- W2073778345 abstract "Deposition mechanism of nano-structured ZnO films has been investigated in the absence and presence of chloride ions from aqueous solution. The resulting opto-electronic properties were interpreted extensively, using X-ray diffraction (XRD), X-ray Absorption Near Edge Spectroscopy (XANES), field emission scanning electron microscopy (FE-SEM), UV-Visible spectroscopy and four probe techniques. The ZnO deposition is mass transport controlled process and the interaction of chloride ions with the surface has great influence on diffusion kinetics, considering the substantial species (Zn2+ and OH−) involved in the construction of ZnO film. This effect does not change major lattice parameters, as shown with detailed analysis of XRD data. However, the texture coefficient (Tc) (0 0 2) value is higher in presence of chloride ions containing synthesis solution which gave vertically aligned, well defined and uniformly dispersed nanorods structure. The calculated Eg values are in the range 3.28–3.41 eV and 3.22–3.31 eV for ZnO nanorods and nanotowers synthesized at different deposition periods, respectively. Furthermore, the charge mobility values regarding the deposition periods were measured to be in the ranges from 130.4 to 449.2 cm2 V−1 s−1 and 126.2 to 204.7 cm2 V−1 s−1 for nanorods and nanotowers, respectively. From XANES results, it was shown that the Zn K-edge spectrum is dominated by the transition of Zn 1s core electrons into the unoccupied Zn 4p states of the conduction band. Comparing the rod and tower nano-structured ZnO thin films, the excitation behavior of valence band electrons is different. Moreover, the density states of Zn 4p are higher for ZnO nanorods." @default.
- W2073778345 created "2016-06-24" @default.
- W2073778345 creator A5023140563 @default.
- W2073778345 creator A5029050904 @default.
- W2073778345 creator A5049950170 @default.
- W2073778345 creator A5052162991 @default.
- W2073778345 creator A5071814946 @default.
- W2073778345 creator A5080807348 @default.
- W2073778345 date "2015-06-01" @default.
- W2073778345 modified "2023-09-25" @default.
- W2073778345 title "Electrosynthesis of ZnO nanorods and nanotowers: Morphology and X-ray Absorption Near Edge Spectroscopy studies" @default.
- W2073778345 cites W1966591473 @default.
- W2073778345 cites W1967652077 @default.
- W2073778345 cites W1971977630 @default.
- W2073778345 cites W1977465337 @default.
- W2073778345 cites W1978898149 @default.
- W2073778345 cites W1986263383 @default.
- W2073778345 cites W1992423898 @default.
- W2073778345 cites W2003135287 @default.
- W2073778345 cites W2003211648 @default.
- W2073778345 cites W2009752536 @default.
- W2073778345 cites W2014919042 @default.
- W2073778345 cites W2018374778 @default.
- W2073778345 cites W2020405765 @default.
- W2073778345 cites W2026190771 @default.
- W2073778345 cites W2038380406 @default.
- W2073778345 cites W2039880069 @default.
- W2073778345 cites W2044317465 @default.
- W2073778345 cites W2045960627 @default.
- W2073778345 cites W2055498968 @default.
- W2073778345 cites W2059223131 @default.
- W2073778345 cites W2060049125 @default.
- W2073778345 cites W2060707159 @default.
- W2073778345 cites W2068388534 @default.
- W2073778345 cites W2071357981 @default.
- W2073778345 cites W2071559674 @default.
- W2073778345 cites W2072846133 @default.
- W2073778345 cites W2072909732 @default.
- W2073778345 cites W2072980100 @default.
- W2073778345 cites W2074284827 @default.
- W2073778345 cites W2080089027 @default.
- W2073778345 cites W2081500083 @default.
- W2073778345 cites W2082846455 @default.
- W2073778345 cites W2085144708 @default.
- W2073778345 cites W2128410109 @default.
- W2073778345 cites W2139257718 @default.
- W2073778345 cites W2335742416 @default.
- W2073778345 cites W2062052541 @default.
- W2073778345 doi "https://doi.org/10.1016/j.apsusc.2015.02.166" @default.
- W2073778345 hasPublicationYear "2015" @default.
- W2073778345 type Work @default.
- W2073778345 sameAs 2073778345 @default.
- W2073778345 citedByCount "14" @default.
- W2073778345 countsByYear W20737783452015 @default.
- W2073778345 countsByYear W20737783452016 @default.
- W2073778345 countsByYear W20737783452017 @default.
- W2073778345 countsByYear W20737783452018 @default.
- W2073778345 countsByYear W20737783452019 @default.
- W2073778345 countsByYear W20737783452020 @default.
- W2073778345 countsByYear W20737783452021 @default.
- W2073778345 crossrefType "journal-article" @default.
- W2073778345 hasAuthorship W2073778345A5023140563 @default.
- W2073778345 hasAuthorship W2073778345A5029050904 @default.
- W2073778345 hasAuthorship W2073778345A5049950170 @default.
- W2073778345 hasAuthorship W2073778345A5052162991 @default.
- W2073778345 hasAuthorship W2073778345A5071814946 @default.
- W2073778345 hasAuthorship W2073778345A5080807348 @default.
- W2073778345 hasConcept C110715899 @default.
- W2073778345 hasConcept C113196181 @default.
- W2073778345 hasConcept C119824511 @default.
- W2073778345 hasConcept C120665830 @default.
- W2073778345 hasConcept C121332964 @default.
- W2073778345 hasConcept C126201875 @default.
- W2073778345 hasConcept C127413603 @default.
- W2073778345 hasConcept C159985019 @default.
- W2073778345 hasConcept C171250308 @default.
- W2073778345 hasConcept C175708663 @default.
- W2073778345 hasConcept C185592680 @default.
- W2073778345 hasConcept C192562407 @default.
- W2073778345 hasConcept C26771246 @default.
- W2073778345 hasConcept C32891209 @default.
- W2073778345 hasConcept C42360764 @default.
- W2073778345 hasConcept C43617362 @default.
- W2073778345 hasConcept C62520636 @default.
- W2073778345 hasConceptScore W2073778345C110715899 @default.
- W2073778345 hasConceptScore W2073778345C113196181 @default.
- W2073778345 hasConceptScore W2073778345C119824511 @default.
- W2073778345 hasConceptScore W2073778345C120665830 @default.
- W2073778345 hasConceptScore W2073778345C121332964 @default.
- W2073778345 hasConceptScore W2073778345C126201875 @default.
- W2073778345 hasConceptScore W2073778345C127413603 @default.
- W2073778345 hasConceptScore W2073778345C159985019 @default.
- W2073778345 hasConceptScore W2073778345C171250308 @default.
- W2073778345 hasConceptScore W2073778345C175708663 @default.
- W2073778345 hasConceptScore W2073778345C185592680 @default.
- W2073778345 hasConceptScore W2073778345C192562407 @default.
- W2073778345 hasConceptScore W2073778345C26771246 @default.
- W2073778345 hasConceptScore W2073778345C32891209 @default.