• W2058570819 abstract "Single crystals of zone-refined lead were deformed in tension at temperatures from 4.2 to 273°K and strain rates over 4 orders of magnitude at 77°K. The three stages of deformation typical of a face-centered-cubic metal were observed. The characteristics of these stages and their variations with temperature, etc., were normal, except for the observation that stage II was composed of two distinct regions of linear hardening. Stage III was examined, in particular, in order to determine the stacking-fault energy, γ, of lead following the procedure used by Berner for copper. A value of γ = 25 ergs/cms2 was obtained for lead. Des monocristaux de plomb purifié par fusion zonale ont été déformés en tension à des températures entre 4.2 et 273°K et avec des vitesses de déformation s'étendant sur quatre ordres de grandeur à 77°K. Les trois étapes de déformation typiques d'un métal cubique à faces centrées ont été observées. Les caractéristiques de ces étapes et de leurs variations avec la température etc… étaient normales en dehors du fait que l'étape II était constituéé de deux régions distinctes de durcissement linéaire. L'étape III a été examinée en particulier, en vue de la détermination de l'énergie des défauts d'empilement, γ, du plomb d'après la méthode utilisée par Berner pour le cuivre. La valeur de γ = 25 ergs/cms2 a été obtenue pour le plomb. Einkristalle aus zonengereinigtem Blei wurden bei Temperaturen von 4.2 bis 273°K zugverformt; die Verformungsgeschwindigkeiten erstreckten sich bei 77°K über vier Gröβenordnungen. Die für ein kubisch-flächenzentriertes Metall typischen drei Deformationsstufen wurden beobachtet. Die Kenngröβen dieser Stufen und ihre Temperaturabhängigkeit waren normal, abgesehen von der Beobachtung, daβ Stufe II aus zwei getrennten Bereichen linearer Verfestigung zusammengesetzt war. Stufe III wurde insbesondere zu dem Zweck untersucht, die Stapelfehlerenergie γ von Blei mit Hilfe der von Berner bei Kupfer benutzten Methode zu bestimmen. Es ergab sich für Blei γ = 25 erg/cm2." @default.
• W2058570819 created "2016-06-24" @default.
• W2058570819 creator A5024430645 @default.
• W2058570819 creator A5070448973 @default.
• W2058570819 creator A5086003816 @default.
• W2058570819 date "1962-03-01" @default.
• W2058570819 modified "2023-09-23" @default.
• W2058570819 title "The plasticity of lead single crystals and the determination of stack-fault energy" @default.
• W2058570819 cites W146125274 @default.
• W2058570819 cites W1972536370 @default.
• W2058570819 cites W1972821403 @default.
• W2058570819 cites W1975292278 @default.
• W2058570819 cites W1988865222 @default.
• W2058570819 cites W2010118235 @default.
• W2058570819 cites W2023262102 @default.
• W2058570819 cites W2023403848 @default.
• W2058570819 cites W2036735967 @default.
• W2058570819 cites W2041436026 @default.
• W2058570819 cites W2041685867 @default.
• W2058570819 cites W2061045283 @default.
• W2058570819 cites W2077100814 @default.
• W2058570819 cites W2085859019 @default.
• W2058570819 cites W2086865295 @default.
• W2058570819 cites W2091056805 @default.
• W2058570819 cites W2093568248 @default.
• W2058570819 doi "https://doi.org/10.1016/0001-6160(62)90115-3" @default.
• W2058570819 hasPublicationYear "1962" @default.
• W2058570819 type Work @default.
• W2058570819 sameAs 2058570819 @default.
• W2058570819 citedByCount "36" @default.
• W2058570819 countsByYear W20585708192013 @default.
• W2058570819 countsByYear W20585708192014 @default.
• W2058570819 countsByYear W20585708192015 @default.
• W2058570819 countsByYear W20585708192022 @default.
• W2058570819 crossrefType "journal-article" @default.
• W2058570819 hasAuthorship W2058570819A5024430645 @default.
• W2058570819 hasAuthorship W2058570819A5070448973 @default.
• W2058570819 hasAuthorship W2058570819A5086003816 @default.
• W2058570819 hasConcept C159122135 @default.
• W2058570819 hasConcept C159985019 @default.
• W2058570819 hasConcept C185592680 @default.
• W2058570819 hasConcept C192562407 @default.
• W2058570819 hasConcept C199289684 @default.
• W2058570819 hasConcept C22372946 @default.
• W2058570819 hasConcept C2779227376 @default.
• W2058570819 hasConcept C44255700 @default.
• W2058570819 hasConcept C8010536 @default.
• W2058570819 hasConceptScore W2058570819C159122135 @default.
• W2058570819 hasConceptScore W2058570819C159985019 @default.
• W2058570819 hasConceptScore W2058570819C185592680 @default.
• W2058570819 hasConceptScore W2058570819C192562407 @default.
• W2058570819 hasConceptScore W2058570819C199289684 @default.
• W2058570819 hasConceptScore W2058570819C22372946 @default.
• W2058570819 hasConceptScore W2058570819C2779227376 @default.
• W2058570819 hasConceptScore W2058570819C44255700 @default.
• W2058570819 hasConceptScore W2058570819C8010536 @default.
• W2058570819 hasIssue "3" @default.
• W2058570819 hasLocation W20585708191 @default.
• W2058570819 hasOpenAccess W2058570819 @default.
• W2058570819 hasPrimaryLocation W20585708191 @default.
• W2058570819 hasRelatedWork W1990686913 @default.
• W2058570819 hasRelatedWork W2081397108 @default.
• W2058570819 hasRelatedWork W2082116212 @default.
• W2058570819 hasRelatedWork W2613411130 @default.
• W2058570819 hasRelatedWork W2786330696 @default.
• W2058570819 hasRelatedWork W2787351387 @default.
• W2058570819 hasRelatedWork W2801178258 @default.
• W2058570819 hasRelatedWork W2894819644 @default.
• W2058570819 hasRelatedWork W2951945800 @default.
• W2058570819 hasRelatedWork W4321381457 @default.
• W2058570819 hasVolume "10" @default.
• W2058570819 isParatext "false" @default.
• W2058570819 isRetracted "false" @default.
• W2058570819 magId "2058570819" @default.
• W2058570819 workType "article" @default.