- W2051279838 abstract "This work aims at investigating the effect of thermal aging on tensile properties of three-dimension (3D) and five-direction braided carbon fiber/BMI resin composites prepared by resin transfer molding (RTM) process. The influence of high temperature on the tensile strength and the failure mechanisms of un-aged and aged composites were studied, respectively. As for the thermal aging condition, 180 for 24h was selected. The tensile strength of both un-aged and aged specimens were tested by SHIMADZU universal material testing machine at room temperature. The fracture modes of specimens were observed by scanning electron microscopy (SEM). It was found that the tensile load at break and tensile strength decreased after ageing. From the SEM views of the failed samples, the fracture surface presented hackles which were specific to the debonding of the interface between fibers and matrix. A lot of fibers were pulled-out in the aged state specimen. It can be confirmed that the failure occurred at the fiber/matrix interface and the fiber/matrix interface seemed to be weak in aged carbon fabrics reinforced BMI composites." @default.
- W2051279838 created "2016-06-24" @default.
- W2051279838 creator A5028697859 @default.
- W2051279838 creator A5033723799 @default.
- W2051279838 creator A5037989560 @default.
- W2051279838 creator A5075133682 @default.
- W2051279838 creator A5080733133 @default.
- W2051279838 creator A5091092296 @default.
- W2051279838 date "2010-10-01" @default.
- W2051279838 modified "2023-10-16" @default.
- W2051279838 title "The Effect of Thermal Aging on Tensile Strength of Three-Dimension and Five-Direction Braided Carbon Fiber/BMI Composites" @default.
- W2051279838 cites W1981156647 @default.
- W2051279838 cites W2022207799 @default.
- W2051279838 cites W2023665901 @default.
- W2051279838 cites W2037726410 @default.
- W2051279838 cites W2074413379 @default.
- W2051279838 cites W2079049692 @default.
- W2051279838 cites W2093316942 @default.
- W2051279838 cites W2094512893 @default.
- W2051279838 cites W2127527558 @default.
- W2051279838 doi "https://doi.org/10.4028/www.scientific.net/amr.150-151.1139" @default.
- W2051279838 hasPublicationYear "2010" @default.
- W2051279838 type Work @default.
- W2051279838 sameAs 2051279838 @default.
- W2051279838 citedByCount "0" @default.
- W2051279838 crossrefType "journal-article" @default.
- W2051279838 hasAuthorship W2051279838A5028697859 @default.
- W2051279838 hasAuthorship W2051279838A5033723799 @default.
- W2051279838 hasAuthorship W2051279838A5037989560 @default.
- W2051279838 hasAuthorship W2051279838A5075133682 @default.
- W2051279838 hasAuthorship W2051279838A5080733133 @default.
- W2051279838 hasAuthorship W2051279838A5091092296 @default.
- W2051279838 hasConcept C112950240 @default.
- W2051279838 hasConcept C159985019 @default.
- W2051279838 hasConcept C182508753 @default.
- W2051279838 hasConcept C192562407 @default.
- W2051279838 hasConcept C26771246 @default.
- W2051279838 hasConcept C2780566776 @default.
- W2051279838 hasConcept C37696544 @default.
- W2051279838 hasConcept C43369102 @default.
- W2051279838 hasConcept C519885992 @default.
- W2051279838 hasConceptScore W2051279838C112950240 @default.
- W2051279838 hasConceptScore W2051279838C159985019 @default.
- W2051279838 hasConceptScore W2051279838C182508753 @default.
- W2051279838 hasConceptScore W2051279838C192562407 @default.
- W2051279838 hasConceptScore W2051279838C26771246 @default.
- W2051279838 hasConceptScore W2051279838C2780566776 @default.
- W2051279838 hasConceptScore W2051279838C37696544 @default.
- W2051279838 hasConceptScore W2051279838C43369102 @default.
- W2051279838 hasConceptScore W2051279838C519885992 @default.
- W2051279838 hasLocation W20512798381 @default.
- W2051279838 hasOpenAccess W2051279838 @default.
- W2051279838 hasPrimaryLocation W20512798381 @default.
- W2051279838 hasRelatedWork W1655377547 @default.
- W2051279838 hasRelatedWork W1975963801 @default.
- W2051279838 hasRelatedWork W2171517100 @default.
- W2051279838 hasRelatedWork W2385183841 @default.
- W2051279838 hasRelatedWork W2387616028 @default.
- W2051279838 hasRelatedWork W2975089001 @default.
- W2051279838 hasRelatedWork W3111019487 @default.
- W2051279838 hasRelatedWork W3148576459 @default.
- W2051279838 hasRelatedWork W4285407003 @default.
- W2051279838 hasRelatedWork W4312355382 @default.
- W2051279838 hasVolume "150-151" @default.
- W2051279838 isParatext "false" @default.
- W2051279838 isRetracted "false" @default.
- W2051279838 magId "2051279838" @default.
- W2051279838 workType "article" @default.