• W2059090955 abstract "A.C. impedance properties of HA/Ti compound layer coated Ti-30Ta-()Nb alloys have been studied by electrochemical method. Ti-30Ta binary alloys contained 3, 7, 10 and 15 wt% Nb were manufactured by the vacuum furnace system. And then specimen was homogenized at for 24 hrs. The sample was cut and polished for corrosion test and coating. It was coated with HA/Ti compound layer by magnetron sputter. The non-coated and coated morphology of Ti alloy were analyzed by X-ray diffractometer (XRD), energy X-ray dispersive spectroscopy (EDX) and filed emission scanning electron microscope (FE-SEM). The corrosion behaviors were investigated using A.C. impedance test (PARSTAT 2273, USA) in 0.9% NaCl solution at . Ti-30Ta-()Nb alloys showed the phase, and phase peak was predominantly appeared in the case of increasingly Nb contents. The microstructures of Ti alloy were transformed from needle-like structure to equiaxed structure as Nb content increased. From the analysis of coating surface, HA/Ti composite surface uniformed coating layer with 750 nm thickness. The growth directions of film were (211), (112), (300) and (202) for HA/Ti composite coating on the surface after heat treatment at , whereas, the growth direction of film was (110) for Ti coating. The polarization resistance () of HA/Ti composite coated Ti-alloys were higher than those of the Ti and HA coated samples in 0.9% NaCl solution at . Especially, corrosion resistance of Ti-Ta-Nb system increased as Nb content increased." @default.
• W2059090955 created "2016-06-24" @default.
• W2059090955 creator A5035270313 @default.
• W2059090955 creator A5044124597 @default.
• W2059090955 creator A5055589825 @default.
• W2059090955 creator A5057259726 @default.
• W2059090955 creator A5067782124 @default.
• W2059090955 creator A5080910090 @default.
• W2059090955 creator A5083900223 @default.
• W2059090955 date "2008-10-31" @default.
• W2059090955 modified "2023-09-26" @default.
• W2059090955 title "A.C. Impedance Properties of HA/Ti Compound Layer coated Ti-30Ta-(3~15)Nb Alloys" @default.
• W2059090955 cites W1968139702 @default.
• W2059090955 cites W1974853662 @default.
• W2059090955 cites W1979551464 @default.
• W2059090955 cites W1994050002 @default.
• W2059090955 cites W2026174735 @default.
• W2059090955 cites W2052111549 @default.
• W2059090955 cites W2087616431 @default.
• W2059090955 doi "https://doi.org/10.5695/jkise.2008.41.5.181" @default.
• W2059090955 hasPublicationYear "2008" @default.
• W2059090955 type Work @default.
• W2059090955 sameAs 2059090955 @default.
• W2059090955 citedByCount "0" @default.
• W2059090955 crossrefType "journal-article" @default.
• W2059090955 hasAuthorship W2059090955A5035270313 @default.
• W2059090955 hasAuthorship W2059090955A5044124597 @default.
• W2059090955 hasAuthorship W2059090955A5055589825 @default.
• W2059090955 hasAuthorship W2059090955A5057259726 @default.
• W2059090955 hasAuthorship W2059090955A5067782124 @default.
• W2059090955 hasAuthorship W2059090955A5080910090 @default.
• W2059090955 hasAuthorship W2059090955A5083900223 @default.
• W2059090955 hasBestOaLocation W20590909551 @default.
• W2059090955 hasConcept C119599485 @default.
• W2059090955 hasConcept C127413603 @default.
• W2059090955 hasConcept C159985019 @default.
• W2059090955 hasConcept C17829176 @default.
• W2059090955 hasConcept C192562407 @default.
• W2059090955 hasConcept C2779227376 @default.
• W2059090955 hasConceptScore W2059090955C119599485 @default.
• W2059090955 hasConceptScore W2059090955C127413603 @default.
• W2059090955 hasConceptScore W2059090955C159985019 @default.
• W2059090955 hasConceptScore W2059090955C17829176 @default.
• W2059090955 hasConceptScore W2059090955C192562407 @default.
• W2059090955 hasConceptScore W2059090955C2779227376 @default.
• W2059090955 hasIssue "5" @default.
• W2059090955 hasLocation W20590909551 @default.
• W2059090955 hasOpenAccess W2059090955 @default.
• W2059090955 hasPrimaryLocation W20590909551 @default.
• W2059090955 hasRelatedWork W1994103032 @default.
• W2059090955 hasRelatedWork W2011052271 @default.
• W2059090955 hasRelatedWork W2051270029 @default.
• W2059090955 hasRelatedWork W2082293200 @default.
• W2059090955 hasRelatedWork W2137307547 @default.
• W2059090955 hasRelatedWork W2366754381 @default.
• W2059090955 hasRelatedWork W2380293314 @default.
• W2059090955 hasRelatedWork W2943188944 @default.
• W2059090955 hasRelatedWork W4285802202 @default.
• W2059090955 hasRelatedWork W4317433637 @default.
• W2059090955 hasVolume "41" @default.
• W2059090955 isParatext "false" @default.
• W2059090955 isRetracted "false" @default.
• W2059090955 magId "2059090955" @default.
• W2059090955 workType "article" @default.