- W2056565927 abstract "Abstract This study was conducted to explain the tensile strength loss of wood due to the modification with 1,3-dimethylol-4,5-dihydroxyethyleneurea (DMDHEU) and glutaraldehyde (GA). Modified and control wood blocks were macerated to deliberate fibres, and handsheets were produced thereof. The nitrogen content of the fibres indicated that maceration removed the major proportions of DMDHEU. The stability of GA in wood during maceration was not assessed. Tensile strength determined at zero span (z-strength) and finite span (f-strength) was equal for the handsheets from DMDHEU-modified fibres and the control handsheets. The microscopic appearance of the tested finite-span paper strips from DMDHEU-modified fibres mainly indicated interfibre failure and did not differ from the fibre fracture mode of the control handsheets. In contrast, the z-strength of the handsheets from GA-modified fibres was lower than that of controls and decreased with increasing content of GA in the initial modified wood. The f-strength behaviour of the handsheets from GA-modified fibres was the opposite: it was higher than that of controls and increased with increasing GA content. The microscopic appearance of the rapture zones of the finite-span testing mainly indicated intrafibre failure for the GA-modified fibres. It was concluded that cross-linking is likely to be the major reason for tensile strength loss of GA- and DMDHEU-modified wood. In terms of DMDHEU-modified wood, the incrustation of the cell wall by the resin and the reduction in pliability could play an additional role." @default.
- W2056565927 created "2016-06-24" @default.
- W2056565927 creator A5038600610 @default.
- W2056565927 creator A5046706574 @default.
- W2056565927 creator A5091591686 @default.
- W2056565927 date "2014-12-17" @default.
- W2056565927 modified "2023-10-18" @default.
- W2056565927 title "Tensile strength of handsheets prepared with macerated fibres from solid wood modified with cross-linking agents" @default.
- W2056565927 cites W2003076660 @default.
- W2056565927 cites W2017293985 @default.
- W2056565927 cites W2026132031 @default.
- W2056565927 cites W2029516390 @default.
- W2056565927 cites W2034856943 @default.
- W2056565927 cites W2041815979 @default.
- W2056565927 cites W2056158953 @default.
- W2056565927 cites W2066451534 @default.
- W2056565927 cites W2069411252 @default.
- W2056565927 cites W2100853775 @default.
- W2056565927 cites W2128690832 @default.
- W2056565927 cites W2132444826 @default.
- W2056565927 cites W216930140 @default.
- W2056565927 cites W2322422238 @default.
- W2056565927 cites W2322694031 @default.
- W2056565927 cites W2330630385 @default.
- W2056565927 cites W3159884256 @default.
- W2056565927 cites W4256350525 @default.
- W2056565927 cites W4293227709 @default.
- W2056565927 doi "https://doi.org/10.1515/hf-2014-0216" @default.
- W2056565927 hasPublicationYear "2014" @default.
- W2056565927 type Work @default.
- W2056565927 sameAs 2056565927 @default.
- W2056565927 citedByCount "3" @default.
- W2056565927 countsByYear W20565659272016 @default.
- W2056565927 countsByYear W20565659272018 @default.
- W2056565927 countsByYear W20565659272019 @default.
- W2056565927 crossrefType "journal-article" @default.
- W2056565927 hasAuthorship W2056565927A5038600610 @default.
- W2056565927 hasAuthorship W2056565927A5046706574 @default.
- W2056565927 hasAuthorship W2056565927A5091591686 @default.
- W2056565927 hasConcept C112950240 @default.
- W2056565927 hasConcept C159985019 @default.
- W2056565927 hasConcept C185592680 @default.
- W2056565927 hasConcept C192562407 @default.
- W2056565927 hasConcept C2777529624 @default.
- W2056565927 hasConcept C2988076202 @default.
- W2056565927 hasConcept C43617362 @default.
- W2056565927 hasConcept C74940592 @default.
- W2056565927 hasConceptScore W2056565927C112950240 @default.
- W2056565927 hasConceptScore W2056565927C159985019 @default.
- W2056565927 hasConceptScore W2056565927C185592680 @default.
- W2056565927 hasConceptScore W2056565927C192562407 @default.
- W2056565927 hasConceptScore W2056565927C2777529624 @default.
- W2056565927 hasConceptScore W2056565927C2988076202 @default.
- W2056565927 hasConceptScore W2056565927C43617362 @default.
- W2056565927 hasConceptScore W2056565927C74940592 @default.
- W2056565927 hasIssue "8" @default.
- W2056565927 hasLocation W20565659271 @default.
- W2056565927 hasOpenAccess W2056565927 @default.
- W2056565927 hasPrimaryLocation W20565659271 @default.
- W2056565927 hasRelatedWork W1975608897 @default.
- W2056565927 hasRelatedWork W1997159941 @default.
- W2056565927 hasRelatedWork W2044949441 @default.
- W2056565927 hasRelatedWork W2056565927 @default.
- W2056565927 hasRelatedWork W2332396214 @default.
- W2056565927 hasRelatedWork W2387616028 @default.
- W2056565927 hasRelatedWork W2531393654 @default.
- W2056565927 hasRelatedWork W2795554382 @default.
- W2056565927 hasRelatedWork W3122552578 @default.
- W2056565927 hasRelatedWork W4285731133 @default.
- W2056565927 hasVolume "69" @default.
- W2056565927 isParatext "false" @default.
- W2056565927 isRetracted "false" @default.
- W2056565927 magId "2056565927" @default.
- W2056565927 workType "article" @default.