- W2040207637 abstract "Abstract The electrical resistivity of Cu-15 at.%Pd alloys ordered and disordered by annealing at various temperatures and immediately quenched, is measured, and differential scanning calorimetry (DSC) of each sample is performed to obtain the order parameters at various temperatures. Electrical resistivity measurement reveals that the anomalous increase in the electrical resistivity just below the order-disorder transition temperature Tc is commonly observed in all samples, irrespective of the quenching temperature. By the DSC measurement of each sample it is also shown that the change in the order parameter S with the quenching temperature is very similar to that reported in other superlattice alloys such as Can. By relating the residual resistivity and the temperature coefficient of the resistivity to S for each sample, it is derived that the residual resistivity decreases approximately in proportion to S 4.6, and the temperature coefficient increases properly in proportion to S 2 as the temperature is raised. Further, it is found that the resistivity versus temperature curve calculated from the change in the S during heating using the above relationships is in good agreement with the experimental curve obtained directly by the resistivity measurement. By combining this fact with the antiphase domain structure reported previously by the present authors, it is concluded that the anomalous increase in the resistivity just below Tc in Cu-15 at.%Pd alloys can be ascribed mainly to the larger temperature coefficient of resistivity in the ordered state than in the disordered state." @default.
- W2040207637 created "2016-06-24" @default.
- W2040207637 creator A5032763375 @default.
- W2040207637 creator A5081346703 @default.
- W2040207637 creator A5084017516 @default.
- W2040207637 date "1995-01-01" @default.
- W2040207637 modified "2023-10-16" @default.
- W2040207637 title "Relations between the electrical resistivity changes and the thermal behaviour in ordered Cu-15at.%Pd alloys during continuous heating" @default.
- W2040207637 cites W1518288465 @default.
- W2040207637 cites W1970489534 @default.
- W2040207637 cites W1974024597 @default.
- W2040207637 cites W1982249310 @default.
- W2040207637 cites W2012401801 @default.
- W2040207637 cites W2012539262 @default.
- W2040207637 cites W2049240588 @default.
- W2040207637 cites W2064274431 @default.
- W2040207637 cites W2066746515 @default.
- W2040207637 cites W2079151880 @default.
- W2040207637 cites W2134624005 @default.
- W2040207637 cites W2160166198 @default.
- W2040207637 cites W2606160517 @default.
- W2040207637 cites W2606175480 @default.
- W2040207637 cites W2606272463 @default.
- W2040207637 cites W2606390935 @default.
- W2040207637 cites W2606929336 @default.
- W2040207637 cites W2607241934 @default.
- W2040207637 doi "https://doi.org/10.1080/01418639508240292" @default.
- W2040207637 hasPublicationYear "1995" @default.
- W2040207637 type Work @default.
- W2040207637 sameAs 2040207637 @default.
- W2040207637 citedByCount "3" @default.
- W2040207637 crossrefType "journal-article" @default.
- W2040207637 hasAuthorship W2040207637A5032763375 @default.
- W2040207637 hasAuthorship W2040207637A5081346703 @default.
- W2040207637 hasAuthorship W2040207637A5084017516 @default.
- W2040207637 hasConcept C121332964 @default.
- W2040207637 hasConcept C121745418 @default.
- W2040207637 hasConcept C159985019 @default.
- W2040207637 hasConcept C16643434 @default.
- W2040207637 hasConcept C191897082 @default.
- W2040207637 hasConcept C192562407 @default.
- W2040207637 hasConcept C26873012 @default.
- W2040207637 hasConcept C2777855556 @default.
- W2040207637 hasConcept C2780911149 @default.
- W2040207637 hasConcept C39519442 @default.
- W2040207637 hasConcept C62520636 @default.
- W2040207637 hasConcept C69990965 @default.
- W2040207637 hasConcept C91881484 @default.
- W2040207637 hasConcept C97355855 @default.
- W2040207637 hasConceptScore W2040207637C121332964 @default.
- W2040207637 hasConceptScore W2040207637C121745418 @default.
- W2040207637 hasConceptScore W2040207637C159985019 @default.
- W2040207637 hasConceptScore W2040207637C16643434 @default.
- W2040207637 hasConceptScore W2040207637C191897082 @default.
- W2040207637 hasConceptScore W2040207637C192562407 @default.
- W2040207637 hasConceptScore W2040207637C26873012 @default.
- W2040207637 hasConceptScore W2040207637C2777855556 @default.
- W2040207637 hasConceptScore W2040207637C2780911149 @default.
- W2040207637 hasConceptScore W2040207637C39519442 @default.
- W2040207637 hasConceptScore W2040207637C62520636 @default.
- W2040207637 hasConceptScore W2040207637C69990965 @default.
- W2040207637 hasConceptScore W2040207637C91881484 @default.
- W2040207637 hasConceptScore W2040207637C97355855 @default.
- W2040207637 hasIssue "1" @default.
- W2040207637 hasLocation W20402076371 @default.
- W2040207637 hasOpenAccess W2040207637 @default.
- W2040207637 hasPrimaryLocation W20402076371 @default.
- W2040207637 hasRelatedWork W2020623472 @default.
- W2040207637 hasRelatedWork W2030619169 @default.
- W2040207637 hasRelatedWork W2040207637 @default.
- W2040207637 hasRelatedWork W2061505218 @default.
- W2040207637 hasRelatedWork W2077354285 @default.
- W2040207637 hasRelatedWork W2081754359 @default.
- W2040207637 hasRelatedWork W2084422496 @default.
- W2040207637 hasRelatedWork W2084478771 @default.
- W2040207637 hasRelatedWork W2091249699 @default.
- W2040207637 hasRelatedWork W2131198404 @default.
- W2040207637 hasVolume "71" @default.
- W2040207637 isParatext "false" @default.
- W2040207637 isRetracted "false" @default.
- W2040207637 magId "2040207637" @default.
- W2040207637 workType "article" @default.