- W2047464861 abstract "Electrical fatigue tests have been conducted on PLZT ferroelectric ceramics. It was found that the higher the applied electrical field magnitude, the faster the Pr decreases; the samples under the same electrical field magnitude but with square wave have higher fatigue rate than that of sine wave. It was observed that at low frequency of applied field (50Hz and 500Hz), the polarization decreased very quickly and dropped below 70% of the original value within 106.2 switching cycles, however, when fatigue test were conducted at high frequencies of 100kHz and 300kHz, the polarization did not change significantly even after 109 cycles. The SEM analysis indicated that the facture mode was mainly of trans-granular for the virgin non-fatigued sample, while of inter-granular for the fatigue sample. The quantitative information on the 90° domain switching was measured in situ using X-ray diffraction. The effects of electrical characters on electrical fatigue behavior were explained according to the mechanism of electrical fatigue in PLZT ferroelectric ceramics." @default.
- W2047464861 created "2016-06-24" @default.
- W2047464861 creator A5000037532 @default.
- W2047464861 creator A5003258061 @default.
- W2047464861 creator A5011751219 @default.
- W2047464861 creator A5046914885 @default.
- W2047464861 creator A5050095797 @default.
- W2047464861 date "2007-02-01" @default.
- W2047464861 modified "2023-09-27" @default.
- W2047464861 title "Effects of Electrical Characters on Electrical Fatigue Behavior in PLZT Ferroelectric Ceramics" @default.
- W2047464861 cites W1980270939 @default.
- W2047464861 cites W2035349998 @default.
- W2047464861 cites W2068523141 @default.
- W2047464861 cites W2069856143 @default.
- W2047464861 cites W2079958464 @default.
- W2047464861 cites W2093199128 @default.
- W2047464861 cites W4246749317 @default.
- W2047464861 doi "https://doi.org/10.4028/www.scientific.net/kem.280-283.159" @default.
- W2047464861 hasPublicationYear "2007" @default.
- W2047464861 type Work @default.
- W2047464861 sameAs 2047464861 @default.
- W2047464861 citedByCount "4" @default.
- W2047464861 crossrefType "journal-article" @default.
- W2047464861 hasAuthorship W2047464861A5000037532 @default.
- W2047464861 hasAuthorship W2047464861A5003258061 @default.
- W2047464861 hasAuthorship W2047464861A5011751219 @default.
- W2047464861 hasAuthorship W2047464861A5046914885 @default.
- W2047464861 hasAuthorship W2047464861A5050095797 @default.
- W2047464861 hasConcept C119599485 @default.
- W2047464861 hasConcept C121332964 @default.
- W2047464861 hasConcept C127413603 @default.
- W2047464861 hasConcept C133386390 @default.
- W2047464861 hasConcept C134132462 @default.
- W2047464861 hasConcept C147789679 @default.
- W2047464861 hasConcept C159985019 @default.
- W2047464861 hasConcept C165801399 @default.
- W2047464861 hasConcept C185592680 @default.
- W2047464861 hasConcept C192562407 @default.
- W2047464861 hasConcept C205049153 @default.
- W2047464861 hasConcept C2777949652 @default.
- W2047464861 hasConcept C49040817 @default.
- W2047464861 hasConcept C60799052 @default.
- W2047464861 hasConcept C62520636 @default.
- W2047464861 hasConcept C66907618 @default.
- W2047464861 hasConcept C79090758 @default.
- W2047464861 hasConcept C96352100 @default.
- W2047464861 hasConceptScore W2047464861C119599485 @default.
- W2047464861 hasConceptScore W2047464861C121332964 @default.
- W2047464861 hasConceptScore W2047464861C127413603 @default.
- W2047464861 hasConceptScore W2047464861C133386390 @default.
- W2047464861 hasConceptScore W2047464861C134132462 @default.
- W2047464861 hasConceptScore W2047464861C147789679 @default.
- W2047464861 hasConceptScore W2047464861C159985019 @default.
- W2047464861 hasConceptScore W2047464861C165801399 @default.
- W2047464861 hasConceptScore W2047464861C185592680 @default.
- W2047464861 hasConceptScore W2047464861C192562407 @default.
- W2047464861 hasConceptScore W2047464861C205049153 @default.
- W2047464861 hasConceptScore W2047464861C2777949652 @default.
- W2047464861 hasConceptScore W2047464861C49040817 @default.
- W2047464861 hasConceptScore W2047464861C60799052 @default.
- W2047464861 hasConceptScore W2047464861C62520636 @default.
- W2047464861 hasConceptScore W2047464861C66907618 @default.
- W2047464861 hasConceptScore W2047464861C79090758 @default.
- W2047464861 hasConceptScore W2047464861C96352100 @default.
- W2047464861 hasLocation W20474648611 @default.
- W2047464861 hasOpenAccess W2047464861 @default.
- W2047464861 hasPrimaryLocation W20474648611 @default.
- W2047464861 hasRelatedWork W1595466225 @default.
- W2047464861 hasRelatedWork W1994076047 @default.
- W2047464861 hasRelatedWork W2013705760 @default.
- W2047464861 hasRelatedWork W2061552984 @default.
- W2047464861 hasRelatedWork W2182688652 @default.
- W2047464861 hasRelatedWork W2281145519 @default.
- W2047464861 hasRelatedWork W2602905260 @default.
- W2047464861 hasRelatedWork W3183729852 @default.
- W2047464861 hasRelatedWork W4385302714 @default.
- W2047464861 hasRelatedWork W84992954 @default.
- W2047464861 hasVolume "280-283" @default.
- W2047464861 isParatext "false" @default.
- W2047464861 isRetracted "false" @default.
- W2047464861 magId "2047464861" @default.
- W2047464861 workType "article" @default.