• W2060085151 abstract "The dynamic failure of an alumina particle-reinforced 6061-T6 aluminum alloy composite has been studied using a tension Kolsky bar, and the process of fracture has been investigated using scanning electron microscopy. The failure of a 6061-T6 aluminum alloy was also studied for purposes of comparison. The composite was found to fail in a macroscopically brittle manner in tension, with a failure strain that increased with the nominal strain rate. Differences in hardening rate that are observed in dynamic tension and compression are ascribed to the development of internal damage within the composite in the form of particle cracking. Examination of the fracture surface of the monolithic alloy after dynamic failure shows a ductile failure through void nucleation, growth and coalescence, with substantial void sheet formation. Examination of the fracture surface of the composite after dynamic failure shows microscopically ductile failure in the matrix following brittle cracking of the particles. The dynamic failure process is hypothesized to consist of: (a) cracking of the reinforcing particles; (b) partial debonding at the particle—matrix interface resulting in the nucleation of voids within the matrix; and (c) the growth and coalescence of voids in the matrix to form the final failure surface. The failure process itself quickly localizes within the specimen, so that only a small part of the specimen is affected by all of the damage processes of particle cracking, interface failure and void growth." @default.
• W2060085151 created "2016-06-24" @default.
• W2060085151 creator A5004445335 @default.
• W2060085151 creator A5033981216 @default.
• W2060085151 date "1995-09-01" @default.
• W2060085151 modified "2023-09-24" @default.
• W2060085151 title "Dynamic failure mechanisms in a 6061-T6 Al/Al2O3 metal—matrix composite" @default.
• W2060085151 cites W1970360940 @default.
• W2060085151 cites W1971513723 @default.
• W2060085151 cites W1974666087 @default.
• W2060085151 cites W1975302813 @default.
• W2060085151 cites W1979200182 @default.
• W2060085151 cites W1980383227 @default.
• W2060085151 cites W1980886201 @default.
• W2060085151 cites W1989911696 @default.
• W2060085151 cites W1992012346 @default.
• W2060085151 cites W1999229809 @default.
• W2060085151 cites W2003466194 @default.
• W2060085151 cites W2003867299 @default.
• W2060085151 cites W2004648855 @default.
• W2060085151 cites W2004997190 @default.
• W2060085151 cites W2006248502 @default.
• W2060085151 cites W2015914796 @default.
• W2060085151 cites W2020710537 @default.
• W2060085151 cites W2022180638 @default.
• W2060085151 cites W2022490662 @default.
• W2060085151 cites W2024586276 @default.
• W2060085151 cites W2032168277 @default.
• W2060085151 cites W2032891522 @default.
• W2060085151 cites W2038041964 @default.
• W2060085151 cites W2043202524 @default.
• W2060085151 cites W2043221775 @default.
• W2060085151 cites W2050537779 @default.
• W2060085151 cites W2055113504 @default.
• W2060085151 cites W2062412513 @default.
• W2060085151 cites W2066686121 @default.
• W2060085151 cites W2069911591 @default.
• W2060085151 cites W2083645710 @default.
• W2060085151 cites W2083997530 @default.
• W2060085151 cites W2152997984 @default.
• W2060085151 cites W2362502680 @default.
• W2060085151 cites W399563657 @default.
• W2060085151 cites W4235492610 @default.
• W2060085151 doi "https://doi.org/10.1016/0020-7683(94)00285-5" @default.
• W2060085151 hasPublicationYear "1995" @default.
• W2060085151 type Work @default.
• W2060085151 sameAs 2060085151 @default.
• W2060085151 citedByCount "54" @default.
• W2060085151 countsByYear W20600851512012 @default.
• W2060085151 countsByYear W20600851512013 @default.
• W2060085151 countsByYear W20600851512014 @default.
• W2060085151 countsByYear W20600851512015 @default.
• W2060085151 countsByYear W20600851512016 @default.
• W2060085151 countsByYear W20600851512017 @default.
• W2060085151 countsByYear W20600851512019 @default.
• W2060085151 countsByYear W20600851512021 @default.
• W2060085151 countsByYear W20600851512022 @default.
• W2060085151 countsByYear W20600851512023 @default.
• W2060085151 crossrefType "journal-article" @default.
• W2060085151 hasAuthorship W2060085151A5004445335 @default.
• W2060085151 hasAuthorship W2060085151A5033981216 @default.
• W2060085151 hasBestOaLocation W20600851511 @default.
• W2060085151 hasConcept C104779481 @default.
• W2060085151 hasConcept C121332964 @default.
• W2060085151 hasConcept C136478896 @default.
• W2060085151 hasConcept C149792144 @default.
• W2060085151 hasConcept C159985019 @default.
• W2060085151 hasConcept C178790620 @default.
• W2060085151 hasConcept C185592680 @default.
• W2060085151 hasConcept C192562407 @default.
• W2060085151 hasConcept C2777925586 @default.
• W2060085151 hasConcept C2779772531 @default.
• W2060085151 hasConcept C2780026712 @default.
• W2060085151 hasConcept C58396970 @default.
• W2060085151 hasConcept C61048295 @default.
• W2060085151 hasConcept C87355193 @default.
• W2060085151 hasConceptScore W2060085151C104779481 @default.
• W2060085151 hasConceptScore W2060085151C121332964 @default.
• W2060085151 hasConceptScore W2060085151C136478896 @default.
• W2060085151 hasConceptScore W2060085151C149792144 @default.
• W2060085151 hasConceptScore W2060085151C159985019 @default.
• W2060085151 hasConceptScore W2060085151C178790620 @default.
• W2060085151 hasConceptScore W2060085151C185592680 @default.
• W2060085151 hasConceptScore W2060085151C192562407 @default.
• W2060085151 hasConceptScore W2060085151C2777925586 @default.
• W2060085151 hasConceptScore W2060085151C2779772531 @default.
• W2060085151 hasConceptScore W2060085151C2780026712 @default.
• W2060085151 hasConceptScore W2060085151C58396970 @default.
• W2060085151 hasConceptScore W2060085151C61048295 @default.
• W2060085151 hasConceptScore W2060085151C87355193 @default.
• W2060085151 hasIssue "17-18" @default.
• W2060085151 hasLocation W20600851511 @default.
• W2060085151 hasOpenAccess W2060085151 @default.
• W2060085151 hasPrimaryLocation W20600851511 @default.
• W2060085151 hasRelatedWork W1971548764 @default.
• W2060085151 hasRelatedWork W1982314687 @default.
• W2060085151 hasRelatedWork W2900524175 @default.
• W2060085151 hasRelatedWork W3036603183 @default.

• next