- W2043946006 abstract "A comparison of the surface roughness factor (SRF), determined by xenon adsorption, has been made for the surfaces of 304 and 316 stainless steels irradiated with 100 keV helium ions. The variation of the SRF value was measured as a function of ion dose. Topological changes of the irradiated surfaces were determined by scanning electron microscopy (SEM). The SRF values were found to increase with increasing ion dose on both of the specimens. The unirradiated surface has SRF values of 2.7 and 1.9 for 304 SS and 316 SS, respectively. After the irradiation to a dose of 0.2 C/cm2 and 0.5 C/cm2 at room temperature, SRF increased to 25.6 and 28.1, respectively, on 304 SS, and 7.8 and 14.7, respectively, on 316 SS. SEM photographs revealed that the surfaces were heavily damaged by blistering and flaking for these ion doses, but differently for the two specimens. The average blister diameter observed on the irradiated 304 SS specimen was found to be about three times larger than that observed on the 316 SS specimen. The average number of exfoliated surface layers was about 3.5 for 304 SS, while it was 15 for 316 SS for the identical ion dose of 0.5 C/cm2. The differences in the SRF values observed on the two materials can be explained by the size and density of blisters and flakes, and the number of ruptured blister skins sticking to the surface." @default.
- W2043946006 created "2016-06-24" @default.
- W2043946006 creator A5016530711 @default.
- W2043946006 creator A5023952072 @default.
- W2043946006 creator A5032445352 @default.
- W2043946006 creator A5047155721 @default.
- W2043946006 creator A5088123290 @default.
- W2043946006 date "1981-01-01" @default.
- W2043946006 modified "2023-09-26" @default.
- W2043946006 title "Surface roughness factor measurements of 304 and 316 stainless steels with helium ion irradiation" @default.
- W2043946006 cites W1995805852 @default.
- W2043946006 cites W2010182288 @default.
- W2043946006 cites W2012293461 @default.
- W2043946006 cites W2014399962 @default.
- W2043946006 cites W2020864457 @default.
- W2043946006 cites W2041356200 @default.
- W2043946006 cites W2043996615 @default.
- W2043946006 cites W2066353843 @default.
- W2043946006 cites W2069069094 @default.
- W2043946006 cites W2070067526 @default.
- W2043946006 cites W2092183064 @default.
- W2043946006 cites W2116445599 @default.
- W2043946006 cites W2148176134 @default.
- W2043946006 cites W2256211498 @default.
- W2043946006 doi "https://doi.org/10.1016/0022-3115(82)90639-0" @default.
- W2043946006 hasPublicationYear "1981" @default.
- W2043946006 type Work @default.
- W2043946006 sameAs 2043946006 @default.
- W2043946006 citedByCount "7" @default.
- W2043946006 crossrefType "journal-article" @default.
- W2043946006 hasAuthorship W2043946006A5016530711 @default.
- W2043946006 hasAuthorship W2043946006A5023952072 @default.
- W2043946006 hasAuthorship W2043946006A5032445352 @default.
- W2043946006 hasAuthorship W2043946006A5047155721 @default.
- W2043946006 hasAuthorship W2043946006A5088123290 @default.
- W2043946006 hasConcept C107365816 @default.
- W2043946006 hasConcept C111337013 @default.
- W2043946006 hasConcept C113196181 @default.
- W2043946006 hasConcept C121332964 @default.
- W2043946006 hasConcept C145148216 @default.
- W2043946006 hasConcept C159985019 @default.
- W2043946006 hasConcept C178790620 @default.
- W2043946006 hasConcept C185544564 @default.
- W2043946006 hasConcept C185592680 @default.
- W2043946006 hasConcept C192562407 @default.
- W2043946006 hasConcept C26771246 @default.
- W2043946006 hasConcept C2780949179 @default.
- W2043946006 hasConcept C43617362 @default.
- W2043946006 hasConcept C546029482 @default.
- W2043946006 hasConcept C548442186 @default.
- W2043946006 hasConcept C71039073 @default.
- W2043946006 hasConceptScore W2043946006C107365816 @default.
- W2043946006 hasConceptScore W2043946006C111337013 @default.
- W2043946006 hasConceptScore W2043946006C113196181 @default.
- W2043946006 hasConceptScore W2043946006C121332964 @default.
- W2043946006 hasConceptScore W2043946006C145148216 @default.
- W2043946006 hasConceptScore W2043946006C159985019 @default.
- W2043946006 hasConceptScore W2043946006C178790620 @default.
- W2043946006 hasConceptScore W2043946006C185544564 @default.
- W2043946006 hasConceptScore W2043946006C185592680 @default.
- W2043946006 hasConceptScore W2043946006C192562407 @default.
- W2043946006 hasConceptScore W2043946006C26771246 @default.
- W2043946006 hasConceptScore W2043946006C2780949179 @default.
- W2043946006 hasConceptScore W2043946006C43617362 @default.
- W2043946006 hasConceptScore W2043946006C546029482 @default.
- W2043946006 hasConceptScore W2043946006C548442186 @default.
- W2043946006 hasConceptScore W2043946006C71039073 @default.
- W2043946006 hasLocation W20439460061 @default.
- W2043946006 hasOpenAccess W2043946006 @default.
- W2043946006 hasPrimaryLocation W20439460061 @default.
- W2043946006 hasRelatedWork W1512319868 @default.
- W2043946006 hasRelatedWork W1988234332 @default.
- W2043946006 hasRelatedWork W2009613684 @default.
- W2043946006 hasRelatedWork W2009908443 @default.
- W2043946006 hasRelatedWork W2196605515 @default.
- W2043946006 hasRelatedWork W2351696714 @default.
- W2043946006 hasRelatedWork W2374963277 @default.
- W2043946006 hasRelatedWork W2387616028 @default.
- W2043946006 hasRelatedWork W3018992776 @default.
- W2043946006 hasRelatedWork W3144367999 @default.
- W2043946006 hasVolume "103" @default.
- W2043946006 isParatext "false" @default.
- W2043946006 isRetracted "false" @default.
- W2043946006 magId "2043946006" @default.
- W2043946006 workType "article" @default.