• W2072582194 abstract "The microstructure evolution in the course of crystallization of a splat-quenched Fe73,5Si13.5B9Nb3Cu1 amorphous alloy was investigated by atom probe field ion microscopy (APFIM) and high resolution transmission electron microscopy (HRTEM). All the alloying elements were found to be distributed homogeneously as an amorphous solid solution in the as-quenched state. At an initial stage of annealing, a concentration fluctuation of Cu was found to occur. Cu formed clusters of a few nanometer diameter and their composition was found to be approximately 30 at.% Cu at the beginning. In the later stage, a b.c.c. FeSi solid solution and the B and Nb enriched amorphous phase with the smaller Si content were found to coexist. In addition to these two phases, Cu enriched particles containing approximately 60 at.% Cu were found to be present in the intergranular regions, although we were not successful yet to determine whether this was a crystalline or amorphous phase. Based on these observations, we discuss the crystallization process of this alloy at 550°C which leads to the emergence of excellent soft magnetic properties. On étudie par microscopie ionique à émission de champ et sonde atomique et par microscopie électronique en haute résolution, l'évolution de la microstructure au cours de la cristallisation d'un alliage amorphe Fe73.5Si13.5B9Nb3Cu1 trempé entre pistons. On trouve que tons les éléments d'alliage sont répartis d'une manière homogène en une solution solide amorphe à l'état brut de trempe. Au début du recuit, on trouve qu'une fluctuation de concentration de cuivre se produit. Le cuivre forme des amas de quelques nanomètres de diamètre dont la composition est d'environ 30 at.% Cu au début. A l'étape finale, on trouve qu'une solution solide c.c. FeSi et la phase amorphe enrichie en niobium et en bore avec une faible teneur en silicium coexistent. En plus de cas deux phases, des particules enrichies en cuivre contenant environ 60 at.% Cu sont observees dans les régions intergranulaires, bien que l'on n'ait pas réussi encore à déterminer s'il s'agit d'une phase cristallisee ou amorphe. En se basant sur ces observations, on discute le mécanisme de cristallisation de cet alliage à 550°C, mecanisme qui conduit à l'apparition d'excellentes propriétés magnétiques douces. Die Entwicklung der Mikrostruktur im Verlauf der Kristallisation der spritzabgeschreckten amorphen Legierungen Fe73.5Si13.5B9Nb3Cu1 wird mit Atomsonde und hochauflösender Durchstrahlungselektronenmikroskopie untersucht. Sämtliche Legierungselemente sind in der Art einer festen Lösung in dem abgeschreckten Material homogen verteilt. Zu Beginn des Ausheilens tritt eine Fluktuation in der Kupferkonzentration auf. Cu-Cluster mit einigen wenigen Nanometer Durchmesser bilden sich; deren Zusammensetzung beträgt zu Beginn etwa 30 At.% Cu. In einem späteren Stadium finden sich koexistierend ein k.r.z. FeSi-Mischkristall und die mit B und Ni angereicherte amorphe Phase, die einen kleineren Si-Gehalt aufweist. Zusätzlich zu diesen beiden Phasen werden Cu-reiche Teilchen mit etwa 60 At.% Cu in den intergranularen Bereichen gefunden; allerdings konnten wir bisher nicht bestimmen, ob diese Phase kristallin oder amorph ist. Anhand dieser Beobachtungen diskutieren wir den Kristallisationsprozeβ dieser Legierung bei 550°C, welcher zum Auftreten ausgezeichneter weichmagnetischer Eigenschaften führt." @default.
• W2072582194 created "2016-06-24" @default.
• W2072582194 creator A5006274503 @default.
• W2072582194 creator A5008412118 @default.
• W2072582194 creator A5009222196 @default.
• W2072582194 creator A5009666612 @default.
• W2072582194 creator A5026898221 @default.
• W2072582194 date "1992-09-01" @default.
• W2072582194 modified "2023-09-29" @default.
• W2072582194 title "The microstructure evolution of a Fe73.5Si13.5B9Nb3Cu1 nanocrystalline soft magnetic material" @default.
• W2072582194 cites W1508238136 @default.
• W2072582194 cites W1975738704 @default.
• W2072582194 cites W1980000935 @default.
• W2072582194 cites W1990341574 @default.
• W2072582194 cites W1997649662 @default.
• W2072582194 cites W2005858960 @default.
• W2072582194 cites W2020883157 @default.
• W2072582194 cites W2063673661 @default.
• W2072582194 cites W2072136467 @default.
• W2072582194 cites W2118539261 @default.
• W2072582194 doi "https://doi.org/10.1016/0956-7151(92)90131-w" @default.
• W2072582194 hasPublicationYear "1992" @default.
• W2072582194 type Work @default.
• W2072582194 sameAs 2072582194 @default.
• W2072582194 citedByCount "318" @default.
• W2072582194 countsByYear W20725821942012 @default.
• W2072582194 countsByYear W20725821942013 @default.
• W2072582194 countsByYear W20725821942014 @default.
• W2072582194 countsByYear W20725821942015 @default.
• W2072582194 countsByYear W20725821942016 @default.
• W2072582194 countsByYear W20725821942017 @default.
• W2072582194 countsByYear W20725821942018 @default.
• W2072582194 countsByYear W20725821942019 @default.
• W2072582194 countsByYear W20725821942020 @default.
• W2072582194 countsByYear W20725821942021 @default.
• W2072582194 countsByYear W20725821942022 @default.
• W2072582194 countsByYear W20725821942023 @default.
• W2072582194 crossrefType "journal-article" @default.
• W2072582194 hasAuthorship W2072582194A5006274503 @default.
• W2072582194 hasAuthorship W2072582194A5008412118 @default.
• W2072582194 hasAuthorship W2072582194A5009222196 @default.
• W2072582194 hasAuthorship W2072582194A5009666612 @default.
• W2072582194 hasAuthorship W2072582194A5026898221 @default.
• W2072582194 hasConcept C123266363 @default.
• W2072582194 hasConcept C127413603 @default.
• W2072582194 hasConcept C140676511 @default.
• W2072582194 hasConcept C146088050 @default.
• W2072582194 hasConcept C161368742 @default.
• W2072582194 hasConcept C16876290 @default.
• W2072582194 hasConcept C171250308 @default.
• W2072582194 hasConcept C175854130 @default.
• W2072582194 hasConcept C185592680 @default.
• W2072582194 hasConcept C191897082 @default.
• W2072582194 hasConcept C192562407 @default.
• W2072582194 hasConcept C203036418 @default.
• W2072582194 hasConcept C2777855556 @default.
• W2072582194 hasConcept C2780026712 @default.
• W2072582194 hasConcept C42360764 @default.
• W2072582194 hasConcept C56052488 @default.
• W2072582194 hasConcept C8010536 @default.
• W2072582194 hasConcept C87976508 @default.
• W2072582194 hasConceptScore W2072582194C123266363 @default.
• W2072582194 hasConceptScore W2072582194C127413603 @default.
• W2072582194 hasConceptScore W2072582194C140676511 @default.
• W2072582194 hasConceptScore W2072582194C146088050 @default.
• W2072582194 hasConceptScore W2072582194C161368742 @default.
• W2072582194 hasConceptScore W2072582194C16876290 @default.
• W2072582194 hasConceptScore W2072582194C171250308 @default.
• W2072582194 hasConceptScore W2072582194C175854130 @default.
• W2072582194 hasConceptScore W2072582194C185592680 @default.
• W2072582194 hasConceptScore W2072582194C191897082 @default.
• W2072582194 hasConceptScore W2072582194C192562407 @default.
• W2072582194 hasConceptScore W2072582194C203036418 @default.
• W2072582194 hasConceptScore W2072582194C2777855556 @default.
• W2072582194 hasConceptScore W2072582194C2780026712 @default.
• W2072582194 hasConceptScore W2072582194C42360764 @default.
• W2072582194 hasConceptScore W2072582194C56052488 @default.
• W2072582194 hasConceptScore W2072582194C8010536 @default.
• W2072582194 hasConceptScore W2072582194C87976508 @default.
• W2072582194 hasIssue "9" @default.
• W2072582194 hasLocation W20725821941 @default.
• W2072582194 hasOpenAccess W2072582194 @default.
• W2072582194 hasPrimaryLocation W20725821941 @default.
• W2072582194 hasRelatedWork W1619015128 @default.
• W2072582194 hasRelatedWork W1968678550 @default.
• W2072582194 hasRelatedWork W1968854389 @default.
• W2072582194 hasRelatedWork W1983193014 @default.
• W2072582194 hasRelatedWork W1997351886 @default.
• W2072582194 hasRelatedWork W2033004232 @default.
• W2072582194 hasRelatedWork W2076395637 @default.
• W2072582194 hasRelatedWork W2382063843 @default.
• W2072582194 hasRelatedWork W2537003350 @default.
• W2072582194 hasRelatedWork W2562599428 @default.
• W2072582194 hasVolume "40" @default.
• W2072582194 isParatext "false" @default.
• W2072582194 isRetracted "false" @default.
• W2072582194 magId "2072582194" @default.
• W2072582194 workType "article" @default.