- W2072406593 abstract "High resolution transmission electron microscopy (HRTEM) was used to study the morphology of ultralow-density transparent condensed-silica (CS) aerogels. Silica aerogels were synthesized by two slightly different two-step polymerization processes and they were supercritically dried in a high temperature autoclave. Aerogel CS1 had a density of 9 kg/m3 and a BET surface area of 574 m2/g; aerogel CS2 had a density of 30 kg/m3 and a specific surface area of 630 m2/g. Both samples were fractured, vertically replicated with 0.95 nm Pt-C and backed with approximately 12 nm of rotary evaporated carbon. The silica aerogel was then removed from the replica with dilute HF acid and the replicas were studied by HRTEM. The stereoscopic HRTEM images reveal that connectors in both CS aerogels are extended filaments which resemble bottlebrushes, having microporosity. This morphology results from side-chain formation on a nearly linear CS stem. The slightly different chemistry leads to different morphologies for the two aerogels. For CS1, the connectors between stems have diameters ranging from 1.7 to 14.2 nm with an average of 6.4 ± 0.5 nm and connector lengths averaged 62 ± 21 nm with some as long as 132 nm. Pore sizes ranged from 13 to 240 nm with an average of 74 ± 43 nm. The pores were slightly larger than those in CS2 which ranged from 12 to 277 nm and averaged 61 ± 56 nm. For CS2, the connectors had diameters ranging from 1.5 to 16.5 nm and averaging 9.7 ± 0.5 nm. The connector lengths in the CS2 aerogel averaged 58 ± 27 nm with some as long as 127 nm. The connector diameters in CS2 (9.7 ± 0.5 nm) were the only important aerogel feature significantly different and greater than those in CS1 (6.4 ± 0.5 nm). The CS1 and CS2 connectors had side-chain diameters of 2 ± 0.7 and 0.95 ± 0.5 nm, respectively, and a similar microporosity of approximately 2.0 ± 1 nm." @default.
- W2072406593 created "2016-06-24" @default.
- W2072406593 creator A5040509817 @default.
- W2072406593 creator A5057651809 @default.
- W2072406593 creator A5061748601 @default.
- W2072406593 date "1995-06-01" @default.
- W2072406593 modified "2023-09-27" @default.
- W2072406593 title "High resolution transmission electron microscopy nanostructure of condensed-silica aerogels" @default.
- W2072406593 cites W1966177403 @default.
- W2072406593 cites W2026231468 @default.
- W2072406593 cites W2026352002 @default.
- W2072406593 cites W2027442857 @default.
- W2072406593 cites W2041387083 @default.
- W2072406593 doi "https://doi.org/10.1016/0022-3093(95)00083-6" @default.
- W2072406593 hasPublicationYear "1995" @default.
- W2072406593 type Work @default.
- W2072406593 sameAs 2072406593 @default.
- W2072406593 citedByCount "33" @default.
- W2072406593 countsByYear W20724065932013 @default.
- W2072406593 countsByYear W20724065932022 @default.
- W2072406593 crossrefType "journal-article" @default.
- W2072406593 hasAuthorship W2072406593A5040509817 @default.
- W2072406593 hasAuthorship W2072406593A5057651809 @default.
- W2072406593 hasAuthorship W2072406593A5061748601 @default.
- W2072406593 hasBestOaLocation W20724065931 @default.
- W2072406593 hasConcept C127413603 @default.
- W2072406593 hasConcept C138268822 @default.
- W2072406593 hasConcept C146088050 @default.
- W2072406593 hasConcept C154945302 @default.
- W2072406593 hasConcept C159985019 @default.
- W2072406593 hasConcept C161368742 @default.
- W2072406593 hasConcept C171250308 @default.
- W2072406593 hasConcept C186187911 @default.
- W2072406593 hasConcept C192562407 @default.
- W2072406593 hasConcept C2780012831 @default.
- W2072406593 hasConcept C41008148 @default.
- W2072406593 hasConcept C42360764 @default.
- W2072406593 hasConcept C44228677 @default.
- W2072406593 hasConcept C521977710 @default.
- W2072406593 hasConceptScore W2072406593C127413603 @default.
- W2072406593 hasConceptScore W2072406593C138268822 @default.
- W2072406593 hasConceptScore W2072406593C146088050 @default.
- W2072406593 hasConceptScore W2072406593C154945302 @default.
- W2072406593 hasConceptScore W2072406593C159985019 @default.
- W2072406593 hasConceptScore W2072406593C161368742 @default.
- W2072406593 hasConceptScore W2072406593C171250308 @default.
- W2072406593 hasConceptScore W2072406593C186187911 @default.
- W2072406593 hasConceptScore W2072406593C192562407 @default.
- W2072406593 hasConceptScore W2072406593C2780012831 @default.
- W2072406593 hasConceptScore W2072406593C41008148 @default.
- W2072406593 hasConceptScore W2072406593C42360764 @default.
- W2072406593 hasConceptScore W2072406593C44228677 @default.
- W2072406593 hasConceptScore W2072406593C521977710 @default.
- W2072406593 hasLocation W20724065931 @default.
- W2072406593 hasOpenAccess W2072406593 @default.
- W2072406593 hasPrimaryLocation W20724065931 @default.
- W2072406593 hasRelatedWork W1966007651 @default.
- W2072406593 hasRelatedWork W1981048778 @default.
- W2072406593 hasRelatedWork W2011115721 @default.
- W2072406593 hasRelatedWork W2023463640 @default.
- W2072406593 hasRelatedWork W2040612319 @default.
- W2072406593 hasRelatedWork W2050913572 @default.
- W2072406593 hasRelatedWork W2145886304 @default.
- W2072406593 hasRelatedWork W2390567448 @default.
- W2072406593 hasRelatedWork W2392263473 @default.
- W2072406593 hasRelatedWork W2950695928 @default.
- W2072406593 hasVolume "186" @default.
- W2072406593 isParatext "false" @default.
- W2072406593 isRetracted "false" @default.
- W2072406593 magId "2072406593" @default.
- W2072406593 workType "article" @default.