- W2056322959 abstract "Raw filaments of ultrahigh molecular weight poly(tetrafluoroethylene) (PTFE) (8.4 × 106) were prepared by the paste extrusion of fine powder. The raw filaments with a sag ratio of 25% were annealed at 360 °C, higher than the apparent melting point of 330 °C estimated by differential scanning calorimetry (DSC), at a heating rate of 10 °C/min. After annealing for 30 min, they were cooled to room temperature at desired rates. The resultant monofilaments were annealed for 30 min at 388 °C and were elongated up to 100 times at the same temperature. Young's modulus and the tensile strength were sensitive to the sag ratio of raw filaments under heating and cooling processes. The maximum values of Young's modulus and the tensile strength of drawn fibers reached 57.6 and 2.31 GPa, respectively, at 25−26 °C associated with the crystal transition at room temperature, when the sag ratio was 25% corresponding to the intrinsic shrinkage of the raw filaments. This indicates that a suitable level of the entanglement mesh to assure the maximum values of the tensile strength and Young's modulus was formed by the drastic shrinkage (25%) of the raw filaments, leading to molecular motion without constraints. This phenomenon is discussed in terms of the morphology of the monofilaments and drawn fibers as studied by optical microscopy (crossed-polarized), differential scanning calorimetry, and X-ray diffraction techniques. The production of high-strength PTFE fibers is attributed to the appearance of thermotropic liquid crystals at temperatures higher than the apparent melting point, reflecting the chain rigidity of PTFE." @default.
- W2056322959 created "2016-06-24" @default.
- W2056322959 creator A5019386579 @default.
- W2056322959 creator A5046040268 @default.
- W2056322959 creator A5074460774 @default.
- W2056322959 date "1996-01-01" @default.
- W2056322959 modified "2023-09-25" @default.
- W2056322959 title "Development of High-Modulus and High-Strength Poly(tetrafluoroethylene) Fibers by Elongation at a Liquid Crystalline State" @default.
- W2056322959 cites W1969414926 @default.
- W2056322959 cites W1969461198 @default.
- W2056322959 cites W1977466115 @default.
- W2056322959 cites W1994556932 @default.
- W2056322959 cites W1995618943 @default.
- W2056322959 cites W2023779440 @default.
- W2056322959 cites W2025327632 @default.
- W2056322959 cites W2057709001 @default.
- W2056322959 cites W2067302659 @default.
- W2056322959 cites W2069651853 @default.
- W2056322959 cites W2070198524 @default.
- W2056322959 cites W2095427608 @default.
- W2056322959 cites W2135734607 @default.
- W2056322959 cites W2160704982 @default.
- W2056322959 cites W2315103241 @default.
- W2056322959 cites W2319108482 @default.
- W2056322959 cites W2325651392 @default.
- W2056322959 cites W4233611193 @default.
- W2056322959 doi "https://doi.org/10.1021/ma951790d" @default.
- W2056322959 hasPublicationYear "1996" @default.
- W2056322959 type Work @default.
- W2056322959 sameAs 2056322959 @default.
- W2056322959 citedByCount "12" @default.
- W2056322959 countsByYear W20563229592015 @default.
- W2056322959 countsByYear W20563229592016 @default.
- W2056322959 countsByYear W20563229592018 @default.
- W2056322959 countsByYear W20563229592020 @default.
- W2056322959 crossrefType "journal-article" @default.
- W2056322959 hasAuthorship W2056322959A5019386579 @default.
- W2056322959 hasAuthorship W2056322959A5046040268 @default.
- W2056322959 hasAuthorship W2056322959A5074460774 @default.
- W2056322959 hasConcept C112950240 @default.
- W2056322959 hasConcept C121332964 @default.
- W2056322959 hasConcept C13530604 @default.
- W2056322959 hasConcept C15920480 @default.
- W2056322959 hasConcept C159985019 @default.
- W2056322959 hasConcept C180145272 @default.
- W2056322959 hasConcept C192562407 @default.
- W2056322959 hasConcept C196029304 @default.
- W2056322959 hasConcept C22064058 @default.
- W2056322959 hasConcept C2776906716 @default.
- W2056322959 hasConcept C2777855556 @default.
- W2056322959 hasConcept C2994273327 @default.
- W2056322959 hasConcept C39519442 @default.
- W2056322959 hasConcept C521977710 @default.
- W2056322959 hasConcept C97355855 @default.
- W2056322959 hasConceptScore W2056322959C112950240 @default.
- W2056322959 hasConceptScore W2056322959C121332964 @default.
- W2056322959 hasConceptScore W2056322959C13530604 @default.
- W2056322959 hasConceptScore W2056322959C15920480 @default.
- W2056322959 hasConceptScore W2056322959C159985019 @default.
- W2056322959 hasConceptScore W2056322959C180145272 @default.
- W2056322959 hasConceptScore W2056322959C192562407 @default.
- W2056322959 hasConceptScore W2056322959C196029304 @default.
- W2056322959 hasConceptScore W2056322959C22064058 @default.
- W2056322959 hasConceptScore W2056322959C2776906716 @default.
- W2056322959 hasConceptScore W2056322959C2777855556 @default.
- W2056322959 hasConceptScore W2056322959C2994273327 @default.
- W2056322959 hasConceptScore W2056322959C39519442 @default.
- W2056322959 hasConceptScore W2056322959C521977710 @default.
- W2056322959 hasConceptScore W2056322959C97355855 @default.
- W2056322959 hasIssue "21" @default.
- W2056322959 hasLocation W20563229591 @default.
- W2056322959 hasOpenAccess W2056322959 @default.
- W2056322959 hasPrimaryLocation W20563229591 @default.
- W2056322959 hasRelatedWork W1983999384 @default.
- W2056322959 hasRelatedWork W1995223015 @default.
- W2056322959 hasRelatedWork W2000654421 @default.
- W2056322959 hasRelatedWork W2035305037 @default.
- W2056322959 hasRelatedWork W2057472760 @default.
- W2056322959 hasRelatedWork W2089085266 @default.
- W2056322959 hasRelatedWork W2729932191 @default.
- W2056322959 hasRelatedWork W2766828284 @default.
- W2056322959 hasRelatedWork W2795554382 @default.
- W2056322959 hasRelatedWork W4386460133 @default.
- W2056322959 hasVolume "29" @default.
- W2056322959 isParatext "false" @default.
- W2056322959 isRetracted "false" @default.
- W2056322959 magId "2056322959" @default.
- W2056322959 workType "article" @default.