- W2057863757 abstract "MCrAlY(M=Ni and/or Co) overlay coatings are wildly adopted on hot components in gas turbine engines to protect them from rapid oxidation.Various methods can be applied to prepare MCrAlY overlay coatings,which formed by the arc ion plating method possess outstanding properties in terms of interfacial strength,porosity and componential distribution,and thus excellent oxidation properties.To increase the A1 content is deemed an economical and effective solution for enhancing the service performance and life for MCrAlY coatings at elevated temperature because the degradation process relies greatly on the ceaseless forming and spallation process of the protectiveα-Al_2O_3 scales during high-temperature oxidation.However,high content of A1 will lower the melting point and decrease the ductility of the coating.This phenomenon can be partly resolved through a gradient coating design.In this paper,a conventional NiCrAlY coating and a gradient NiCrAlY coating have been prepared by the combined method of arc ion plating and subsequent diffusion treatment on Nibase superalloy substrate.The microstructures,morphologies,isothermal oxidation behavior at 1000 and 1100℃and cyclic oxidation behavior at 1100℃have been investigated on the two kinds of the coatings.The results have revealed that the conventional NiCrAlY coating with uniform components is composed ofγ′/γphase,β-NiA1 phase and someα-Cr precipitate phase.While the gradient NiCrA1Y coating have showed layered microstructure,i.e.,an Al-enriched outer layer and a Cr-enriched inner layer,primarily consists ofβ-NiA1 phase,γ′/γphase and someα-Cr precipitate phase in the outer layer.During the oxidation,it is evident that the vanishment ofβ-NiA1 phase and the enlargement ofγ′/γphase for both the coatings.Nevertheless,the gradient coating has maintained higher Al content during long-term oxidation due to the massiveβ-NiA1 phase obtained in the outer layer after vacuum annealing and the Cr(W) zones precipitated beside the Cr-enriched inner layer during the oxidation. Adequateβ-NiA1 phase,as reservoir phase of Al,directly delay the process of Al depletion;Cr(W) zones,to a certain extent,slow down the degradation by hindering the diffusion of Al from the gradient coating to the substrate.As a result,the ability of forming and healing the protectiveα-Al_2O_3 scales in the gradient coating have been enhanced,which has eventually improved the high-temperature oxidation properties." @default.
- W2057863757 created "2016-06-24" @default.
- W2057863757 creator A5003655901 @default.
- W2057863757 creator A5009045351 @default.
- W2057863757 creator A5027918641 @default.
- W2057863757 creator A5046195255 @default.
- W2057863757 creator A5068307345 @default.
- W2057863757 creator A5071186892 @default.
- W2057863757 creator A5087259589 @default.
- W2057863757 date "2012-01-01" @default.
- W2057863757 modified "2023-10-14" @default.
- W2057863757 title "STUDY OF OXIDATION BEHAVIOR OF THE GRADIENT NiCrAlY COATING AT 1000 AND 1100 ℃" @default.
- W2057863757 doi "https://doi.org/10.3724/sp.j.1037.2012.00024" @default.
- W2057863757 hasPublicationYear "2012" @default.
- W2057863757 type Work @default.
- W2057863757 sameAs 2057863757 @default.
- W2057863757 citedByCount "3" @default.
- W2057863757 countsByYear W20578637572015 @default.
- W2057863757 countsByYear W20578637572022 @default.
- W2057863757 countsByYear W20578637572023 @default.
- W2057863757 crossrefType "journal-article" @default.
- W2057863757 hasAuthorship W2057863757A5003655901 @default.
- W2057863757 hasAuthorship W2057863757A5009045351 @default.
- W2057863757 hasAuthorship W2057863757A5027918641 @default.
- W2057863757 hasAuthorship W2057863757A5046195255 @default.
- W2057863757 hasAuthorship W2057863757A5068307345 @default.
- W2057863757 hasAuthorship W2057863757A5071186892 @default.
- W2057863757 hasAuthorship W2057863757A5087259589 @default.
- W2057863757 hasBestOaLocation W20578637571 @default.
- W2057863757 hasConcept C159985019 @default.
- W2057863757 hasConcept C191897082 @default.
- W2057863757 hasConcept C192562407 @default.
- W2057863757 hasConcept C2781448156 @default.
- W2057863757 hasConceptScore W2057863757C159985019 @default.
- W2057863757 hasConceptScore W2057863757C191897082 @default.
- W2057863757 hasConceptScore W2057863757C192562407 @default.
- W2057863757 hasConceptScore W2057863757C2781448156 @default.
- W2057863757 hasIssue "6" @default.
- W2057863757 hasLocation W20578637571 @default.
- W2057863757 hasOpenAccess W2057863757 @default.
- W2057863757 hasPrimaryLocation W20578637571 @default.
- W2057863757 hasRelatedWork W2018879842 @default.
- W2057863757 hasRelatedWork W2737498735 @default.
- W2057863757 hasRelatedWork W2744391499 @default.
- W2057863757 hasRelatedWork W2898370298 @default.
- W2057863757 hasRelatedWork W2899084033 @default.
- W2057863757 hasRelatedWork W3041790586 @default.
- W2057863757 hasRelatedWork W3120461830 @default.
- W2057863757 hasRelatedWork W3144504424 @default.
- W2057863757 hasRelatedWork W4230250635 @default.
- W2057863757 hasRelatedWork W4292492973 @default.
- W2057863757 hasVolume "48" @default.
- W2057863757 isParatext "false" @default.
- W2057863757 isRetracted "false" @default.
- W2057863757 magId "2057863757" @default.
- W2057863757 workType "article" @default.