Matches in SemOpenAlex for { <https://semopenalex.org/work/W2053265036> ?p ?o ?g. }
- W2053265036 endingPage "18492" @default.
- W2053265036 startingPage "18479" @default.
- W2053265036 abstract "Multilayer structures of alternating thin titanium and tungsten oxide layers having dimensions of ∼20 nm have been fabricated from titanium alkoxide and various tungstate precursor solutions using the dip coating technique. Single, double, and triple layer titanate and tungstate thin films were deposited on silicon substrates, and these films were initially annealed at 400 °C. Structural and microstructural aspects of the films were investigated using a variety of techniques, including X-ray reflectometry, grazing incidence X-ray absorption spectroscopy (GIXAS), cross-sectional transmission electron microscopy (TEM), and secondary ion mass spectrometry. The dimensions of the films and the character of the interfaces were principally gauged by cross-sectional TEM and X-ray reflectometery. All films were continuous on a local scale and had relatively low surface roughness. At the treatment temperature of 400 °C, only the tungsten oxide component showed appreciable crystallinity. The multilayer films had relatively diffuse interfaces, even after annealing in air at this temperature. At these temperatures, easily measurable diffusion of tungsten into the titanium oxide component was observed, whereas the diffusion of titanium into the tungsten oxide component occurred to a lesser degree. At higher temperatures, interdiffusion of components was found to be significant. TEM, X-ray diffraction, and Ti K-edge GIXAS measurements indicated that annealing at 400 °C generated films in which the titanate component remained amorphous while the tungstate component crystallized in the tetragonal modification of WO3, which is normally stable only at high temperatures. Grazing incidence X-ray absorption spectroscopy allowed the degree of distortion of the tungsten oxygen polyhedra to be monitored as a function of depth into the film. The photoelectrochemical activity of the multilayer film electrodes was investigated, and the activity for water photo-oxidation was assessed. The photoelectrochemical response was greatest when crystalline WO3 was bounded on both sides by amorphous TiO2 layers. In this bounded state, WO3 had unique structural characteristics." @default.
- W2053265036 created "2016-06-24" @default.
- W2053265036 creator A5026753346 @default.
- W2053265036 creator A5028321794 @default.
- W2053265036 creator A5028766417 @default.
- W2053265036 creator A5038536852 @default.
- W2053265036 creator A5048804110 @default.
- W2053265036 creator A5066781741 @default.
- W2053265036 creator A5085390176 @default.
- W2053265036 creator A5087054588 @default.
- W2053265036 date "2007-11-29" @default.
- W2053265036 modified "2023-10-06" @default.
- W2053265036 title "Sol−Gel Tungsten Oxide/Titanium Oxide Multilayer Nanoheterostructured Thin Films: Structural and Photoelectrochemical Properties" @default.
- W2053265036 cites W1541889240 @default.
- W2053265036 cites W1964256568 @default.
- W2053265036 cites W1964485505 @default.
- W2053265036 cites W1965336726 @default.
- W2053265036 cites W1965534423 @default.
- W2053265036 cites W1966118057 @default.
- W2053265036 cites W1966224994 @default.
- W2053265036 cites W1967526418 @default.
- W2053265036 cites W1967828814 @default.
- W2053265036 cites W1967889874 @default.
- W2053265036 cites W1969549344 @default.
- W2053265036 cites W1971187049 @default.
- W2053265036 cites W1972981165 @default.
- W2053265036 cites W1973426739 @default.
- W2053265036 cites W1974713017 @default.
- W2053265036 cites W1975878087 @default.
- W2053265036 cites W1979458060 @default.
- W2053265036 cites W1980216394 @default.
- W2053265036 cites W1980547608 @default.
- W2053265036 cites W1981150487 @default.
- W2053265036 cites W1987754321 @default.
- W2053265036 cites W1991077818 @default.
- W2053265036 cites W1996358785 @default.
- W2053265036 cites W1996502169 @default.
- W2053265036 cites W1996551500 @default.
- W2053265036 cites W1996950168 @default.
- W2053265036 cites W1999832181 @default.
- W2053265036 cites W2002297285 @default.
- W2053265036 cites W2003248734 @default.
- W2053265036 cites W2006773423 @default.
- W2053265036 cites W2009981131 @default.
- W2053265036 cites W2020520201 @default.
- W2053265036 cites W2023876473 @default.
- W2053265036 cites W2024912484 @default.
- W2053265036 cites W2025730292 @default.
- W2053265036 cites W2025914103 @default.
- W2053265036 cites W2027711110 @default.
- W2053265036 cites W2028475557 @default.
- W2053265036 cites W2032471250 @default.
- W2053265036 cites W2033741219 @default.
- W2053265036 cites W2038921486 @default.
- W2053265036 cites W2042165078 @default.
- W2053265036 cites W2042492216 @default.
- W2053265036 cites W2044537745 @default.
- W2053265036 cites W2045069486 @default.
- W2053265036 cites W2045923049 @default.
- W2053265036 cites W2048904549 @default.
- W2053265036 cites W2050200664 @default.
- W2053265036 cites W2053589001 @default.
- W2053265036 cites W2054148497 @default.
- W2053265036 cites W2061029321 @default.
- W2053265036 cites W2064999376 @default.
- W2053265036 cites W2069925538 @default.
- W2053265036 cites W2070448667 @default.
- W2053265036 cites W2071694048 @default.
- W2053265036 cites W2073129013 @default.
- W2053265036 cites W2076864733 @default.
- W2053265036 cites W2076869235 @default.
- W2053265036 cites W2078269862 @default.
- W2053265036 cites W2081470582 @default.
- W2053265036 cites W2083972440 @default.
- W2053265036 cites W2085771955 @default.
- W2053265036 cites W2086529087 @default.
- W2053265036 cites W2088226920 @default.
- W2053265036 cites W2091551050 @default.
- W2053265036 cites W2092628956 @default.
- W2053265036 cites W2101534409 @default.
- W2053265036 cites W2119944602 @default.
- W2053265036 cites W2157184897 @default.
- W2053265036 cites W2322708922 @default.
- W2053265036 cites W2332577109 @default.
- W2053265036 cites W2474383008 @default.
- W2053265036 cites W2519271653 @default.
- W2053265036 cites W2769164846 @default.
- W2053265036 cites W2949966838 @default.
- W2053265036 cites W2952726272 @default.
- W2053265036 cites W3024874795 @default.
- W2053265036 doi "https://doi.org/10.1021/jp0729112" @default.
- W2053265036 hasPublicationYear "2007" @default.
- W2053265036 type Work @default.
- W2053265036 sameAs 2053265036 @default.
- W2053265036 citedByCount "19" @default.
- W2053265036 countsByYear W20532650362012 @default.
- W2053265036 countsByYear W20532650362014 @default.
- W2053265036 countsByYear W20532650362015 @default.