value in a previously developed hierarchal fracture model was calibrated for SAC387. The ability of the model to predict non-intuitive failure initiation sites due to the under bump metallurgy (UBM) geometry is demonstrated. The hierarchal fracture process model was inspired by information theory and continuum thermodynamics. It was earlier proposed to capture the length-scale and temporal hierarchy inherent in quasi-static fracture processes. This single parameter model allows for a non-empirical, geometry independent approach to predicting crack growth by relating equivalent inelastic dissipations and a material constant to the probability of fracture at a material point." @default.
- W2036701473 created "2016-06-24" @default.
- W2036701473 creator A5040914154 @default.
- W2036701473 creator A5058428016 @default.
- W2036701473 creator A5080314217 @default.
- W2036701473 creator A5088467503 @default.
- W2036701473 date "2009-01-01" @default.
- W2036701473 modified "2023-09-26" @default.
- W2036701473 title "Characterization of Crack Fronts in a WLCSP Package: Experiments and Models for Application of a Multiscale Fracture Theory" @default.
- W2036701473 doi "https://doi.org/10.1115/interpack2009-89402" @default.
- W2036701473 hasPublicationYear "2009" @default.
- W2036701473 type Work @default.
- W2036701473 sameAs 2036701473 @default.
- W2036701473 citedByCount "1" @default.
- W2036701473 crossrefType "proceedings-article" @default.
- W2036701473 hasAuthorship W2036701473A5040914154 @default.
- W2036701473 hasAuthorship W2036701473A5058428016 @default.
- W2036701473 hasAuthorship W2036701473A5080314217 @default.
- W2036701473 hasAuthorship W2036701473A5088467503 @default.
- W2036701473 hasConcept C126233035 @default.
- W2036701473 hasConcept C127413603 @default.
- W2036701473 hasConcept C135628077 @default.
- W2036701473 hasConcept C149912024 @default.
- W2036701473 hasConcept C159985019 @default.
- W2036701473 hasConcept C160671074 @default.
- W2036701473 hasConcept C171250308 @default.
- W2036701473 hasConcept C192562407 @default.
- W2036701473 hasConcept C2776512210 @default.
- W2036701473 hasConcept C43369102 @default.
- W2036701473 hasConcept C50296614 @default.
- W2036701473 hasConcept C59085676 @default.
- W2036701473 hasConcept C66938386 @default.
- W2036701473 hasConceptScore W2036701473C126233035 @default.
- W2036701473 hasConceptScore W2036701473C127413603 @default.
- W2036701473 hasConceptScore W2036701473C135628077 @default.
- W2036701473 hasConceptScore W2036701473C149912024 @default.
- W2036701473 hasConceptScore W2036701473C159985019 @default.
- W2036701473 hasConceptScore W2036701473C160671074 @default.
- W2036701473 hasConceptScore W2036701473C171250308 @default.
- W2036701473 hasConceptScore W2036701473C192562407 @default.
- W2036701473 hasConceptScore W2036701473C2776512210 @default.
- W2036701473 hasConceptScore W2036701473C43369102 @default.
- W2036701473 hasConceptScore W2036701473C50296614 @default.
- W2036701473 hasConceptScore W2036701473C59085676 @default.
- W2036701473 hasConceptScore W2036701473C66938386 @default.
- W2036701473 hasLocation W20367014731 @default.
- W2036701473 hasOpenAccess W2036701473 @default.
- W2036701473 hasPrimaryLocation W20367014731 @default.
- W2036701473 hasRelatedWork W1979080992 @default.
- W2036701473 hasRelatedWork W1989251040 @default.
- W2036701473 hasRelatedWork W1992780447 @default.
- W2036701473 hasRelatedWork W2032385735 @default.
- W2036701473 hasRelatedWork W2048829577 @default.
- W2036701473 hasRelatedWork W2112270026 @default.
- W2036701473 hasRelatedWork W2536868607 @default.
- W2036701473 hasRelatedWork W2606250390 @default.
- W2036701473 hasRelatedWork W4283375541 @default.
- W2036701473 hasRelatedWork W4307276148 @default.
- W2036701473 isParatext "false" @default.
- W2036701473 isRetracted "false" @default.
- W2036701473 magId "2036701473" @default.
- W2036701473 workType "article" @default.