• W2072385008 abstract "Two distinct hardening stages were observed in niobium irradiated at 25°C to 1018 cm−2 with Be(d.n) neutrons and 16 MeV protons. The low fluence stage persisted to a fluence of 5 × 1017 cm−2 and was attributed to impurity atom-point defect complexes. The higher fluence stage had a square root fluence dependence which was attributed to point defect clusters with a barrier strength, β of 4–7 for both 14 MeV neutron and 16 MeV proton irradiated niobium. Protons induced 1.6 times more hardening than Be(d.n) neutrons in the low fluence hardening stage. Nous avons observé deux stades distincts de durcissement dans le niobium irradié à 25 :C. jusqu'à 1018cm−2 avec des neutrons Be(d.n) et des protons de 16 MeV. Le stade de faible fluence se poursuivait jusqu'à une fluence de 5 × 1017cm−2 et nous l'avons attribué à des complexes entre un atome d'impureté et un défaut ponctuel. Le stade de fluence plus élevée variait en fonction de la racine carrée de la fluence. ce que nous avons attribué à des amas de défauts ponctuels dont la force de barrière était comprise entre 4 et 7 pour le niobium irradié tant avec des neutrons de 14 MeV qu'avec des protons de 16 MeV. Les protons produisaient un durcissement 1.6 fois plus grand que les neutrons Be(d.n). dans le stade de durcissement de fluence faible. Niob, welches bei 25°C mit bis zu 1018cm−2 Neutronen Be(d.n) oder Protonen (16 MeV) bestrahlt worden ist, weist zwei deutliche Bereiche der Bestrahlungsverfestigung auf. Der Bereich bei kleiner Dosis reicht bis zu einer Dosis von 5 × 1017cm−2 und wird der Wechselwirkung von Verunreinigungsatomen mit Punktdefektagglomeraten zugeschrieben. Der Bereich bei höherer Doses wiess eine Wurzelabhängigkeit auf und wurde Punktdefektagglomeraten mit einer Barrierenstärke β von 4–7 für beide Bestrahlungsarten zugeschrieben. Protonen verfestigten 1,6-mal stärker im Bereich niedriger Dosis als die 14 MeV-Neutronen." @default.
• W2072385008 created "2016-06-24" @default.
• W2072385008 creator A5016560617 @default.
• W2072385008 creator A5024831104 @default.
• W2072385008 creator A5075197786 @default.
• W2072385008 date "1982-07-01" @default.
• W2072385008 modified "2023-09-28" @default.
• W2072385008 title "Hardening stages in niobium irradiated with 14 MeV neutrons and 16 MeV protons" @default.
• W2072385008 cites W1038209357 @default.
• W2072385008 cites W1978413381 @default.
• W2072385008 cites W1999993252 @default.
• W2072385008 cites W2015606063 @default.
• W2072385008 cites W2022338654 @default.
• W2072385008 cites W2036627683 @default.
• W2072385008 cites W2050898875 @default.
• W2072385008 cites W2061243181 @default.
• W2072385008 cites W2064744214 @default.
• W2072385008 cites W2067709539 @default.
• W2072385008 cites W2068858045 @default.
• W2072385008 cites W2073814746 @default.
• W2072385008 cites W2080539401 @default.
• W2072385008 cites W2089970845 @default.
• W2072385008 cites W2103350462 @default.
• W2072385008 doi "https://doi.org/10.1016/0001-6160(82)90162-6" @default.
• W2072385008 hasPublicationYear "1982" @default.
• W2072385008 type Work @default.
• W2072385008 sameAs 2072385008 @default.
• W2072385008 citedByCount "4" @default.
• W2072385008 crossrefType "journal-article" @default.
• W2072385008 hasAuthorship W2072385008A5016560617 @default.
• W2072385008 hasAuthorship W2072385008A5024831104 @default.
• W2072385008 hasAuthorship W2072385008A5075197786 @default.
• W2072385008 hasConcept C111337013 @default.
• W2072385008 hasConcept C121332964 @default.
• W2072385008 hasConcept C152568617 @default.
• W2072385008 hasConcept C185544564 @default.
• W2072385008 hasConcept C191897082 @default.
• W2072385008 hasConcept C192562407 @default.
• W2072385008 hasConcept C22078206 @default.
• W2072385008 hasConcept C507968137 @default.
• W2072385008 hasConcept C54516573 @default.
• W2072385008 hasConcept C81988546 @default.
• W2072385008 hasConceptScore W2072385008C111337013 @default.
• W2072385008 hasConceptScore W2072385008C121332964 @default.
• W2072385008 hasConceptScore W2072385008C152568617 @default.
• W2072385008 hasConceptScore W2072385008C185544564 @default.
• W2072385008 hasConceptScore W2072385008C191897082 @default.
• W2072385008 hasConceptScore W2072385008C192562407 @default.
• W2072385008 hasConceptScore W2072385008C22078206 @default.
• W2072385008 hasConceptScore W2072385008C507968137 @default.
• W2072385008 hasConceptScore W2072385008C54516573 @default.
• W2072385008 hasConceptScore W2072385008C81988546 @default.
• W2072385008 hasIssue "7" @default.
• W2072385008 hasLocation W20723850081 @default.
• W2072385008 hasOpenAccess W2072385008 @default.
• W2072385008 hasPrimaryLocation W20723850081 @default.
• W2072385008 hasRelatedWork W1047906341 @default.
• W2072385008 hasRelatedWork W1974435746 @default.
• W2072385008 hasRelatedWork W1981284082 @default.
• W2072385008 hasRelatedWork W2016443595 @default.
• W2072385008 hasRelatedWork W2017633453 @default.
• W2072385008 hasRelatedWork W2085551008 @default.
• W2072385008 hasRelatedWork W2268316218 @default.
• W2072385008 hasRelatedWork W2359455641 @default.
• W2072385008 hasRelatedWork W2394392068 @default.
• W2072385008 hasRelatedWork W2473625511 @default.
• W2072385008 hasVolume "30" @default.
• W2072385008 isParatext "false" @default.
• W2072385008 isRetracted "false" @default.
• W2072385008 magId "2072385008" @default.
• W2072385008 workType "article" @default.