- W2070603194 abstract "Aluminum doped zinc oxide (ZnO:Al) thin films were deposited on soda-lime glass substrates by the chemical spray technique. The atomization of the solution was carried out by ultrasonic excitation. Six different starting solutions from both unmilled and milled Zn and Al precursors, dissolved in a mix of methanol and acetic acid, were prepared. The milling process was carried out using a planetary ball mill at a speed of 300 rpm, and different milling times, namely, 15, 25, 35, 45, and 60 min. Molar concentration, [Al]/[Zn] atomic ratio, deposition temperature and time, were kept at constant values; 0.2 M, 3 at.%, 475 °C, and 10 min, respectively. Results show that, under the same deposition conditions, electrical resistivities of ZnO:Al thin films deposited from milled precursors are lower than those obtained for films deposited from unmilled precursors. X-ray diffraction analysis revealed that all films display a polycrystalline structure, fitting well with the hexagonal wurtzite structure. Changes in surface morphology were observed by scanning electron microscopy (SEM) as well, since films deposited from unmilled precursors show triangular shaped grains, in contrast to films deposited from 15 and 35 min milled precursors that display thin slices with hexagonal shapes. The use of milled precursors to prepare starting solutions for depositing ZnO:Al thin films by ultrasonic pyrolysis influences their physical properties." @default.
- W2070603194 created "2016-06-24" @default.
- W2070603194 creator A5001509972 @default.
- W2070603194 creator A5017662532 @default.
- W2070603194 creator A5037818583 @default.
- W2070603194 creator A5049687965 @default.
- W2070603194 creator A5058174441 @default.
- W2070603194 creator A5075404066 @default.
- W2070603194 creator A5076593395 @default.
- W2070603194 date "2012-08-16" @default.
- W2070603194 modified "2023-09-27" @default.
- W2070603194 title "Effect of the Milling Time of the Precursors on the Physical Properties of Sprayed Aluminum-Doped Zinc Oxide (ZnO:Al) Thin Films" @default.
- W2070603194 cites W1662279726 @default.
- W2070603194 cites W1989183348 @default.
- W2070603194 cites W1999105847 @default.
- W2070603194 cites W2009483320 @default.
- W2070603194 cites W2059311510 @default.
- W2070603194 cites W2066995108 @default.
- W2070603194 cites W2070023439 @default.
- W2070603194 cites W2077990740 @default.
- W2070603194 cites W2087896447 @default.
- W2070603194 cites W2105749082 @default.
- W2070603194 cites W2119294367 @default.
- W2070603194 cites W2154513850 @default.
- W2070603194 cites W2156344543 @default.
- W2070603194 cites W4210978293 @default.
- W2070603194 doi "https://doi.org/10.3390/ma5081404" @default.
- W2070603194 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/5448938" @default.
- W2070603194 hasPublicationYear "2012" @default.
- W2070603194 type Work @default.
- W2070603194 sameAs 2070603194 @default.
- W2070603194 citedByCount "7" @default.
- W2070603194 countsByYear W20706031942014 @default.
- W2070603194 countsByYear W20706031942016 @default.
- W2070603194 countsByYear W20706031942018 @default.
- W2070603194 countsByYear W20706031942020 @default.
- W2070603194 countsByYear W20706031942022 @default.
- W2070603194 countsByYear W20706031942023 @default.
- W2070603194 crossrefType "journal-article" @default.
- W2070603194 hasAuthorship W2070603194A5001509972 @default.
- W2070603194 hasAuthorship W2070603194A5017662532 @default.
- W2070603194 hasAuthorship W2070603194A5037818583 @default.
- W2070603194 hasAuthorship W2070603194A5049687965 @default.
- W2070603194 hasAuthorship W2070603194A5058174441 @default.
- W2070603194 hasAuthorship W2070603194A5075404066 @default.
- W2070603194 hasAuthorship W2070603194A5076593395 @default.
- W2070603194 hasBestOaLocation W20706031941 @default.
- W2070603194 hasConcept C113196181 @default.
- W2070603194 hasConcept C127413603 @default.
- W2070603194 hasConcept C137637335 @default.
- W2070603194 hasConcept C159985019 @default.
- W2070603194 hasConcept C171250308 @default.
- W2070603194 hasConcept C178790620 @default.
- W2070603194 hasConcept C185592680 @default.
- W2070603194 hasConcept C19067145 @default.
- W2070603194 hasConcept C191897082 @default.
- W2070603194 hasConcept C192562407 @default.
- W2070603194 hasConcept C26771246 @default.
- W2070603194 hasConcept C3045981 @default.
- W2070603194 hasConcept C42360764 @default.
- W2070603194 hasConcept C535196362 @default.
- W2070603194 hasConceptScore W2070603194C113196181 @default.
- W2070603194 hasConceptScore W2070603194C127413603 @default.
- W2070603194 hasConceptScore W2070603194C137637335 @default.
- W2070603194 hasConceptScore W2070603194C159985019 @default.
- W2070603194 hasConceptScore W2070603194C171250308 @default.
- W2070603194 hasConceptScore W2070603194C178790620 @default.
- W2070603194 hasConceptScore W2070603194C185592680 @default.
- W2070603194 hasConceptScore W2070603194C19067145 @default.
- W2070603194 hasConceptScore W2070603194C191897082 @default.
- W2070603194 hasConceptScore W2070603194C192562407 @default.
- W2070603194 hasConceptScore W2070603194C26771246 @default.
- W2070603194 hasConceptScore W2070603194C3045981 @default.
- W2070603194 hasConceptScore W2070603194C42360764 @default.
- W2070603194 hasConceptScore W2070603194C535196362 @default.
- W2070603194 hasIssue "8" @default.
- W2070603194 hasLocation W20706031941 @default.
- W2070603194 hasLocation W20706031942 @default.
- W2070603194 hasOpenAccess W2070603194 @default.
- W2070603194 hasPrimaryLocation W20706031941 @default.
- W2070603194 hasRelatedWork W1977590682 @default.
- W2070603194 hasRelatedWork W2001710938 @default.
- W2070603194 hasRelatedWork W2079907008 @default.
- W2070603194 hasRelatedWork W2340582311 @default.
- W2070603194 hasRelatedWork W2380683956 @default.
- W2070603194 hasRelatedWork W2560643093 @default.
- W2070603194 hasRelatedWork W2900851969 @default.
- W2070603194 hasRelatedWork W3020987970 @default.
- W2070603194 hasRelatedWork W3135628771 @default.
- W2070603194 hasRelatedWork W4289889336 @default.
- W2070603194 hasVolume "5" @default.
- W2070603194 isParatext "false" @default.
- W2070603194 isRetracted "false" @default.
- W2070603194 magId "2070603194" @default.
- W2070603194 workType "article" @default.