- W2037422435 abstract "Yttria-stabilized zirconia (YSZ) thin films were deposited by pulsed laser deposition (PLD) at laser repetition frequencies of 10–50 Hz. Controlling the laser repetition frequency can achieve high deposition rate of YSZ, but high deposition rate at high laser repetition frequency can adversely affect the crystallinity of the resulting film. In the present work, X-ray diffraction (XRD) of YSZ thin films deposited at 10–50 Hz unexpectedly indicated no significant differences. Well-crystallized YSZ thin films were obtained for all laser repetition frequencies. This result may be due to a sufficient substrate temperature of 1000 K during processing. The oxide-ion conductivity of each thin film was comparable to that of bulk YSZ. Only minor differences in Y2O3 content, residual stress, grain size, and grain-boundary width were observed among the films. We concluded that similar quality YSZ thin films were obtained at all deposition frequencies. Oxide-ion conductivity was affected by the temperature at which the substrate was deposited. The YSZ thin films deposited at 900 K and 1000 K showed similar oxide-ion conductivity and films deposited at 800 K showed lower oxide-ion conductivity. This difference could perhaps be due to narrow grain-boundary width. The YSZ thin film with highest oxide-ion conductivity was fabricated at an intermediate substrate temperature of 900 K with a deposition rate of 86 nm·min−1 at 50 Hz, without additional high-temperature annealing greater than 1273 K. The YSZ growth rates were faster than the rates for other gas-phase methods such as midfrequency and DC sputtering." @default.
- W2037422435 created "2016-06-24" @default.
- W2037422435 creator A5002284239 @default.
- W2037422435 creator A5005284999 @default.
- W2037422435 creator A5016442340 @default.
- W2037422435 creator A5049314701 @default.
- W2037422435 creator A5081463891 @default.
- W2037422435 creator A5085682509 @default.
- W2037422435 date "2015-06-01" @default.
- W2037422435 modified "2023-09-23" @default.
- W2037422435 title "Effect of Rate on Pulsed Laser Deposition of Yttria-Stabilized Zirconia Electrolyte Thin Films for SOFCs" @default.
- W2037422435 cites W1666471348 @default.
- W2037422435 cites W1967584837 @default.
- W2037422435 cites W1979850233 @default.
- W2037422435 cites W1989578156 @default.
- W2037422435 cites W1992982886 @default.
- W2037422435 cites W1996278083 @default.
- W2037422435 cites W2001939961 @default.
- W2037422435 cites W2009669102 @default.
- W2037422435 cites W2018252717 @default.
- W2037422435 cites W2028998021 @default.
- W2037422435 cites W2031038589 @default.
- W2037422435 cites W2032837175 @default.
- W2037422435 cites W2042068339 @default.
- W2037422435 cites W2054253611 @default.
- W2037422435 cites W2055989421 @default.
- W2037422435 cites W2062061777 @default.
- W2037422435 cites W2063836104 @default.
- W2037422435 cites W2079176041 @default.
- W2037422435 cites W2107143943 @default.
- W2037422435 cites W2114655503 @default.
- W2037422435 cites W2155044782 @default.
- W2037422435 cites W2157289534 @default.
- W2037422435 cites W2319034138 @default.
- W2037422435 cites W4232691165 @default.
- W2037422435 cites W4237877171 @default.
- W2037422435 cites W4248310927 @default.
- W2037422435 doi "https://doi.org/10.1115/1.4029423" @default.
- W2037422435 hasPublicationYear "2015" @default.
- W2037422435 type Work @default.
- W2037422435 sameAs 2037422435 @default.
- W2037422435 citedByCount "2" @default.
- W2037422435 countsByYear W20374224352017 @default.
- W2037422435 countsByYear W20374224352019 @default.
- W2037422435 crossrefType "journal-article" @default.
- W2037422435 hasAuthorship W2037422435A5002284239 @default.
- W2037422435 hasAuthorship W2037422435A5005284999 @default.
- W2037422435 hasAuthorship W2037422435A5016442340 @default.
- W2037422435 hasAuthorship W2037422435A5049314701 @default.
- W2037422435 hasAuthorship W2037422435A5081463891 @default.
- W2037422435 hasAuthorship W2037422435A5085682509 @default.
- W2037422435 hasConcept C111368507 @default.
- W2037422435 hasConcept C113196181 @default.
- W2037422435 hasConcept C123609680 @default.
- W2037422435 hasConcept C127313418 @default.
- W2037422435 hasConcept C131540310 @default.
- W2037422435 hasConcept C134132462 @default.
- W2037422435 hasConcept C147789679 @default.
- W2037422435 hasConcept C159985019 @default.
- W2037422435 hasConcept C171250308 @default.
- W2037422435 hasConcept C185592680 @default.
- W2037422435 hasConcept C19067145 @default.
- W2037422435 hasConcept C191897082 @default.
- W2037422435 hasConcept C192191005 @default.
- W2037422435 hasConcept C192562407 @default.
- W2037422435 hasConcept C199289684 @default.
- W2037422435 hasConcept C2777289219 @default.
- W2037422435 hasConcept C2779851234 @default.
- W2037422435 hasConcept C37982897 @default.
- W2037422435 hasConcept C43617362 @default.
- W2037422435 hasConcept C46275449 @default.
- W2037422435 hasConcept C47908070 @default.
- W2037422435 hasConcept C87976508 @default.
- W2037422435 hasConcept C96410337 @default.
- W2037422435 hasConceptScore W2037422435C111368507 @default.
- W2037422435 hasConceptScore W2037422435C113196181 @default.
- W2037422435 hasConceptScore W2037422435C123609680 @default.
- W2037422435 hasConceptScore W2037422435C127313418 @default.
- W2037422435 hasConceptScore W2037422435C131540310 @default.
- W2037422435 hasConceptScore W2037422435C134132462 @default.
- W2037422435 hasConceptScore W2037422435C147789679 @default.
- W2037422435 hasConceptScore W2037422435C159985019 @default.
- W2037422435 hasConceptScore W2037422435C171250308 @default.
- W2037422435 hasConceptScore W2037422435C185592680 @default.
- W2037422435 hasConceptScore W2037422435C19067145 @default.
- W2037422435 hasConceptScore W2037422435C191897082 @default.
- W2037422435 hasConceptScore W2037422435C192191005 @default.
- W2037422435 hasConceptScore W2037422435C192562407 @default.
- W2037422435 hasConceptScore W2037422435C199289684 @default.
- W2037422435 hasConceptScore W2037422435C2777289219 @default.
- W2037422435 hasConceptScore W2037422435C2779851234 @default.
- W2037422435 hasConceptScore W2037422435C37982897 @default.
- W2037422435 hasConceptScore W2037422435C43617362 @default.
- W2037422435 hasConceptScore W2037422435C46275449 @default.
- W2037422435 hasConceptScore W2037422435C47908070 @default.
- W2037422435 hasConceptScore W2037422435C87976508 @default.
- W2037422435 hasConceptScore W2037422435C96410337 @default.
- W2037422435 hasIssue "3" @default.
- W2037422435 hasLocation W20374224351 @default.
- W2037422435 hasOpenAccess W2037422435 @default.