- W2062938488 endingPage "1526" @default.
- W2062938488 startingPage "1522" @default.
- W2062938488 abstract "Abstract Porous silicon (PSi) was formed at different current densities in the range of 5–60 mA/cm2 by electrochemical anodized etching in HF for different durations in the range of 10–30 min. Above this PSi structure, SnO2 films were deposited by the spin coating technique. The PSi has been characterized by X-ray diffraction studies. Peaks pertaining to PSi along with those corresponding to SnO2 are observed. Atomic force microscopic studies indicate that very fine needle like silicon nanostructures are observed which is the result of the best PSi structure formed at 30 mA/cm2. For the SnO2 covered PSi structures, larger grains are observed with uniform coverage. The PSi samples prepared at current densities above and below 30 mA/cm2 show PL spectra with asymmetric and overlapped peaks. The PL profile of thin SnO2 film coated on PSi shows a peak at 633 nm and a small hump at about 660 nm." @default.
- W2062938488 created "2016-06-24" @default.
- W2062938488 creator A5009775210 @default.
- W2062938488 creator A5032664318 @default.
- W2062938488 creator A5037330519 @default.
- W2062938488 creator A5042699128 @default.
- W2062938488 creator A5043896372 @default.
- W2062938488 creator A5084915894 @default.
- W2062938488 date "2011-03-01" @default.
- W2062938488 modified "2023-10-16" @default.
- W2062938488 title "Development of porous silicon matrix and characteristics of porous silicon/tin oxide structures" @default.
- W2062938488 cites W1976837130 @default.
- W2062938488 cites W1990210578 @default.
- W2062938488 cites W1995142902 @default.
- W2062938488 cites W2021254327 @default.
- W2062938488 cites W2025816486 @default.
- W2062938488 cites W2029494088 @default.
- W2062938488 cites W2040594394 @default.
- W2062938488 cites W2048123096 @default.
- W2062938488 cites W2048329043 @default.
- W2062938488 cites W2055298388 @default.
- W2062938488 cites W2066600857 @default.
- W2062938488 cites W2066780666 @default.
- W2062938488 cites W2077776339 @default.
- W2062938488 cites W2080777936 @default.
- W2062938488 cites W2136736830 @default.
- W2062938488 doi "https://doi.org/10.1016/j.jnoncrysol.2011.01.003" @default.
- W2062938488 hasPublicationYear "2011" @default.
- W2062938488 type Work @default.
- W2062938488 sameAs 2062938488 @default.
- W2062938488 citedByCount "4" @default.
- W2062938488 countsByYear W20629384882013 @default.
- W2062938488 countsByYear W20629384882018 @default.
- W2062938488 countsByYear W20629384882019 @default.
- W2062938488 countsByYear W20629384882022 @default.
- W2062938488 crossrefType "journal-article" @default.
- W2062938488 hasAuthorship W2062938488A5009775210 @default.
- W2062938488 hasAuthorship W2062938488A5032664318 @default.
- W2062938488 hasAuthorship W2062938488A5037330519 @default.
- W2062938488 hasAuthorship W2062938488A5042699128 @default.
- W2062938488 hasAuthorship W2062938488A5043896372 @default.
- W2062938488 hasAuthorship W2062938488A5084915894 @default.
- W2062938488 hasConcept C106487976 @default.
- W2062938488 hasConcept C127413603 @default.
- W2062938488 hasConcept C159985019 @default.
- W2062938488 hasConcept C191897082 @default.
- W2062938488 hasConcept C192562407 @default.
- W2062938488 hasConcept C2776685891 @default.
- W2062938488 hasConcept C2777431650 @default.
- W2062938488 hasConcept C2779105228 @default.
- W2062938488 hasConcept C2779851234 @default.
- W2062938488 hasConcept C2780924660 @default.
- W2062938488 hasConcept C42360764 @default.
- W2062938488 hasConcept C525849907 @default.
- W2062938488 hasConcept C544956773 @default.
- W2062938488 hasConcept C6648577 @default.
- W2062938488 hasConceptScore W2062938488C106487976 @default.
- W2062938488 hasConceptScore W2062938488C127413603 @default.
- W2062938488 hasConceptScore W2062938488C159985019 @default.
- W2062938488 hasConceptScore W2062938488C191897082 @default.
- W2062938488 hasConceptScore W2062938488C192562407 @default.
- W2062938488 hasConceptScore W2062938488C2776685891 @default.
- W2062938488 hasConceptScore W2062938488C2777431650 @default.
- W2062938488 hasConceptScore W2062938488C2779105228 @default.
- W2062938488 hasConceptScore W2062938488C2779851234 @default.
- W2062938488 hasConceptScore W2062938488C2780924660 @default.
- W2062938488 hasConceptScore W2062938488C42360764 @default.
- W2062938488 hasConceptScore W2062938488C525849907 @default.
- W2062938488 hasConceptScore W2062938488C544956773 @default.
- W2062938488 hasConceptScore W2062938488C6648577 @default.
- W2062938488 hasIssue "6" @default.
- W2062938488 hasLocation W20629384881 @default.
- W2062938488 hasOpenAccess W2062938488 @default.
- W2062938488 hasPrimaryLocation W20629384881 @default.
- W2062938488 hasRelatedWork W1604090598 @default.
- W2062938488 hasRelatedWork W1968054989 @default.
- W2062938488 hasRelatedWork W1974934904 @default.
- W2062938488 hasRelatedWork W1984367251 @default.
- W2062938488 hasRelatedWork W2004485938 @default.
- W2062938488 hasRelatedWork W2043535345 @default.
- W2062938488 hasRelatedWork W2074893258 @default.
- W2062938488 hasRelatedWork W2093275523 @default.
- W2062938488 hasRelatedWork W2100013560 @default.
- W2062938488 hasRelatedWork W2384279159 @default.
- W2062938488 hasVolume "357" @default.
- W2062938488 isParatext "false" @default.
- W2062938488 isRetracted "false" @default.
- W2062938488 magId "2062938488" @default.
- W2062938488 workType "article" @default.