- W2072616673 abstract "The aim of this article is to study the growth rate of intermetallic compounds at the interface of cold roll bonded Al/Cu bimetal at 250°C and compare the results with a similar study performed on friction welding of Al to Cu. Samples of tri-layered Cu–Al–Cu composite were produced by the cold roll welding process and heat treated at constant temperature of 250°C for 1 to 1000 h. The thickness, morphology and composition of the intermetallic compound at the interface of Cu and Al were studied by optical and scanning electron microscope and EDX analyzer. The presence of various intermetallic compounds (Cu3Al, Cu4Al3, CuAl and CuAl2) was detected and the priority of formation of each compound was studied. The bond strength and electrical resistivity of different samples were measured by peeling test and a high precision micro-ohmmeter, respectively. The variations of resistivity and bond strength versus thickness of intermetallic compound were plotted. It was observed that the strength and electrical conductivity are greatly reduced by increasing the thickness of intermetallic compounds. Moreover, the growth rate of intermetallic compounds in roll welded bimetal composite is lower compared with that reported for similar friction welded specimens." @default.
- W2072616673 created "2016-06-24" @default.
- W2072616673 creator A5028213612 @default.
- W2072616673 creator A5044089791 @default.
- W2072616673 creator A5082758326 @default.
- W2072616673 date "2001-04-01" @default.
- W2072616673 modified "2023-10-16" @default.
- W2072616673 title "Growth rate of intermetallic compounds in Al/Cu bimetal produced by cold roll welding process" @default.
- W2072616673 cites W2051054919 @default.
- W2072616673 doi "https://doi.org/10.1016/s0925-8388(01)00872-6" @default.
- W2072616673 hasPublicationYear "2001" @default.
- W2072616673 type Work @default.
- W2072616673 sameAs 2072616673 @default.
- W2072616673 citedByCount "336" @default.
- W2072616673 countsByYear W20726166732012 @default.
- W2072616673 countsByYear W20726166732013 @default.
- W2072616673 countsByYear W20726166732014 @default.
- W2072616673 countsByYear W20726166732015 @default.
- W2072616673 countsByYear W20726166732016 @default.
- W2072616673 countsByYear W20726166732017 @default.
- W2072616673 countsByYear W20726166732018 @default.
- W2072616673 countsByYear W20726166732019 @default.
- W2072616673 countsByYear W20726166732020 @default.
- W2072616673 countsByYear W20726166732021 @default.
- W2072616673 countsByYear W20726166732022 @default.
- W2072616673 countsByYear W20726166732023 @default.
- W2072616673 crossrefType "journal-article" @default.
- W2072616673 hasAuthorship W2072616673A5028213612 @default.
- W2072616673 hasAuthorship W2072616673A5044089791 @default.
- W2072616673 hasAuthorship W2072616673A5082758326 @default.
- W2072616673 hasConcept C119599485 @default.
- W2072616673 hasConcept C127413603 @default.
- W2072616673 hasConcept C159985019 @default.
- W2072616673 hasConcept C191897082 @default.
- W2072616673 hasConcept C192562407 @default.
- W2072616673 hasConcept C19474535 @default.
- W2072616673 hasConcept C26771246 @default.
- W2072616673 hasConcept C27501479 @default.
- W2072616673 hasConcept C2780026712 @default.
- W2072616673 hasConcept C69990965 @default.
- W2072616673 hasConcept C74793105 @default.
- W2072616673 hasConceptScore W2072616673C119599485 @default.
- W2072616673 hasConceptScore W2072616673C127413603 @default.
- W2072616673 hasConceptScore W2072616673C159985019 @default.
- W2072616673 hasConceptScore W2072616673C191897082 @default.
- W2072616673 hasConceptScore W2072616673C192562407 @default.
- W2072616673 hasConceptScore W2072616673C19474535 @default.
- W2072616673 hasConceptScore W2072616673C26771246 @default.
- W2072616673 hasConceptScore W2072616673C27501479 @default.
- W2072616673 hasConceptScore W2072616673C2780026712 @default.
- W2072616673 hasConceptScore W2072616673C69990965 @default.
- W2072616673 hasConceptScore W2072616673C74793105 @default.
- W2072616673 hasIssue "1-2" @default.
- W2072616673 hasLocation W20726166731 @default.
- W2072616673 hasOpenAccess W2072616673 @default.
- W2072616673 hasPrimaryLocation W20726166731 @default.
- W2072616673 hasRelatedWork W2061542128 @default.
- W2072616673 hasRelatedWork W2062761185 @default.
- W2072616673 hasRelatedWork W2334256141 @default.
- W2072616673 hasRelatedWork W2349813156 @default.
- W2072616673 hasRelatedWork W2373318203 @default.
- W2072616673 hasRelatedWork W2393810422 @default.
- W2072616673 hasRelatedWork W2799532055 @default.
- W2072616673 hasRelatedWork W2950635310 @default.
- W2072616673 hasRelatedWork W2970344547 @default.
- W2072616673 hasRelatedWork W3158960024 @default.
- W2072616673 hasVolume "319" @default.
- W2072616673 isParatext "false" @default.
- W2072616673 isRetracted "false" @default.
- W2072616673 magId "2072616673" @default.
- W2072616673 workType "article" @default.