- W2055899739 abstract "The adhesion strength between poly(ethylene terephthalate-co-isophthalate) (co-PET) and tin-free steel (TFS) was investigated by varying the lamination temperature using a blister test. As the lamination temperature increased, the adhesion strength increased rapidly at the beginning and then saturated. The main reason for the increase of adhesion with the lamination temperature was an improved degree of wetting. This was manifested by the fact that the variation in the degree of wetting was very similar to that of the adhesion strength. The degree of wetting was dependent on the melt viscosity of co-PET. The results of differential scanning calorimetry (DSC) and rheometrics dynamic spectrometry (RDS) showed that the high extent of the crystalline phase increased remarkably the melt viscosity of co-PET, leading to incomplete wetting. When the co-PET/TFS joint was immersed in hydrochloric acid solution, the pattern of the front penetration line and the rate of penetration of hydrochloric acid solution into the co-PET/TFS interface were different, depending on the lamination temperature and the direction of penetration. The wet adhesion strength was found to increase with increasing lamination temperature because the size of voids at the co-PET/TFS interface resulting from incomplete wetting decreased." @default.
- W2055899739 created "2016-06-24" @default.
- W2055899739 creator A5000422327 @default.
- W2055899739 creator A5026673257 @default.
- W2055899739 creator A5046871804 @default.
- W2055899739 creator A5059603743 @default.
- W2055899739 creator A5059958529 @default.
- W2055899739 creator A5070179898 @default.
- W2055899739 date "2000-01-01" @default.
- W2055899739 modified "2023-09-26" @default.
- W2055899739 title "Effects of the lamination temperature on the properties of poly(ethylene terephthalate-co-isophthalate) in polyester-laminated tin-free steel can — II. Adhesion mechanism of poly(ethylene terephthalate-co-isophthalate) to TFS" @default.
- W2055899739 cites W1995809841 @default.
- W2055899739 cites W2004370219 @default.
- W2055899739 cites W2015251113 @default.
- W2055899739 cites W2024321919 @default.
- W2055899739 cites W2063406573 @default.
- W2055899739 cites W2078967797 @default.
- W2055899739 cites W2082092201 @default.
- W2055899739 cites W409084602 @default.
- W2055899739 doi "https://doi.org/10.1163/156856100743149" @default.
- W2055899739 hasPublicationYear "2000" @default.
- W2055899739 type Work @default.
- W2055899739 sameAs 2055899739 @default.
- W2055899739 citedByCount "5" @default.
- W2055899739 countsByYear W20558997392013 @default.
- W2055899739 countsByYear W20558997392020 @default.
- W2055899739 countsByYear W20558997392021 @default.
- W2055899739 crossrefType "journal-article" @default.
- W2055899739 hasAuthorship W2055899739A5000422327 @default.
- W2055899739 hasAuthorship W2055899739A5026673257 @default.
- W2055899739 hasAuthorship W2055899739A5046871804 @default.
- W2055899739 hasAuthorship W2055899739A5059603743 @default.
- W2055899739 hasAuthorship W2055899739A5059958529 @default.
- W2055899739 hasAuthorship W2055899739A5070179898 @default.
- W2055899739 hasConcept C119394753 @default.
- W2055899739 hasConcept C121332964 @default.
- W2055899739 hasConcept C127413603 @default.
- W2055899739 hasConcept C134514944 @default.
- W2055899739 hasConcept C159985019 @default.
- W2055899739 hasConcept C161790260 @default.
- W2055899739 hasConcept C178790620 @default.
- W2055899739 hasConcept C185592680 @default.
- W2055899739 hasConcept C192562407 @default.
- W2055899739 hasConcept C2777557983 @default.
- W2055899739 hasConcept C2778597550 @default.
- W2055899739 hasConcept C2779227376 @default.
- W2055899739 hasConcept C2780017307 @default.
- W2055899739 hasConcept C39519442 @default.
- W2055899739 hasConcept C42475967 @default.
- W2055899739 hasConcept C6556556 @default.
- W2055899739 hasConcept C68928338 @default.
- W2055899739 hasConcept C80107235 @default.
- W2055899739 hasConcept C84416704 @default.
- W2055899739 hasConcept C97355855 @default.
- W2055899739 hasConceptScore W2055899739C119394753 @default.
- W2055899739 hasConceptScore W2055899739C121332964 @default.
- W2055899739 hasConceptScore W2055899739C127413603 @default.
- W2055899739 hasConceptScore W2055899739C134514944 @default.
- W2055899739 hasConceptScore W2055899739C159985019 @default.
- W2055899739 hasConceptScore W2055899739C161790260 @default.
- W2055899739 hasConceptScore W2055899739C178790620 @default.
- W2055899739 hasConceptScore W2055899739C185592680 @default.
- W2055899739 hasConceptScore W2055899739C192562407 @default.
- W2055899739 hasConceptScore W2055899739C2777557983 @default.
- W2055899739 hasConceptScore W2055899739C2778597550 @default.
- W2055899739 hasConceptScore W2055899739C2779227376 @default.
- W2055899739 hasConceptScore W2055899739C2780017307 @default.
- W2055899739 hasConceptScore W2055899739C39519442 @default.
- W2055899739 hasConceptScore W2055899739C42475967 @default.
- W2055899739 hasConceptScore W2055899739C6556556 @default.
- W2055899739 hasConceptScore W2055899739C68928338 @default.
- W2055899739 hasConceptScore W2055899739C80107235 @default.
- W2055899739 hasConceptScore W2055899739C84416704 @default.
- W2055899739 hasConceptScore W2055899739C97355855 @default.
- W2055899739 hasIssue "9" @default.
- W2055899739 hasLocation W20558997391 @default.
- W2055899739 hasOpenAccess W2055899739 @default.
- W2055899739 hasPrimaryLocation W20558997391 @default.
- W2055899739 hasRelatedWork W1792133765 @default.
- W2055899739 hasRelatedWork W1890923107 @default.
- W2055899739 hasRelatedWork W2001229197 @default.
- W2055899739 hasRelatedWork W2059605712 @default.
- W2055899739 hasRelatedWork W2062627117 @default.
- W2055899739 hasRelatedWork W2160185461 @default.
- W2055899739 hasRelatedWork W2362730178 @default.
- W2055899739 hasRelatedWork W2414752894 @default.
- W2055899739 hasRelatedWork W2508701374 @default.
- W2055899739 hasRelatedWork W4302380434 @default.
- W2055899739 hasVolume "14" @default.
- W2055899739 isParatext "false" @default.
- W2055899739 isRetracted "false" @default.
- W2055899739 magId "2055899739" @default.
- W2055899739 workType "article" @default.