• W2057756834 abstract "Introduction Storage temperature influences the properties of Portland cement during mixing. Because of similarities between Portland cement and mineral trioxide aggregate, the aim of the present study was to evaluate surface microhardness, topography, and phase structure of white mineral trioxide aggregate (WMTA) after storage in a range of temperatures. Methods Thirty WMTA sachets were divided into 3 groups of 10. The 3 groups were stored at 4°C, 25°C, and 40°C for 48 hours with accompanying ampules. Sachets were immediately mixed after removal from storage according to manufacturer's instructions and mixed and packed into cylindrical glass tubes at room temperature. Surface microhardness of each specimen was measured after 3 days. Four specimens from each group were prepared and observed under scanning electron microscope and x-ray diffraction. Data were subjected to one-way analysis of variance and a post hoc Tukey test at P <.05. Results Mean surface hardness ± standard deviation after storage at 4°C, 25°C, and 40°C were 25.23 ± 5.99, 53.56 ± 3.28, and 62.89 ± 1.76, respectively. Statistically significant differences were observed among the groups (P < .001). More voids and a disorganized, flake-like topography were observed in specimens stored at 4°C in comparison with those stored at 25°C and 40°C. X-ray diffraction meter generated similar peaks at 40°C and 25°C, but slight differences were observed at 4°C. Conclusions This study indicated that storage temperature might influence surface hardness and microstructure of WMTA." @default.
• W2057756834 created "2016-06-24" @default.
• W2057756834 creator A5006095966 @default.
• W2057756834 creator A5031117882 @default.
• W2057756834 creator A5052341101 @default.
• W2057756834 creator A5071514665 @default.
• W2057756834 creator A5085887146 @default.
• W2057756834 date "2010-08-01" @default.
• W2057756834 modified "2023-09-27" @default.
• W2057756834 title "Effects of Storage Temperature on Surface Hardness, Microstructure, and Phase Formation of White Mineral Trioxide Aggregate" @default.
• W2057756834 cites W1965647110 @default.
• W2057756834 cites W1968205036 @default.
• W2057756834 cites W1969014836 @default.
• W2057756834 cites W1982263094 @default.
• W2057756834 cites W1982931029 @default.
• W2057756834 cites W1985351372 @default.
• W2057756834 cites W1986097146 @default.
• W2057756834 cites W1986681040 @default.
• W2057756834 cites W1994845945 @default.
• W2057756834 cites W1996088685 @default.
• W2057756834 cites W1998155178 @default.
• W2057756834 cites W1999464424 @default.
• W2057756834 cites W2008906182 @default.
• W2057756834 cites W2010305820 @default.
• W2057756834 cites W2011598997 @default.
• W2057756834 cites W2012128825 @default.
• W2057756834 cites W2045259947 @default.
• W2057756834 cites W2059500428 @default.
• W2057756834 cites W2061242736 @default.
• W2057756834 cites W2061409196 @default.
• W2057756834 cites W2068787060 @default.
• W2057756834 cites W2072279306 @default.
• W2057756834 cites W2076192772 @default.
• W2057756834 cites W2080244000 @default.
• W2057756834 cites W2085406085 @default.
• W2057756834 cites W2086521215 @default.
• W2057756834 cites W2114271436 @default.
• W2057756834 cites W2128814878 @default.
• W2057756834 cites W2132926987 @default.
• W2057756834 cites W2137663799 @default.
• W2057756834 cites W2164652880 @default.
• W2057756834 cites W2171939576 @default.
• W2057756834 cites W42277940 @default.
• W2057756834 cites W4254437392 @default.
• W2057756834 doi "https://doi.org/10.1016/j.joen.2010.04.022" @default.
• W2057756834 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/20647108" @default.
• W2057756834 hasPublicationYear "2010" @default.
• W2057756834 type Work @default.
• W2057756834 sameAs 2057756834 @default.
• W2057756834 citedByCount "30" @default.
• W2057756834 countsByYear W20577568342012 @default.
• W2057756834 countsByYear W20577568342013 @default.
• W2057756834 countsByYear W20577568342014 @default.
• W2057756834 countsByYear W20577568342015 @default.
• W2057756834 countsByYear W20577568342016 @default.
• W2057756834 countsByYear W20577568342017 @default.
• W2057756834 countsByYear W20577568342019 @default.
• W2057756834 countsByYear W20577568342021 @default.
• W2057756834 countsByYear W20577568342023 @default.
• W2057756834 crossrefType "journal-article" @default.
• W2057756834 hasAuthorship W2057756834A5006095966 @default.
• W2057756834 hasAuthorship W2057756834A5031117882 @default.
• W2057756834 hasAuthorship W2057756834A5052341101 @default.
• W2057756834 hasAuthorship W2057756834A5071514665 @default.
• W2057756834 hasAuthorship W2057756834A5085887146 @default.
• W2057756834 hasConcept C159985019 @default.
• W2057756834 hasConcept C165720898 @default.
• W2057756834 hasConcept C185592680 @default.
• W2057756834 hasConcept C192562407 @default.
• W2057756834 hasConcept C199289684 @default.
• W2057756834 hasConcept C199343813 @default.
• W2057756834 hasConcept C26771246 @default.
• W2057756834 hasConcept C2777090975 @default.
• W2057756834 hasConcept C71924100 @default.
• W2057756834 hasConcept C87976508 @default.
• W2057756834 hasConceptScore W2057756834C159985019 @default.
• W2057756834 hasConceptScore W2057756834C165720898 @default.
• W2057756834 hasConceptScore W2057756834C185592680 @default.
• W2057756834 hasConceptScore W2057756834C192562407 @default.
• W2057756834 hasConceptScore W2057756834C199289684 @default.
• W2057756834 hasConceptScore W2057756834C199343813 @default.
• W2057756834 hasConceptScore W2057756834C26771246 @default.
• W2057756834 hasConceptScore W2057756834C2777090975 @default.
• W2057756834 hasConceptScore W2057756834C71924100 @default.
• W2057756834 hasConceptScore W2057756834C87976508 @default.
• W2057756834 hasIssue "8" @default.
• W2057756834 hasLocation W20577568341 @default.
• W2057756834 hasLocation W20577568342 @default.
• W2057756834 hasOpenAccess W2057756834 @default.
• W2057756834 hasPrimaryLocation W20577568341 @default.
• W2057756834 hasRelatedWork W2010582503 @default.
• W2057756834 hasRelatedWork W2063388647 @default.
• W2057756834 hasRelatedWork W2068113961 @default.
• W2057756834 hasRelatedWork W2083437883 @default.
• W2057756834 hasRelatedWork W2357564724 @default.
• W2057756834 hasRelatedWork W2387616028 @default.
• W2057756834 hasRelatedWork W3015701583 @default.
• W2057756834 hasRelatedWork W3118359290 @default.

• next