- W2064913612 abstract "The effect of the growth condition on the microstructure and mechanical behaviour of the NiAl–Mo eutectic alloy was investigated. Samples of the eutectic alloy were prepared using an arc furnace under argon atmosphere and then directionally solidified. The samples directionally solidified showed regular and aligned eutectic microstructure. Compression tests were performed at room temperature and 1173 K. Vickers hardness was determined at several temperatures, from room temperature to 1150 K. Mechanical properties of NiAl were also determined. Results showed that when the growth rate is gradually increased from 8 to 50 mm/h the aligned microstructure presents higher fibre density, which leads to higher strength level at room temperature, while further increase in the growth rate causes the microstructure the loose regularity. NiAl presents a well defined mechanical behaviour transition, while the NiAl–Mo eutectic alloy softens almost linearly. The highest yield strength value of NiAl–Mo was found to be about 1200 and 300 MPa at room temperature and 1173 K, respectively." @default.
- W2064913612 created "2016-06-24" @default.
- W2064913612 creator A5001245099 @default.
- W2064913612 creator A5012445269 @default.
- W2064913612 creator A5043964207 @default.
- W2064913612 date "2004-11-01" @default.
- W2064913612 modified "2023-10-03" @default.
- W2064913612 title "Influence of growth rate on the microstructure and mechanical behaviour of a NiAl–Mo eutectic alloy" @default.
- W2064913612 cites W1663768834 @default.
- W2064913612 cites W1976032556 @default.
- W2064913612 cites W1993781533 @default.
- W2064913612 cites W1998616372 @default.
- W2064913612 cites W2020909920 @default.
- W2064913612 cites W2032425094 @default.
- W2064913612 cites W2032934598 @default.
- W2064913612 cites W2040756634 @default.
- W2064913612 cites W2058112640 @default.
- W2064913612 cites W2066260029 @default.
- W2064913612 cites W2069966195 @default.
- W2064913612 cites W2075400867 @default.
- W2064913612 cites W2078407369 @default.
- W2064913612 cites W2086482768 @default.
- W2064913612 cites W2317001206 @default.
- W2064913612 cites W2329150415 @default.
- W2064913612 doi "https://doi.org/10.1016/j.jallcom.2004.02.052" @default.
- W2064913612 hasPublicationYear "2004" @default.
- W2064913612 type Work @default.
- W2064913612 sameAs 2064913612 @default.
- W2064913612 citedByCount "28" @default.
- W2064913612 countsByYear W20649136122012 @default.
- W2064913612 countsByYear W20649136122013 @default.
- W2064913612 countsByYear W20649136122014 @default.
- W2064913612 countsByYear W20649136122015 @default.
- W2064913612 countsByYear W20649136122016 @default.
- W2064913612 countsByYear W20649136122020 @default.
- W2064913612 countsByYear W20649136122022 @default.
- W2064913612 countsByYear W20649136122023 @default.
- W2064913612 crossrefType "journal-article" @default.
- W2064913612 hasAuthorship W2064913612A5001245099 @default.
- W2064913612 hasAuthorship W2064913612A5012445269 @default.
- W2064913612 hasAuthorship W2064913612A5043964207 @default.
- W2064913612 hasConcept C133392424 @default.
- W2064913612 hasConcept C159985019 @default.
- W2064913612 hasConcept C18168003 @default.
- W2064913612 hasConcept C191897082 @default.
- W2064913612 hasConcept C192562407 @default.
- W2064913612 hasConcept C27501479 @default.
- W2064913612 hasConcept C2780026712 @default.
- W2064913612 hasConcept C2780289051 @default.
- W2064913612 hasConcept C87976508 @default.
- W2064913612 hasConceptScore W2064913612C133392424 @default.
- W2064913612 hasConceptScore W2064913612C159985019 @default.
- W2064913612 hasConceptScore W2064913612C18168003 @default.
- W2064913612 hasConceptScore W2064913612C191897082 @default.
- W2064913612 hasConceptScore W2064913612C192562407 @default.
- W2064913612 hasConceptScore W2064913612C27501479 @default.
- W2064913612 hasConceptScore W2064913612C2780026712 @default.
- W2064913612 hasConceptScore W2064913612C2780289051 @default.
- W2064913612 hasConceptScore W2064913612C87976508 @default.
- W2064913612 hasIssue "1-2" @default.
- W2064913612 hasLocation W20649136121 @default.
- W2064913612 hasOpenAccess W2064913612 @default.
- W2064913612 hasPrimaryLocation W20649136121 @default.
- W2064913612 hasRelatedWork W1919346256 @default.
- W2064913612 hasRelatedWork W1987487801 @default.
- W2064913612 hasRelatedWork W2025745942 @default.
- W2064913612 hasRelatedWork W2089251307 @default.
- W2064913612 hasRelatedWork W2095005377 @default.
- W2064913612 hasRelatedWork W2106080380 @default.
- W2064913612 hasRelatedWork W2146738552 @default.
- W2064913612 hasRelatedWork W2146788481 @default.
- W2064913612 hasRelatedWork W2347519956 @default.
- W2064913612 hasRelatedWork W2528998499 @default.
- W2064913612 hasVolume "381" @default.
- W2064913612 isParatext "false" @default.
- W2064913612 isRetracted "false" @default.
- W2064913612 magId "2064913612" @default.
- W2064913612 workType "article" @default.