- W2053668323 abstract "The aim of this study was to evaluate the effect of fatigue on fracture toughness and phase transformation of yttria-stabilized zirconia polycrystal materials (Cercon and Lava). The specimens were tested for indentation fracture toughness either with or without being subjected to fatigue (20,000 cycles, 2 Hz, 200 N load). X-ray diffraction (XRD) analysis was used to examine the phase composition of specimens. The indentation images were analyzed using Raman spectroscopy at indentation center (p1), indentation corner (p2), points on crack 100 μm (p3), and 200 μm (p4) away from the corner and a point ∼80 μm away from the crack (p5). Fracture toughness results were statistically analyzed by two-way analysis of variance (ANOVA); XRD and Raman spectroscopy results were analyzed by three-way ANOVA. Fracture toughness of Cercon control (CC) and fatigue (CF) groups were 6.8 and 6.9 MPa√m, respectively, with no significant difference (p > 0.01). Fracture toughness of Lava fatigue (LF; 7.3 MPa√m) was significantly higher than Lava control (LC; p < 0.01). XRD analyses showed CC and LC consisted of tetragonal zirconia, monoclinic zirconia detected after fatigue. After indentation, relative amount of monoclinic phase significantly increased in CC, CF, and LC; decreased in LF. The Raman spectroscopy results indicated that monoclinic fraction was the highest at p2, subsequently at p1 and decreased at p3, p4, and p5 for all groups. Mechanical cycling increased fracture toughness of Cercon and Lava, the second being significant. Phase transformation was also detected after fatigue, which is higher in Lava. Analysis of indentations showed that transformation was highest was at the corner, second at center." @default.
- W2053668323 created "2016-06-24" @default.
- W2053668323 creator A5004056562 @default.
- W2053668323 creator A5014129390 @default.
- W2053668323 creator A5056594379 @default.
- W2053668323 creator A5062427703 @default.
- W2053668323 creator A5072804832 @default.
- W2053668323 date "2011-11-21" @default.
- W2053668323 modified "2023-10-10" @default.
- W2053668323 title "Effect of fatigue on fracture toughness and phase transformation of Y-TZP ceramics by X-ray diffraction and Raman spectroscopy" @default.
- W2053668323 cites W113300537 @default.
- W2053668323 cites W1968066676 @default.
- W2053668323 cites W1971093139 @default.
- W2053668323 cites W1978811067 @default.
- W2053668323 cites W1999463680 @default.
- W2053668323 cites W2001436882 @default.
- W2053668323 cites W2005994131 @default.
- W2053668323 cites W2014199252 @default.
- W2053668323 cites W2016934258 @default.
- W2053668323 cites W2018329346 @default.
- W2053668323 cites W2019131424 @default.
- W2053668323 cites W2019681230 @default.
- W2053668323 cites W2020163454 @default.
- W2053668323 cites W2027598314 @default.
- W2053668323 cites W2028860694 @default.
- W2053668323 cites W2036504935 @default.
- W2053668323 cites W2047145721 @default.
- W2053668323 cites W2055966447 @default.
- W2053668323 cites W2074173877 @default.
- W2053668323 cites W2075244942 @default.
- W2053668323 cites W2078955609 @default.
- W2053668323 cites W2082519204 @default.
- W2053668323 cites W2089071774 @default.
- W2053668323 cites W2092398968 @default.
- W2053668323 cites W2099357186 @default.
- W2053668323 cites W2107148626 @default.
- W2053668323 cites W2110890069 @default.
- W2053668323 cites W2115153333 @default.
- W2053668323 cites W2118353724 @default.
- W2053668323 cites W2119232336 @default.
- W2053668323 cites W2120999486 @default.
- W2053668323 cites W2123587138 @default.
- W2053668323 cites W2124913831 @default.
- W2053668323 cites W2125555400 @default.
- W2053668323 cites W2128596520 @default.
- W2053668323 cites W2129382347 @default.
- W2053668323 cites W2130230700 @default.
- W2053668323 cites W2131964412 @default.
- W2053668323 cites W2140385522 @default.
- W2053668323 cites W2151889862 @default.
- W2053668323 cites W2157094372 @default.
- W2053668323 cites W2158947240 @default.
- W2053668323 cites W2161493225 @default.
- W2053668323 cites W2165607371 @default.
- W2053668323 cites W4247138217 @default.
- W2053668323 doi "https://doi.org/10.1002/jbm.b.31964" @default.
- W2053668323 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/22102326" @default.
- W2053668323 hasPublicationYear "2011" @default.
- W2053668323 type Work @default.
- W2053668323 sameAs 2053668323 @default.
- W2053668323 citedByCount "20" @default.
- W2053668323 countsByYear W20536683232013 @default.
- W2053668323 countsByYear W20536683232014 @default.
- W2053668323 countsByYear W20536683232015 @default.
- W2053668323 countsByYear W20536683232016 @default.
- W2053668323 countsByYear W20536683232017 @default.
- W2053668323 countsByYear W20536683232018 @default.
- W2053668323 countsByYear W20536683232020 @default.
- W2053668323 countsByYear W20536683232022 @default.
- W2053668323 crossrefType "journal-article" @default.
- W2053668323 hasAuthorship W2053668323A5004056562 @default.
- W2053668323 hasAuthorship W2053668323A5014129390 @default.
- W2053668323 hasAuthorship W2053668323A5056594379 @default.
- W2053668323 hasAuthorship W2053668323A5062427703 @default.
- W2053668323 hasAuthorship W2053668323A5072804832 @default.
- W2053668323 hasConcept C115624301 @default.
- W2053668323 hasConcept C120665830 @default.
- W2053668323 hasConcept C121332964 @default.
- W2053668323 hasConcept C123609680 @default.
- W2053668323 hasConcept C134132462 @default.
- W2053668323 hasConcept C159985019 @default.
- W2053668323 hasConcept C178790620 @default.
- W2053668323 hasConcept C185592680 @default.
- W2053668323 hasConcept C192562407 @default.
- W2053668323 hasConcept C2780902562 @default.
- W2053668323 hasConcept C40003534 @default.
- W2053668323 hasConcept C44280652 @default.
- W2053668323 hasConcept C61276311 @default.
- W2053668323 hasConcept C8010536 @default.
- W2053668323 hasConcept C97549433 @default.
- W2053668323 hasConcept C99595764 @default.
- W2053668323 hasConceptScore W2053668323C115624301 @default.
- W2053668323 hasConceptScore W2053668323C120665830 @default.
- W2053668323 hasConceptScore W2053668323C121332964 @default.
- W2053668323 hasConceptScore W2053668323C123609680 @default.
- W2053668323 hasConceptScore W2053668323C134132462 @default.
- W2053668323 hasConceptScore W2053668323C159985019 @default.
- W2053668323 hasConceptScore W2053668323C178790620 @default.