- W2040296722 abstract "Surface damage thresholds of polished calcite crystals were measured with a pulsed ruby laser at the wavelength of 694.3 nm. Three grades of calcite used for laser polarizers were tested: Grade A, Schlieren-Free, and Scatter-Free, as characterized by the manufacturer, Karl Lambrecht Corporation of Chicago. The test samples were cut and polished with the surfaces parallel to the optic axis. Sample dimensions were 1 cm X 1 cm and 2 to 3 mm thick. The ruby laser oscillator was passively Q-switched to produce 12-ns pulses in a single-transverse and longitudinal mode. Samples were irradiated at near-normal incidence to the 1-cm2 surfaces with a laser 1/e2 spot diameter of approximately 0.12 mm. Tests were conducted with a single shot per site, and photoelectric detection of a laser- induced surface spark was used as a sensitive method for detecting the onset of damage. Damage threshold of 30, 60, and 50 mJ/cm2, were determined for the three grades, respectively. No significant threshold differences were observed between test with the laser polarization parallel and perpendicular to the optic axis. Laser-induced damage, visible by scattering of a collinear He-Ne laser beam, was most frequently observed at the rear surfaces, although it sometimes occurred at the front surface alone or in the interior. On the basis of standing wave electric-field analysis, the predicted energy density at the rear surface was more than twice that at the front surface, and laser damage at the rear surface was expected to occur at a correspondingly lower fluence. Early damage at randomly distributed surface imperfections appeared to preclude such a consistent correlation.© (1997) COPYRIGHT SPIE--The International Society for Optical Engineering. Downloading of the abstract is permitted for personal use only." @default.
- W2040296722 created "2016-06-24" @default.
- W2040296722 creator A5012647650 @default.
- W2040296722 creator A5036818147 @default.
- W2040296722 date "1997-05-13" @default.
- W2040296722 modified "2023-09-23" @default.
- W2040296722 title "<title>Surface damage resistance of calcite crystals to nanosecond-pulse 694-nm laser radiation</title>" @default.
- W2040296722 doi "https://doi.org/10.1117/12.274295" @default.
- W2040296722 hasPublicationYear "1997" @default.
- W2040296722 type Work @default.
- W2040296722 sameAs 2040296722 @default.
- W2040296722 citedByCount "0" @default.
- W2040296722 crossrefType "proceedings-article" @default.
- W2040296722 hasAuthorship W2040296722A5012647650 @default.
- W2040296722 hasAuthorship W2040296722A5036818147 @default.
- W2040296722 hasConcept C111337013 @default.
- W2040296722 hasConcept C120665830 @default.
- W2040296722 hasConcept C121332964 @default.
- W2040296722 hasConcept C169150495 @default.
- W2040296722 hasConcept C185544564 @default.
- W2040296722 hasConcept C192562407 @default.
- W2040296722 hasConcept C2778613923 @default.
- W2040296722 hasConcept C49040817 @default.
- W2040296722 hasConcept C520434653 @default.
- W2040296722 hasConcept C6260449 @default.
- W2040296722 hasConceptScore W2040296722C111337013 @default.
- W2040296722 hasConceptScore W2040296722C120665830 @default.
- W2040296722 hasConceptScore W2040296722C121332964 @default.
- W2040296722 hasConceptScore W2040296722C169150495 @default.
- W2040296722 hasConceptScore W2040296722C185544564 @default.
- W2040296722 hasConceptScore W2040296722C192562407 @default.
- W2040296722 hasConceptScore W2040296722C2778613923 @default.
- W2040296722 hasConceptScore W2040296722C49040817 @default.
- W2040296722 hasConceptScore W2040296722C520434653 @default.
- W2040296722 hasConceptScore W2040296722C6260449 @default.
- W2040296722 hasLocation W20402967221 @default.
- W2040296722 hasOpenAccess W2040296722 @default.
- W2040296722 hasPrimaryLocation W20402967221 @default.
- W2040296722 hasRelatedWork W1666233370 @default.
- W2040296722 hasRelatedWork W2009496238 @default.
- W2040296722 hasRelatedWork W2013518214 @default.
- W2040296722 hasRelatedWork W2022700244 @default.
- W2040296722 hasRelatedWork W2050619634 @default.
- W2040296722 hasRelatedWork W2056205737 @default.
- W2040296722 hasRelatedWork W2067802027 @default.
- W2040296722 hasRelatedWork W2126474395 @default.
- W2040296722 hasRelatedWork W2127306438 @default.
- W2040296722 hasRelatedWork W2139831258 @default.
- W2040296722 hasRelatedWork W2370287191 @default.
- W2040296722 hasRelatedWork W2370331498 @default.
- W2040296722 hasRelatedWork W2371217108 @default.
- W2040296722 hasRelatedWork W2392677016 @default.
- W2040296722 hasRelatedWork W2506193649 @default.
- W2040296722 hasRelatedWork W2900505845 @default.
- W2040296722 hasRelatedWork W2945736542 @default.
- W2040296722 hasRelatedWork W294857316 @default.
- W2040296722 hasRelatedWork W3115482122 @default.
- W2040296722 hasRelatedWork W2045333659 @default.
- W2040296722 isParatext "false" @default.
- W2040296722 isRetracted "false" @default.
- W2040296722 magId "2040296722" @default.
- W2040296722 workType "article" @default.