- W2067707952 abstract "Graphite electrodes were electrochemically cycled in Li-ion cells at 50 and 60 °C in order to determine the changes in their surface properties in comparison to the electrodes tested at 25 °C. A 17% drop in planar capacity occurred during the first cycle at 60 °C compared to a 40% at 25 °C and reduced the amount of damage that occurred to graphite due to a rapidly formed solid electrolyte interphase (SEI). During the following cycles, a planar capacity of 3.11 ± 0.12 mAh cm−2 was attained at 60 °C rather than 0.53 ± 0.03 mAh cm−2 at 25 °C. The SEI layer formed at 60 °C predominantly consisted of Li2CO3 and was devoid of residual LiClO4 detected at 25 °C. At 25 °C, the diffusion coefficient of Li+ (DLi+) was calculated as 1.07 × 10−8 cm2 s−1, whereas at 60 °C, DLi+ increased to 3.25 × 10−8 cm2 s−1. A pre-treatment conducted at 60 °C enhanced the cyclic performance of graphite subsequently cycled at 25 °C; a Li2CO3-enriched SEI, generated during the 60 °C pre-treatment, covered the graphite surface uniformly and resulted in a 28% increase in battery capacity at 25 °C." @default.
- W2067707952 created "2016-06-24" @default.
- W2067707952 creator A5025743013 @default.
- W2067707952 creator A5041052057 @default.
- W2067707952 creator A5069392555 @default.
- W2067707952 date "2014-02-01" @default.
- W2067707952 modified "2023-10-03" @default.
- W2067707952 title "Thermal cycling induced capacity enhancement of graphite anodes in lithium-ion cells" @default.
- W2067707952 cites W1516070251 @default.
- W2067707952 cites W1968074637 @default.
- W2067707952 cites W1970060121 @default.
- W2067707952 cites W1972158837 @default.
- W2067707952 cites W1973702134 @default.
- W2067707952 cites W1979562350 @default.
- W2067707952 cites W1981505083 @default.
- W2067707952 cites W1982784803 @default.
- W2067707952 cites W1983672594 @default.
- W2067707952 cites W1985272895 @default.
- W2067707952 cites W1988064910 @default.
- W2067707952 cites W1992944832 @default.
- W2067707952 cites W1993803714 @default.
- W2067707952 cites W1994337062 @default.
- W2067707952 cites W1995721730 @default.
- W2067707952 cites W2001664727 @default.
- W2067707952 cites W2005837643 @default.
- W2067707952 cites W2007513192 @default.
- W2067707952 cites W2015296551 @default.
- W2067707952 cites W2021569306 @default.
- W2067707952 cites W2026219219 @default.
- W2067707952 cites W2027593354 @default.
- W2067707952 cites W2028216476 @default.
- W2067707952 cites W2042581501 @default.
- W2067707952 cites W2044915653 @default.
- W2067707952 cites W2048532212 @default.
- W2067707952 cites W2052500474 @default.
- W2067707952 cites W2054229447 @default.
- W2067707952 cites W2059433227 @default.
- W2067707952 cites W2063777508 @default.
- W2067707952 cites W2064454797 @default.
- W2067707952 cites W2073609557 @default.
- W2067707952 cites W2079887321 @default.
- W2067707952 cites W2087530895 @default.
- W2067707952 cites W2088821011 @default.
- W2067707952 cites W2136547252 @default.
- W2067707952 cites W2164628234 @default.
- W2067707952 cites W2256422229 @default.
- W2067707952 cites W3023435578 @default.
- W2067707952 cites W7826302 @default.
- W2067707952 doi "https://doi.org/10.1016/j.carbon.2013.10.032" @default.
- W2067707952 hasPublicationYear "2014" @default.
- W2067707952 type Work @default.
- W2067707952 sameAs 2067707952 @default.
- W2067707952 citedByCount "25" @default.
- W2067707952 countsByYear W20677079522014 @default.
- W2067707952 countsByYear W20677079522015 @default.
- W2067707952 countsByYear W20677079522016 @default.
- W2067707952 countsByYear W20677079522017 @default.
- W2067707952 countsByYear W20677079522018 @default.
- W2067707952 countsByYear W20677079522019 @default.
- W2067707952 countsByYear W20677079522020 @default.
- W2067707952 countsByYear W20677079522021 @default.
- W2067707952 countsByYear W20677079522022 @default.
- W2067707952 countsByYear W20677079522023 @default.
- W2067707952 crossrefType "journal-article" @default.
- W2067707952 hasAuthorship W2067707952A5025743013 @default.
- W2067707952 hasAuthorship W2067707952A5041052057 @default.
- W2067707952 hasAuthorship W2067707952A5069392555 @default.
- W2067707952 hasConcept C113196181 @default.
- W2067707952 hasConcept C121332964 @default.
- W2067707952 hasConcept C127413603 @default.
- W2067707952 hasConcept C134018914 @default.
- W2067707952 hasConcept C13965031 @default.
- W2067707952 hasConcept C147789679 @default.
- W2067707952 hasConcept C159985019 @default.
- W2067707952 hasConcept C163258240 @default.
- W2067707952 hasConcept C17525397 @default.
- W2067707952 hasConcept C185592680 @default.
- W2067707952 hasConcept C192562407 @default.
- W2067707952 hasConcept C2778541603 @default.
- W2067707952 hasConcept C2779197387 @default.
- W2067707952 hasConcept C2779698641 @default.
- W2067707952 hasConcept C29452124 @default.
- W2067707952 hasConcept C42360764 @default.
- W2067707952 hasConcept C43617362 @default.
- W2067707952 hasConcept C54355233 @default.
- W2067707952 hasConcept C555008776 @default.
- W2067707952 hasConcept C62520636 @default.
- W2067707952 hasConcept C68801617 @default.
- W2067707952 hasConcept C69357855 @default.
- W2067707952 hasConcept C71924100 @default.
- W2067707952 hasConcept C86803240 @default.
- W2067707952 hasConcept C89395315 @default.
- W2067707952 hasConcept C97355855 @default.
- W2067707952 hasConceptScore W2067707952C113196181 @default.
- W2067707952 hasConceptScore W2067707952C121332964 @default.
- W2067707952 hasConceptScore W2067707952C127413603 @default.
- W2067707952 hasConceptScore W2067707952C134018914 @default.
- W2067707952 hasConceptScore W2067707952C13965031 @default.