• W2055015462 abstract "Co-doped Li3V2−xCox(PO4)3/C (x = 0.00, 0.03, 0.05, 0.10, 0.13 or 0.15) compounds were prepared via a solid-state reaction. The Rietveld refinement results indicated that single-phase Li3V2−xCox(PO4)3/C (0 ≤ x ≤ 0.15) with a monoclinic structure was obtained. The X-ray photoelectron spectroscopy (XPS) analysis revealed that the cobalt is present in the +2 oxidation state in Li3V2−xCox(PO4)3. XPS studies also revealed that V4+ and V3+ ions were present in the Co2+-doped system. The initial specific capacity decreased as the Co-doping content increased, increasing monotonically with Co content for x > 0.10. Differential capacity curves of Li3V2−xCox(PO4)3/C compounds showed that the voltage peaks associated with the extraction of three Li+ ions shifted to higher voltages with an increase in Co content, and when the Co2+-doping content reached 0.15, the peak positions returned to those of the unsubstituted Li3V2(PO4)3 phase. For the Li3V1.85Co0.15(PO4)3/C compound, the initial capacity was 163.3 mAh/g (109.4% of the initial capacity of the undoped Li3V2(PO4)3) and 73.4% capacity retention was observed after 50 cycles at a 0.1 C charge/discharge rate. The doping of Co2+into V sites should be favorable for the structural stability of Li3V2−xCox(PO4)3/C compounds and so moderate the volume changes (expansion/contraction) seen during the reversible Li+ extraction/insertion, thus resulting in the improvement of cell cycling ability." @default.
• W2055015462 created "2016-06-24" @default.
• W2055015462 creator A5000344180 @default.
• W2055015462 creator A5037013859 @default.
• W2055015462 creator A5041960519 @default.
• W2055015462 creator A5057762207 @default.
• W2055015462 creator A5060985903 @default.
• W2055015462 creator A5083456268 @default.
• W2055015462 date "2010-02-01" @default.
• W2055015462 modified "2023-10-16" @default.
• W2055015462 title "Synthesis and electrochemical properties of Co-doped Li3V2(PO4)3 cathode materials for lithium-ion batteries" @default.
• W2055015462 cites W1589633704 @default.
• W2055015462 cites W1662595031 @default.
• W2055015462 cites W1978148177 @default.
• W2055015462 cites W1984830583 @default.
• W2055015462 cites W1986529560 @default.
• W2055015462 cites W1989705813 @default.
• W2055015462 cites W1989937017 @default.
• W2055015462 cites W1990498467 @default.
• W2055015462 cites W1995927844 @default.
• W2055015462 cites W2003605084 @default.
• W2055015462 cites W2008764997 @default.
• W2055015462 cites W2013700323 @default.
• W2055015462 cites W2017676880 @default.
• W2055015462 cites W2019418666 @default.
• W2055015462 cites W2030925615 @default.
• W2055015462 cites W2031393568 @default.
• W2055015462 cites W2045275118 @default.
• W2055015462 cites W2055631781 @default.
• W2055015462 cites W2072870145 @default.
• W2055015462 cites W2073926109 @default.
• W2055015462 cites W2080930489 @default.
• W2055015462 cites W2086720446 @default.
• W2055015462 cites W2091839474 @default.
• W2055015462 cites W2094100425 @default.
• W2055015462 cites W2117168765 @default.
• W2055015462 cites W2136822440 @default.
• W2055015462 cites W2167590372 @default.
• W2055015462 cites W2949085436 @default.
• W2055015462 doi "https://doi.org/10.1016/j.electacta.2009.10.028" @default.
• W2055015462 hasPublicationYear "2010" @default.
• W2055015462 type Work @default.
• W2055015462 sameAs 2055015462 @default.
• W2055015462 citedByCount "171" @default.
• W2055015462 countsByYear W20550154622012 @default.
• W2055015462 countsByYear W20550154622013 @default.
• W2055015462 countsByYear W20550154622014 @default.
• W2055015462 countsByYear W20550154622015 @default.
• W2055015462 countsByYear W20550154622016 @default.
• W2055015462 countsByYear W20550154622017 @default.
• W2055015462 countsByYear W20550154622018 @default.
• W2055015462 countsByYear W20550154622019 @default.
• W2055015462 countsByYear W20550154622020 @default.
• W2055015462 countsByYear W20550154622021 @default.
• W2055015462 countsByYear W20550154622022 @default.
• W2055015462 countsByYear W20550154622023 @default.
• W2055015462 crossrefType "journal-article" @default.
• W2055015462 hasAuthorship W2055015462A5000344180 @default.
• W2055015462 hasAuthorship W2055015462A5037013859 @default.
• W2055015462 hasAuthorship W2055015462A5041960519 @default.
• W2055015462 hasAuthorship W2055015462A5057762207 @default.
• W2055015462 hasAuthorship W2055015462A5060985903 @default.
• W2055015462 hasAuthorship W2055015462A5083456268 @default.
• W2055015462 hasConcept C113196181 @default.
• W2055015462 hasConcept C115624301 @default.
• W2055015462 hasConcept C115645028 @default.
• W2055015462 hasConcept C127413603 @default.
• W2055015462 hasConcept C134018914 @default.
• W2055015462 hasConcept C145148216 @default.
• W2055015462 hasConcept C147789679 @default.
• W2055015462 hasConcept C17525397 @default.
• W2055015462 hasConcept C175708663 @default.
• W2055015462 hasConcept C178790620 @default.
• W2055015462 hasConcept C185592680 @default.
• W2055015462 hasConcept C191897082 @default.
• W2055015462 hasConcept C192562407 @default.
• W2055015462 hasConcept C2778541603 @default.
• W2055015462 hasConcept C2778591166 @default.
• W2055015462 hasConcept C42360764 @default.
• W2055015462 hasConcept C43617362 @default.
• W2055015462 hasConcept C49040817 @default.
• W2055015462 hasConcept C52859227 @default.
• W2055015462 hasConcept C544153396 @default.
• W2055015462 hasConcept C57863236 @default.
• W2055015462 hasConcept C61276311 @default.
• W2055015462 hasConcept C71924100 @default.
• W2055015462 hasConcept C8010536 @default.
• W2055015462 hasConceptScore W2055015462C113196181 @default.
• W2055015462 hasConceptScore W2055015462C115624301 @default.
• W2055015462 hasConceptScore W2055015462C115645028 @default.
• W2055015462 hasConceptScore W2055015462C127413603 @default.
• W2055015462 hasConceptScore W2055015462C134018914 @default.
• W2055015462 hasConceptScore W2055015462C145148216 @default.
• W2055015462 hasConceptScore W2055015462C147789679 @default.
• W2055015462 hasConceptScore W2055015462C17525397 @default.
• W2055015462 hasConceptScore W2055015462C175708663 @default.
• W2055015462 hasConceptScore W2055015462C178790620 @default.
• W2055015462 hasConceptScore W2055015462C185592680 @default.

• next