• W2066462893 abstract "Single-crystal hydroxyapatite and OH-carbonated hydroxyapatite have bending strength much higher than that of dense hydroxyapatite ceramic, indicating potential applicability to a load-bearing biomaterial. However, the effects of carbonate on the strength are less clear. The objective of the present study was to determine the bending strength and Young's modulus of these single crystals with carbonate contents from 0 to 0.62 in CO 2 wt%. Three-point bending tests were performed by means of a modified ultramicrohardness tester with a span of 380 μm and a bending direction <210> of the single crystals. The crystals were broken in air, water, and air after immersion in a cell culture medium for 3 wks. The average Young's modulus of the single crystals was from 54 to 79 GPa. The average bending strength of the single crystals in air was 500 ± 184, 468 ± 205, 513 ± 151, and 450 ± 162 MPa for those with 0, 0.09, 0.37, and 0.62 wt% carbonate, respectively. No significant decrease in strength was found for hydroxyapatite single crystals both in water and after the immersion in the medium. However, the strength of OH-carbonated hydroxyapatite single crystals decreased significantly by 23 to 43% in water in proportion to the carbonate content. The strength of single crystals with 0.37 and 0.62 wt% carbonate decreased significantly, even after the immersion in the medium. Therefore, hydroxyapatite single crystals are superior to OH-carbonated hydroxyapatite single crystals as a biomaterial for a load-bearing purpose." @default.
• W2066462893 created "2016-06-24" @default.
• W2066462893 creator A5001541312 @default.
• W2066462893 creator A5019215622 @default.
• W2066462893 creator A5028660614 @default.
• W2066462893 creator A5036324651 @default.
• W2066462893 creator A5037324544 @default.
• W2066462893 creator A5088704191 @default.
• W2066462893 date "1998-07-01" @default.
• W2066462893 modified "2023-10-17" @default.
• W2066462893 title "Mechanical Properties of Hydroxyapatite and OH-carbonated Hydroxyapatite Single Crystals" @default.
• W2066462893 cites W1965368306 @default.
• W2066462893 cites W1969776202 @default.
• W2066462893 cites W1992506292 @default.
• W2066462893 cites W1998225542 @default.
• W2066462893 cites W2003133357 @default.
• W2066462893 cites W2006495643 @default.
• W2066462893 cites W2010275883 @default.
• W2066462893 cites W2010280268 @default.
• W2066462893 cites W2021442258 @default.
• W2066462893 cites W2023477464 @default.
• W2066462893 cites W2045438670 @default.
• W2066462893 cites W2046232956 @default.
• W2066462893 cites W2054524100 @default.
• W2066462893 cites W2055079161 @default.
• W2066462893 cites W2068694754 @default.
• W2066462893 cites W2070935664 @default.
• W2066462893 cites W2118326236 @default.
• W2066462893 cites W2331196128 @default.
• W2066462893 cites W4236621789 @default.
• W2066462893 cites W4237383770 @default.
• W2066462893 doi "https://doi.org/10.1177/00220345980770071201" @default.
• W2066462893 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/9663442" @default.
• W2066462893 hasPublicationYear "1998" @default.
• W2066462893 type Work @default.
• W2066462893 sameAs 2066462893 @default.
• W2066462893 citedByCount "35" @default.
• W2066462893 countsByYear W20664628932012 @default.
• W2066462893 countsByYear W20664628932013 @default.
• W2066462893 countsByYear W20664628932014 @default.
• W2066462893 countsByYear W20664628932015 @default.
• W2066462893 countsByYear W20664628932016 @default.
• W2066462893 countsByYear W20664628932017 @default.
• W2066462893 countsByYear W20664628932018 @default.
• W2066462893 countsByYear W20664628932019 @default.
• W2066462893 countsByYear W20664628932020 @default.
• W2066462893 countsByYear W20664628932021 @default.
• W2066462893 countsByYear W20664628932022 @default.
• W2066462893 crossrefType "journal-article" @default.
• W2066462893 hasAuthorship W2066462893A5001541312 @default.
• W2066462893 hasAuthorship W2066462893A5019215622 @default.
• W2066462893 hasAuthorship W2066462893A5028660614 @default.
• W2066462893 hasAuthorship W2066462893A5036324651 @default.
• W2066462893 hasAuthorship W2066462893A5037324544 @default.
• W2066462893 hasAuthorship W2066462893A5088704191 @default.
• W2066462893 hasConcept C134132462 @default.
• W2066462893 hasConcept C159985019 @default.
• W2066462893 hasConcept C171250308 @default.
• W2066462893 hasConcept C178405089 @default.
• W2066462893 hasConcept C185592680 @default.
• W2066462893 hasConcept C191897082 @default.
• W2066462893 hasConcept C192562407 @default.
• W2066462893 hasConcept C193867417 @default.
• W2066462893 hasConcept C196029304 @default.
• W2066462893 hasConcept C199068039 @default.
• W2066462893 hasConcept C202444582 @default.
• W2066462893 hasConcept C2778414984 @default.
• W2066462893 hasConcept C2780659211 @default.
• W2066462893 hasConcept C33923547 @default.
• W2066462893 hasConcept C73922627 @default.
• W2066462893 hasConcept C8010536 @default.
• W2066462893 hasConceptScore W2066462893C134132462 @default.
• W2066462893 hasConceptScore W2066462893C159985019 @default.
• W2066462893 hasConceptScore W2066462893C171250308 @default.
• W2066462893 hasConceptScore W2066462893C178405089 @default.
• W2066462893 hasConceptScore W2066462893C185592680 @default.
• W2066462893 hasConceptScore W2066462893C191897082 @default.
• W2066462893 hasConceptScore W2066462893C192562407 @default.
• W2066462893 hasConceptScore W2066462893C193867417 @default.
• W2066462893 hasConceptScore W2066462893C196029304 @default.
• W2066462893 hasConceptScore W2066462893C199068039 @default.
• W2066462893 hasConceptScore W2066462893C202444582 @default.
• W2066462893 hasConceptScore W2066462893C2778414984 @default.
• W2066462893 hasConceptScore W2066462893C2780659211 @default.
• W2066462893 hasConceptScore W2066462893C33923547 @default.
• W2066462893 hasConceptScore W2066462893C73922627 @default.
• W2066462893 hasConceptScore W2066462893C8010536 @default.
• W2066462893 hasIssue "7" @default.
• W2066462893 hasLocation W20664628931 @default.
• W2066462893 hasLocation W20664628932 @default.
• W2066462893 hasOpenAccess W2066462893 @default.
• W2066462893 hasPrimaryLocation W20664628931 @default.
• W2066462893 hasRelatedWork W198054552 @default.
• W2066462893 hasRelatedWork W2029692325 @default.
• W2066462893 hasRelatedWork W2078620962 @default.
• W2066462893 hasRelatedWork W2080785017 @default.
• W2066462893 hasRelatedWork W2108887759 @default.
• W2066462893 hasRelatedWork W2366934632 @default.

• next