• W2043171613 abstract "A new type of anode, a Ni framework coated with Sm-doped ceria (SDC), was developed for direct utilization of methane fuel in low-temperature solid oxide fuel cells (SOFCs) with thin-film SDC electrolytes. The coated SDC was prepared with an ion impregnating method and the electrolyte films were fabricated with a co-pressing and co-firing technique. The impregnating process produced an ideal anode microstructure where nickel particles were effectively connected and uniformly covered with nanosized SDC. This anode microstructure was believed to enlarge the triple-phase boundaries and therefore enhance the anode performance. The cell performance was much higher than that of a conventional fuel cell with a Ni-SDC composite anode. In addition, the performance increased with impregnated SDC loading up to a maximum at 20 mg cm−2, indicating that the coated SDC is the contributing factor for the enhanced fuel cell performance. Power density as high as 571 and 353 mW cm−2 were obtained at 600 °C when humidified hydrogen and methane were used as fuels, respectively. The stability of the cell also increased with the SDC loading. No significant degradation was observed for anodes coated with 20 and 25 mg cm−2 SDC. This verifies that the coated SDC electrodes are very effective in suppressing catalytic carbon formation by blocking methane from approaching the Ni, which is catalytically active towards methane pyrolysis. The high performance of this anode shows high promise in the developing field of direct hydrocarbon SOFCs." @default.
• W2043171613 created "2016-06-24" @default.
• W2043171613 creator A5036016266 @default.
• W2043171613 creator A5037437663 @default.
• W2043171613 creator A5068308955 @default.
• W2043171613 creator A5073738793 @default.
• W2043171613 creator A5085679486 @default.
• W2043171613 date "2006-10-01" @default.
• W2043171613 modified "2023-10-07" @default.
• W2043171613 title "Ceria coated Ni as anodes for direct utilization of methane in low-temperature solid oxide fuel cells" @default.
• W2043171613 cites W1488734711 @default.
• W2043171613 cites W1624483887 @default.
• W2043171613 cites W1794469750 @default.
• W2043171613 cites W1971273014 @default.
• W2043171613 cites W1978126170 @default.
• W2043171613 cites W1980047920 @default.
• W2043171613 cites W1988760611 @default.
• W2043171613 cites W1994065157 @default.
• W2043171613 cites W2026680093 @default.
• W2043171613 cites W2031544139 @default.
• W2043171613 cites W2080387012 @default.
• W2043171613 cites W2085368049 @default.
• W2043171613 cites W2097129107 @default.
• W2043171613 cites W2132882481 @default.
• W2043171613 cites W2138952979 @default.
• W2043171613 cites W2140210416 @default.
• W2043171613 cites W2143908655 @default.
• W2043171613 cites W2151040250 @default.
• W2043171613 cites W2153042253 @default.
• W2043171613 cites W2153957004 @default.
• W2043171613 cites W2159844602 @default.
• W2043171613 cites W4211089104 @default.
• W2043171613 cites W4237246242 @default.
• W2043171613 cites W4362215244 @default.
• W2043171613 doi "https://doi.org/10.1016/j.jpowsour.2006.02.020" @default.
• W2043171613 hasPublicationYear "2006" @default.
• W2043171613 type Work @default.
• W2043171613 sameAs 2043171613 @default.
• W2043171613 citedByCount "78" @default.
• W2043171613 countsByYear W20431716132012 @default.
• W2043171613 countsByYear W20431716132013 @default.
• W2043171613 countsByYear W20431716132014 @default.
• W2043171613 countsByYear W20431716132015 @default.
• W2043171613 countsByYear W20431716132016 @default.
• W2043171613 countsByYear W20431716132017 @default.
• W2043171613 countsByYear W20431716132018 @default.
• W2043171613 countsByYear W20431716132019 @default.
• W2043171613 countsByYear W20431716132020 @default.
• W2043171613 countsByYear W20431716132021 @default.
• W2043171613 countsByYear W20431716132022 @default.
• W2043171613 countsByYear W20431716132023 @default.
• W2043171613 crossrefType "journal-article" @default.
• W2043171613 hasAuthorship W2043171613A5036016266 @default.
• W2043171613 hasAuthorship W2043171613A5037437663 @default.
• W2043171613 hasAuthorship W2043171613A5068308955 @default.
• W2043171613 hasAuthorship W2043171613A5073738793 @default.
• W2043171613 hasAuthorship W2043171613A5085679486 @default.
• W2043171613 hasConcept C104779481 @default.
• W2043171613 hasConcept C127413603 @default.
• W2043171613 hasConcept C140205800 @default.
• W2043171613 hasConcept C147789679 @default.
• W2043171613 hasConcept C159985019 @default.
• W2043171613 hasConcept C160331763 @default.
• W2043171613 hasConcept C17525397 @default.
• W2043171613 hasConcept C178790620 @default.
• W2043171613 hasConcept C185592680 @default.
• W2043171613 hasConcept C191897082 @default.
• W2043171613 hasConcept C192562407 @default.
• W2043171613 hasConcept C2778456004 @default.
• W2043171613 hasConcept C2779851234 @default.
• W2043171613 hasConcept C36759035 @default.
• W2043171613 hasConcept C42360764 @default.
• W2043171613 hasConcept C512968161 @default.
• W2043171613 hasConcept C516920438 @default.
• W2043171613 hasConcept C68801617 @default.
• W2043171613 hasConcept C87976508 @default.
• W2043171613 hasConcept C89395315 @default.
• W2043171613 hasConceptScore W2043171613C104779481 @default.
• W2043171613 hasConceptScore W2043171613C127413603 @default.
• W2043171613 hasConceptScore W2043171613C140205800 @default.
• W2043171613 hasConceptScore W2043171613C147789679 @default.
• W2043171613 hasConceptScore W2043171613C159985019 @default.
• W2043171613 hasConceptScore W2043171613C160331763 @default.
• W2043171613 hasConceptScore W2043171613C17525397 @default.
• W2043171613 hasConceptScore W2043171613C178790620 @default.
• W2043171613 hasConceptScore W2043171613C185592680 @default.
• W2043171613 hasConceptScore W2043171613C191897082 @default.
• W2043171613 hasConceptScore W2043171613C192562407 @default.
• W2043171613 hasConceptScore W2043171613C2778456004 @default.
• W2043171613 hasConceptScore W2043171613C2779851234 @default.
• W2043171613 hasConceptScore W2043171613C36759035 @default.
• W2043171613 hasConceptScore W2043171613C42360764 @default.
• W2043171613 hasConceptScore W2043171613C512968161 @default.
• W2043171613 hasConceptScore W2043171613C516920438 @default.
• W2043171613 hasConceptScore W2043171613C68801617 @default.
• W2043171613 hasConceptScore W2043171613C87976508 @default.
• W2043171613 hasConceptScore W2043171613C89395315 @default.
• W2043171613 hasFunder F4320321001 @default.

• next