• W2074453436 abstract "Zirconia-toughened alumina (ZTA)/boron nitride (BN) machinable ceramics have been successfully fabricated by reactive hot pressing. BN was in-situ introduced into the composite by the reaction of aluminum nitride (AlN) and boric acid (H3BO3). The microstructure of ZTA/BN composite was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) techniques. The results indicated that BN grains were uniformly and compactly distributed among Al2O3 and ZrO2 grains. The relative density, flexural strength, fracture toughness, and Vickers hardness increased with increasing temperature. The flexural strength and fracture toughness of the ZTA/BN composite with BN content of 12.5 vol% sintered at 1800 °C achieved high values of 731 MPa and 7.48 MPa m1/2, respectively. These values were much higher than those of the composite with the same composition prepared by conventional powder sintering method, and even higher than those of the monolithic ZTA ceramics. The enhancements of the fracture strength and fracture toughness were primarily ascribed to the reactive hot pressing method which introduced BN in-situ and prevented the aggregation of BN and reduced the flaw sizes. The ZTA/BN composite exhibited excellent machinability and could be drilled using conventional cemented carbide drill bits." @default.
• W2074453436 created "2016-06-24" @default.
• W2074453436 creator A5009249883 @default.
• W2074453436 creator A5028161050 @default.
• W2074453436 creator A5033787604 @default.
• W2074453436 creator A5036284082 @default.
• W2074453436 creator A5051845910 @default.
• W2074453436 creator A5083067904 @default.
• W2074453436 creator A5085538549 @default.
• W2074453436 date "2015-02-01" @default.
• W2074453436 modified "2023-10-18" @default.
• W2074453436 title "Microstructure and mechanical properties of ZTA/BN machinable ceramics fabricated by reactive hot pressing" @default.
• W2074453436 cites W1978634913 @default.
• W2074453436 cites W1982159431 @default.
• W2074453436 cites W1993451610 @default.
• W2074453436 cites W1999462852 @default.
• W2074453436 cites W2000227514 @default.
• W2074453436 cites W2001992355 @default.
• W2074453436 cites W2006769480 @default.
• W2074453436 cites W2011682973 @default.
• W2074453436 cites W2012913375 @default.
• W2074453436 cites W2014204424 @default.
• W2074453436 cites W2042326979 @default.
• W2074453436 cites W2044391411 @default.
• W2074453436 cites W2045436962 @default.
• W2074453436 cites W2046996426 @default.
• W2074453436 cites W2052208263 @default.
• W2074453436 cites W2052971488 @default.
• W2074453436 cites W2057626782 @default.
• W2074453436 cites W2060513701 @default.
• W2074453436 cites W2060873453 @default.
• W2074453436 cites W2065972667 @default.
• W2074453436 cites W2070079038 @default.
• W2074453436 cites W2078157641 @default.
• W2074453436 cites W2083515848 @default.
• W2074453436 cites W2084306492 @default.
• W2074453436 cites W2103663100 @default.
• W2074453436 cites W2169531791 @default.
• W2074453436 doi "https://doi.org/10.1016/j.jeurceramsoc.2014.09.002" @default.
• W2074453436 hasPublicationYear "2015" @default.
• W2074453436 type Work @default.
• W2074453436 sameAs 2074453436 @default.
• W2074453436 citedByCount "21" @default.
• W2074453436 countsByYear W20744534362015 @default.
• W2074453436 countsByYear W20744534362016 @default.
• W2074453436 countsByYear W20744534362017 @default.
• W2074453436 countsByYear W20744534362018 @default.
• W2074453436 countsByYear W20744534362019 @default.
• W2074453436 countsByYear W20744534362020 @default.
• W2074453436 countsByYear W20744534362021 @default.
• W2074453436 countsByYear W20744534362022 @default.
• W2074453436 crossrefType "journal-article" @default.
• W2074453436 hasAuthorship W2074453436A5009249883 @default.
• W2074453436 hasAuthorship W2074453436A5028161050 @default.
• W2074453436 hasAuthorship W2074453436A5033787604 @default.
• W2074453436 hasAuthorship W2074453436A5036284082 @default.
• W2074453436 hasAuthorship W2074453436A5051845910 @default.
• W2074453436 hasAuthorship W2074453436A5083067904 @default.
• W2074453436 hasAuthorship W2074453436A5085538549 @default.
• W2074453436 hasConcept C104779481 @default.
• W2074453436 hasConcept C133392424 @default.
• W2074453436 hasConcept C134132462 @default.
• W2074453436 hasConcept C159985019 @default.
• W2074453436 hasConcept C178405089 @default.
• W2074453436 hasConcept C192562407 @default.
• W2074453436 hasConcept C26771246 @default.
• W2074453436 hasConcept C2776578615 @default.
• W2074453436 hasConcept C2777581544 @default.
• W2074453436 hasConcept C2778794521 @default.
• W2074453436 hasConcept C2780243435 @default.
• W2074453436 hasConcept C82455628 @default.
• W2074453436 hasConcept C87976508 @default.
• W2074453436 hasConcept C97549433 @default.
• W2074453436 hasConceptScore W2074453436C104779481 @default.
• W2074453436 hasConceptScore W2074453436C133392424 @default.
• W2074453436 hasConceptScore W2074453436C134132462 @default.
• W2074453436 hasConceptScore W2074453436C159985019 @default.
• W2074453436 hasConceptScore W2074453436C178405089 @default.
• W2074453436 hasConceptScore W2074453436C192562407 @default.
• W2074453436 hasConceptScore W2074453436C26771246 @default.
• W2074453436 hasConceptScore W2074453436C2776578615 @default.
• W2074453436 hasConceptScore W2074453436C2777581544 @default.
• W2074453436 hasConceptScore W2074453436C2778794521 @default.
• W2074453436 hasConceptScore W2074453436C2780243435 @default.
• W2074453436 hasConceptScore W2074453436C82455628 @default.
• W2074453436 hasConceptScore W2074453436C87976508 @default.
• W2074453436 hasConceptScore W2074453436C97549433 @default.
• W2074453436 hasFunder F4320321001 @default.
• W2074453436 hasFunder F4320321543 @default.
• W2074453436 hasIssue "2" @default.
• W2074453436 hasLocation W20744534361 @default.
• W2074453436 hasOpenAccess W2074453436 @default.
• W2074453436 hasPrimaryLocation W20744534361 @default.
• W2074453436 hasRelatedWork W1967579156 @default.
• W2074453436 hasRelatedWork W1978972422 @default.
• W2074453436 hasRelatedWork W2003154400 @default.
• W2074453436 hasRelatedWork W2007752935 @default.
• W2074453436 hasRelatedWork W2081889034 @default.

• next