- W2040286105 abstract "In this paper, alloy with composition of MgMnAlZnCu was designed by using the strategy of equiatomic ratio and high entropy of mixing. The microstructure and mechanical parameters of the new high entropy alloy cooling in three conditions were studied. The alloy was prepared by induction melting and then it was cast in copper molds in air, water and salt water respectively. The microstructure and properties of alloy samples were examined by microhardness tester, XRD, TEM, SEM and testing machine for material strength. The results showed that the alloy was composed mainly of h.c.p and Al-Mn quasicrystal phases. The alloy exhibit high hardness (431HV-467HV) and high compression strength (428MPa-450MPa) at room temperature. The alloy was fragile and the strains were from 3.29% to 5.53%." @default.
- W2040286105 created "2016-06-24" @default.
- W2040286105 creator A5048741203 @default.
- W2040286105 creator A5050111080 @default.
- W2040286105 creator A5085828491 @default.
- W2040286105 date "2011-06-01" @default.
- W2040286105 modified "2023-10-18" @default.
- W2040286105 title "Microstructure and Mechanical Properties of MgMnAlZnCu High Entropy Alloy Cooling in Three Conditions" @default.
- W2040286105 cites W1964254287 @default.
- W2040286105 cites W1988619801 @default.
- W2040286105 cites W2003975937 @default.
- W2040286105 cites W2046200824 @default.
- W2040286105 cites W2047254669 @default.
- W2040286105 cites W2048392102 @default.
- W2040286105 cites W2050590457 @default.
- W2040286105 cites W2058085399 @default.
- W2040286105 cites W2062453104 @default.
- W2040286105 cites W2072976701 @default.
- W2040286105 cites W2074209728 @default.
- W2040286105 cites W2088918906 @default.
- W2040286105 cites W2112967203 @default.
- W2040286105 cites W2158836063 @default.
- W2040286105 doi "https://doi.org/10.4028/www.scientific.net/msf.686.235" @default.
- W2040286105 hasPublicationYear "2011" @default.
- W2040286105 type Work @default.
- W2040286105 sameAs 2040286105 @default.
- W2040286105 citedByCount "47" @default.
- W2040286105 countsByYear W20402861052014 @default.
- W2040286105 countsByYear W20402861052015 @default.
- W2040286105 countsByYear W20402861052016 @default.
- W2040286105 countsByYear W20402861052017 @default.
- W2040286105 countsByYear W20402861052018 @default.
- W2040286105 countsByYear W20402861052019 @default.
- W2040286105 countsByYear W20402861052020 @default.
- W2040286105 countsByYear W20402861052021 @default.
- W2040286105 countsByYear W20402861052022 @default.
- W2040286105 countsByYear W20402861052023 @default.
- W2040286105 crossrefType "journal-article" @default.
- W2040286105 hasAuthorship W2040286105A5048741203 @default.
- W2040286105 hasAuthorship W2040286105A5050111080 @default.
- W2040286105 hasAuthorship W2040286105A5085828491 @default.
- W2040286105 hasConcept C159985019 @default.
- W2040286105 hasConcept C165720898 @default.
- W2040286105 hasConcept C179133402 @default.
- W2040286105 hasConcept C191897082 @default.
- W2040286105 hasConcept C192562407 @default.
- W2040286105 hasConcept C2780026712 @default.
- W2040286105 hasConcept C65029150 @default.
- W2040286105 hasConcept C87976508 @default.
- W2040286105 hasConceptScore W2040286105C159985019 @default.
- W2040286105 hasConceptScore W2040286105C165720898 @default.
- W2040286105 hasConceptScore W2040286105C179133402 @default.
- W2040286105 hasConceptScore W2040286105C191897082 @default.
- W2040286105 hasConceptScore W2040286105C192562407 @default.
- W2040286105 hasConceptScore W2040286105C2780026712 @default.
- W2040286105 hasConceptScore W2040286105C65029150 @default.
- W2040286105 hasConceptScore W2040286105C87976508 @default.
- W2040286105 hasLocation W20402861051 @default.
- W2040286105 hasOpenAccess W2040286105 @default.
- W2040286105 hasPrimaryLocation W20402861051 @default.
- W2040286105 hasRelatedWork W2040286105 @default.
- W2040286105 hasRelatedWork W2252317227 @default.
- W2040286105 hasRelatedWork W2364995748 @default.
- W2040286105 hasRelatedWork W2370233740 @default.
- W2040286105 hasRelatedWork W2373304857 @default.
- W2040286105 hasRelatedWork W2374643716 @default.
- W2040286105 hasRelatedWork W2377428937 @default.
- W2040286105 hasRelatedWork W2390800713 @default.
- W2040286105 hasRelatedWork W2392620835 @default.
- W2040286105 hasRelatedWork W2619888893 @default.
- W2040286105 hasVolume "686" @default.
- W2040286105 isParatext "false" @default.
- W2040286105 isRetracted "false" @default.
- W2040286105 magId "2040286105" @default.
- W2040286105 workType "article" @default.