- W2062013731 abstract "Abstract Transparent conductive zinc oxide co-doped with tin and aluminum (TAZO) thin films were prepared via sol–gel dip-coating process. Non-toxic ethanol was used in this study instead of 2-methoxyethanol used in conventional work. Dip-coating was repeated several times to obtain relatively thick films consisting of six layers. The films were then annealed at 500 °C for 1 h in air or in vacuum and not subsequently as employed in other studies. The X-ray diffraction patterns indicated that all the samples revealed a single phase of hexagonal ZnO polycrystalline structure with a main peak of (002). The optical band gap and resistivity of the TAZO films were in the ranges of 3.28 to 3.32 eV and 0.52 to 575.25 Ω cm, respectively. The 1.0 at.% Sn, 1.0 at.% Al co-doped ZnO thin film annealed in vacuum was found to have a better photoelectrochemical performance with photocurrent density of about 0.28 mA/cm 2 at a bias of 0.5 V vs. SCE under a 300 W Xe lamp illumination with the intensity of 100 mW/cm 2 . Compared to the same dopant concentration but annealed in air (~ 0.05 mA/cm 2 bias 0.5 V vs. SCE), the photocurrent density of the film annealed in vacuum was 5 times higher than the film annealed in air. Through electrochemical measurements, we found that the dopant concentration of Sn plays an important role in TAZO that affected photocurrent density, stability of water splitting and anti-corrosion." @default.
- W2062013731 created "2016-06-24" @default.
- W2062013731 creator A5027842636 @default.
- W2062013731 creator A5028843492 @default.
- W2062013731 creator A5033485246 @default.
- W2062013731 creator A5047171547 @default.
- W2062013731 creator A5085254274 @default.
- W2062013731 date "2014-11-01" @default.
- W2062013731 modified "2023-09-30" @default.
- W2062013731 title "Structure and characterization of Sn, Al co-doped zinc oxide thin films prepared by sol–gel dip-coating process" @default.
- W2062013731 cites W1964811692 @default.
- W2062013731 cites W1967652077 @default.
- W2062013731 cites W1972624068 @default.
- W2062013731 cites W1975591279 @default.
- W2062013731 cites W1977001398 @default.
- W2062013731 cites W1978367227 @default.
- W2062013731 cites W1979496920 @default.
- W2062013731 cites W1986988787 @default.
- W2062013731 cites W2008362017 @default.
- W2062013731 cites W2013960037 @default.
- W2062013731 cites W2016282962 @default.
- W2062013731 cites W2017414690 @default.
- W2062013731 cites W2019667820 @default.
- W2062013731 cites W2036712523 @default.
- W2062013731 cites W2038468418 @default.
- W2062013731 cites W2041633369 @default.
- W2062013731 cites W2042492216 @default.
- W2062013731 cites W2042709729 @default.
- W2062013731 cites W2052344653 @default.
- W2062013731 cites W2054124407 @default.
- W2062013731 cites W2065242661 @default.
- W2062013731 cites W2074937372 @default.
- W2062013731 cites W2079967229 @default.
- W2062013731 cites W2080462054 @default.
- W2062013731 cites W2083150510 @default.
- W2062013731 cites W2084353158 @default.
- W2062013731 cites W2088676527 @default.
- W2062013731 cites W2089345636 @default.
- W2062013731 cites W2089686332 @default.
- W2062013731 cites W2095265731 @default.
- W2062013731 cites W2121910128 @default.
- W2062013731 cites W2132552826 @default.
- W2062013731 cites W2134902793 @default.
- W2062013731 cites W2141184801 @default.
- W2062013731 cites W2166239777 @default.
- W2062013731 cites W2167802173 @default.
- W2062013731 cites W2326746082 @default.
- W2062013731 cites W2334682583 @default.
- W2062013731 doi "https://doi.org/10.1016/j.tsf.2014.04.051" @default.
- W2062013731 hasPublicationYear "2014" @default.
- W2062013731 type Work @default.
- W2062013731 sameAs 2062013731 @default.
- W2062013731 citedByCount "35" @default.
- W2062013731 countsByYear W20620137312016 @default.
- W2062013731 countsByYear W20620137312017 @default.
- W2062013731 countsByYear W20620137312018 @default.
- W2062013731 countsByYear W20620137312019 @default.
- W2062013731 countsByYear W20620137312020 @default.
- W2062013731 countsByYear W20620137312021 @default.
- W2062013731 countsByYear W20620137312022 @default.
- W2062013731 countsByYear W20620137312023 @default.
- W2062013731 crossrefType "journal-article" @default.
- W2062013731 hasAuthorship W2062013731A5027842636 @default.
- W2062013731 hasAuthorship W2062013731A5028843492 @default.
- W2062013731 hasAuthorship W2062013731A5033485246 @default.
- W2062013731 hasAuthorship W2062013731A5047171547 @default.
- W2062013731 hasAuthorship W2062013731A5085254274 @default.
- W2062013731 hasConcept C127413603 @default.
- W2062013731 hasConcept C171250308 @default.
- W2062013731 hasConcept C179104552 @default.
- W2062013731 hasConcept C185592680 @default.
- W2062013731 hasConcept C19067145 @default.
- W2062013731 hasConcept C191897082 @default.
- W2062013731 hasConcept C192562407 @default.
- W2062013731 hasConcept C2779851234 @default.
- W2062013731 hasConcept C2780841128 @default.
- W2062013731 hasConcept C2781448156 @default.
- W2062013731 hasConcept C38398224 @default.
- W2062013731 hasConcept C42360764 @default.
- W2062013731 hasConcept C49040817 @default.
- W2062013731 hasConcept C49241924 @default.
- W2062013731 hasConcept C535196362 @default.
- W2062013731 hasConcept C57863236 @default.
- W2062013731 hasConceptScore W2062013731C127413603 @default.
- W2062013731 hasConceptScore W2062013731C171250308 @default.
- W2062013731 hasConceptScore W2062013731C179104552 @default.
- W2062013731 hasConceptScore W2062013731C185592680 @default.
- W2062013731 hasConceptScore W2062013731C19067145 @default.
- W2062013731 hasConceptScore W2062013731C191897082 @default.
- W2062013731 hasConceptScore W2062013731C192562407 @default.
- W2062013731 hasConceptScore W2062013731C2779851234 @default.
- W2062013731 hasConceptScore W2062013731C2780841128 @default.
- W2062013731 hasConceptScore W2062013731C2781448156 @default.
- W2062013731 hasConceptScore W2062013731C38398224 @default.
- W2062013731 hasConceptScore W2062013731C42360764 @default.
- W2062013731 hasConceptScore W2062013731C49040817 @default.
- W2062013731 hasConceptScore W2062013731C49241924 @default.
- W2062013731 hasConceptScore W2062013731C535196362 @default.