- W2067996907 abstract "Abstract The bearing strength of a blind riveted single lap joint of a carbon/epoxy composite after thermal exposure was studied. Considering the maximum service temperature based on material specifications and glass transition temperature, six types of specimens were prepared and tested in accordance with ASTM D5961. Failure loads of specimens exposed to a 177 °C environment were above 90% compared to sound specimens. Failure loads of 77% were obtained for specimens exposed to a 232 °C environment for 4 h. Bearing and rivet pulling-through failure modes were observed in all specimens. Delamination caused by degradation of the matrix property was found in specimens exposed to temperature higher than 204 °C." @default.
- W2067996907 created "2016-06-24" @default.
- W2067996907 creator A5017402344 @default.
- W2067996907 creator A5018549371 @default.
- W2067996907 creator A5043350940 @default.
- W2067996907 creator A5055247169 @default.
- W2067996907 creator A5064227856 @default.
- W2067996907 creator A5080160655 @default.
- W2067996907 creator A5081130563 @default.
- W2067996907 date "2008-11-01" @default.
- W2067996907 modified "2023-09-26" @default.
- W2067996907 title "An experimental study on the failure of carbon/epoxy single lap riveted joints after thermal exposure" @default.
- W2067996907 cites W1968410643 @default.
- W2067996907 cites W1971087819 @default.
- W2067996907 cites W1981630034 @default.
- W2067996907 cites W2006823230 @default.
- W2067996907 cites W2015986445 @default.
- W2067996907 cites W2018454062 @default.
- W2067996907 cites W2026405566 @default.
- W2067996907 cites W2038562307 @default.
- W2067996907 cites W2041353542 @default.
- W2067996907 cites W2047482955 @default.
- W2067996907 cites W2087898832 @default.
- W2067996907 cites W2162655237 @default.
- W2067996907 doi "https://doi.org/10.1016/j.compstruct.2008.03.029" @default.
- W2067996907 hasPublicationYear "2008" @default.
- W2067996907 type Work @default.
- W2067996907 sameAs 2067996907 @default.
- W2067996907 citedByCount "23" @default.
- W2067996907 countsByYear W20679969072012 @default.
- W2067996907 countsByYear W20679969072013 @default.
- W2067996907 countsByYear W20679969072014 @default.
- W2067996907 countsByYear W20679969072015 @default.
- W2067996907 countsByYear W20679969072016 @default.
- W2067996907 countsByYear W20679969072017 @default.
- W2067996907 countsByYear W20679969072018 @default.
- W2067996907 countsByYear W20679969072019 @default.
- W2067996907 countsByYear W20679969072021 @default.
- W2067996907 countsByYear W20679969072022 @default.
- W2067996907 countsByYear W20679969072023 @default.
- W2067996907 crossrefType "journal-article" @default.
- W2067996907 hasAuthorship W2067996907A5017402344 @default.
- W2067996907 hasAuthorship W2067996907A5018549371 @default.
- W2067996907 hasAuthorship W2067996907A5043350940 @default.
- W2067996907 hasAuthorship W2067996907A5055247169 @default.
- W2067996907 hasAuthorship W2067996907A5064227856 @default.
- W2067996907 hasAuthorship W2067996907A5080160655 @default.
- W2067996907 hasAuthorship W2067996907A5081130563 @default.
- W2067996907 hasConcept C104779481 @default.
- W2067996907 hasConcept C121332964 @default.
- W2067996907 hasConcept C127413603 @default.
- W2067996907 hasConcept C140205800 @default.
- W2067996907 hasConcept C153294291 @default.
- W2067996907 hasConcept C159985019 @default.
- W2067996907 hasConcept C166595027 @default.
- W2067996907 hasConcept C185324459 @default.
- W2067996907 hasConcept C192562407 @default.
- W2067996907 hasConcept C204530211 @default.
- W2067996907 hasConcept C66938386 @default.
- W2067996907 hasConcept C77595967 @default.
- W2067996907 hasConceptScore W2067996907C104779481 @default.
- W2067996907 hasConceptScore W2067996907C121332964 @default.
- W2067996907 hasConceptScore W2067996907C127413603 @default.
- W2067996907 hasConceptScore W2067996907C140205800 @default.
- W2067996907 hasConceptScore W2067996907C153294291 @default.
- W2067996907 hasConceptScore W2067996907C159985019 @default.
- W2067996907 hasConceptScore W2067996907C166595027 @default.
- W2067996907 hasConceptScore W2067996907C185324459 @default.
- W2067996907 hasConceptScore W2067996907C192562407 @default.
- W2067996907 hasConceptScore W2067996907C204530211 @default.
- W2067996907 hasConceptScore W2067996907C66938386 @default.
- W2067996907 hasConceptScore W2067996907C77595967 @default.
- W2067996907 hasIssue "1-3" @default.
- W2067996907 hasLocation W20679969071 @default.
- W2067996907 hasOpenAccess W2067996907 @default.
- W2067996907 hasPrimaryLocation W20679969071 @default.
- W2067996907 hasRelatedWork W1995958177 @default.
- W2067996907 hasRelatedWork W2047989554 @default.
- W2067996907 hasRelatedWork W2068647851 @default.
- W2067996907 hasRelatedWork W2087017819 @default.
- W2067996907 hasRelatedWork W2092814777 @default.
- W2067996907 hasRelatedWork W2316261790 @default.
- W2067996907 hasRelatedWork W2593200884 @default.
- W2067996907 hasRelatedWork W2738530155 @default.
- W2067996907 hasRelatedWork W2791920325 @default.
- W2067996907 hasRelatedWork W3127421527 @default.
- W2067996907 hasVolume "86" @default.
- W2067996907 isParatext "false" @default.
- W2067996907 isRetracted "false" @default.
- W2067996907 magId "2067996907" @default.
- W2067996907 workType "article" @default.