- W2040702948 abstract "Low energy ion implantation of nitrogen into oxide free aluminium surfaces was used to obtain stoichiometric and pore-free AlN layers of about 8-10 nm thickness. The electrochemical stability of these layers was investigated by anodic cyclic voltammetry, pulse measurements and X-ray Photoelectron Spectroscopy (XPS). For comparison AlN layers prepared by Physical Vapor Deposition (PVD, thickness 2 μm) were examined as well. While AlN is hydrolysed at pH 14 as predicted by thermodynamics, electrochemical stability up to 1.6 V was observed in acetate buffer solution (pH 5.9). Surface analysis reveals that at potentials below 2 V, AlN is covered by an oxide layer of 2 nm. Molecular N 2 dissolved at the AlN/ Al 2 O 3 phase boundary was detected as a product of nitride decomposition. At higher anodic potentials, the oxide layer thickness increases whereas the AlN layer diminishes. Oxidation takes place in a two-step mechanism. Beyond a potential of 1.6 V, the electric field is sufficiently high to initiate the oxidation of N 3- via tunnelling. Although migration of mobile ions (Al 3+ , N 3- , O 2- ) starts, the layer composition remains nearly unchanged. At potentials above 4 V, high-field oxide growth starts until the nitride is completely decomposed. In contrast, the properties of PVD layers on steel substrates are determined mainly by the porosity of the coating. Due to substrate properties, iron dissolution and transpassive oxygen evolution were observed." @default.
- W2040702948 created "2016-06-24" @default.
- W2040702948 creator A5023850635 @default.
- W2040702948 creator A5065563517 @default.
- W2040702948 creator A5088853865 @default.
- W2040702948 date "1998-01-01" @default.
- W2040702948 modified "2023-09-27" @default.
- W2040702948 title "Corrosion and XPS investigations of nitrogen implanted aluminium" @default.
- W2040702948 cites W112633697 @default.
- W2040702948 cites W1988548511 @default.
- W2040702948 cites W2012900432 @default.
- W2040702948 cites W2022646362 @default.
- W2040702948 cites W2061513912 @default.
- W2040702948 cites W2093969955 @default.
- W2040702948 cites W2156472944 @default.
- W2040702948 cites W2726542089 @default.
- W2040702948 cites W3089485186 @default.
- W2040702948 cites W612840647 @default.
- W2040702948 doi "https://doi.org/10.1016/s0013-4686(97)00243-0" @default.
- W2040702948 hasPublicationYear "1998" @default.
- W2040702948 type Work @default.
- W2040702948 sameAs 2040702948 @default.
- W2040702948 citedByCount "16" @default.
- W2040702948 countsByYear W20407029482013 @default.
- W2040702948 countsByYear W20407029482015 @default.
- W2040702948 countsByYear W20407029482019 @default.
- W2040702948 countsByYear W20407029482020 @default.
- W2040702948 crossrefType "journal-article" @default.
- W2040702948 hasAuthorship W2040702948A5023850635 @default.
- W2040702948 hasAuthorship W2040702948A5065563517 @default.
- W2040702948 hasAuthorship W2040702948A5088853865 @default.
- W2040702948 hasConcept C127413603 @default.
- W2040702948 hasConcept C175708663 @default.
- W2040702948 hasConcept C178790620 @default.
- W2040702948 hasConcept C185592680 @default.
- W2040702948 hasConcept C191897082 @default.
- W2040702948 hasConcept C192562407 @default.
- W2040702948 hasConcept C20625102 @default.
- W2040702948 hasConcept C42360764 @default.
- W2040702948 hasConcept C513153333 @default.
- W2040702948 hasConcept C537208039 @default.
- W2040702948 hasConceptScore W2040702948C127413603 @default.
- W2040702948 hasConceptScore W2040702948C175708663 @default.
- W2040702948 hasConceptScore W2040702948C178790620 @default.
- W2040702948 hasConceptScore W2040702948C185592680 @default.
- W2040702948 hasConceptScore W2040702948C191897082 @default.
- W2040702948 hasConceptScore W2040702948C192562407 @default.
- W2040702948 hasConceptScore W2040702948C20625102 @default.
- W2040702948 hasConceptScore W2040702948C42360764 @default.
- W2040702948 hasConceptScore W2040702948C513153333 @default.
- W2040702948 hasConceptScore W2040702948C537208039 @default.
- W2040702948 hasIssue "1-2" @default.
- W2040702948 hasLocation W20407029481 @default.
- W2040702948 hasOpenAccess W2040702948 @default.
- W2040702948 hasPrimaryLocation W20407029481 @default.
- W2040702948 hasRelatedWork W1978019578 @default.
- W2040702948 hasRelatedWork W2039464635 @default.
- W2040702948 hasRelatedWork W2042185635 @default.
- W2040702948 hasRelatedWork W2060084043 @default.
- W2040702948 hasRelatedWork W2358634692 @default.
- W2040702948 hasRelatedWork W2393931971 @default.
- W2040702948 hasRelatedWork W2580545854 @default.
- W2040702948 hasRelatedWork W3097783663 @default.
- W2040702948 hasRelatedWork W640708979 @default.
- W2040702948 hasRelatedWork W2549791658 @default.
- W2040702948 hasVolume "43" @default.
- W2040702948 isParatext "false" @default.
- W2040702948 isRetracted "false" @default.
- W2040702948 magId "2040702948" @default.
- W2040702948 workType "article" @default.