- W2076140635 abstract "Thermo-chemical technique was used to synthesize Cu-Al2O3, nanocomposite powders. The process was carried out by addition of Cu powder to aqueous solution of aluminum nitrate. Afterwards, a thermal treatment at 850℃ for 1 hr was conducted to get insitu powders of CuO and stable alumina (Al2O3, ). The CuO was reduced in hydrogen atmosphere into copper powder. The nanocomposite powders of both copper and alumina were thoroughly mixed, cold pressed into briquettes and sintered at 850℃ in hydrogen atmosphere. The x-ray diffraction and scanning electron microscope (SEM) with energy dispersive spectrometer (EDS) were used to characterize the structure of the obtained powders. The results showed that alumina nanoparticles (20 nm) and ultra fine copper crystallite (200 nm) were obtained. SEM and EDS showed that the alumina particles were uniformly dispersed within the copper crystallite matrix. The structure also revealed formation of a third phase (CuAlO2) at copper-alumina interface. The hardness and density results showed that the gain in hardness was found to be dependent on the alumina contents rather than on the relative densities. The alumina content up to 12.5% resulted in an increase of 47.9% in hardness and slight decrease (7.6%) in relative densities. The results of compression tests showed considerable increase in compression strength (67%) as alumina content increased up to 12.5%. The compression strength showed further increase in compression strength (24%) as strain rates were increased from 10-4 s to 10s. Strain hardening and strain rate parameters “n” and “m” have shown positive values that improved the total strain and they can be used to predict formability of the nanocomposite." @default.
- W2076140635 created "2016-06-24" @default.
- W2076140635 creator A5042661951 @default.
- W2076140635 creator A5050714291 @default.
- W2076140635 creator A5060129075 @default.
- W2076140635 creator A5063778577 @default.
- W2076140635 date "2011-01-01" @default.
- W2076140635 modified "2023-10-16" @default.
- W2076140635 title "Preparation and Characteristics of Cu-Al<sub>2</sub>O<sub>3</sub> Nanocomposite" @default.
- W2076140635 cites W1971790265 @default.
- W2076140635 cites W1983025412 @default.
- W2076140635 cites W1983081829 @default.
- W2076140635 cites W1990742198 @default.
- W2076140635 cites W2039231646 @default.
- W2076140635 cites W2055379573 @default.
- W2076140635 cites W2062434333 @default.
- W2076140635 cites W2090407841 @default.
- W2076140635 cites W2091858186 @default.
- W2076140635 cites W2122708278 @default.
- W2076140635 cites W2137210592 @default.
- W2076140635 cites W2491058251 @default.
- W2076140635 doi "https://doi.org/10.4236/ojmetal.2011.12004" @default.
- W2076140635 hasPublicationYear "2011" @default.
- W2076140635 type Work @default.
- W2076140635 sameAs 2076140635 @default.
- W2076140635 citedByCount "47" @default.
- W2076140635 countsByYear W20761406352013 @default.
- W2076140635 countsByYear W20761406352015 @default.
- W2076140635 countsByYear W20761406352016 @default.
- W2076140635 countsByYear W20761406352017 @default.
- W2076140635 countsByYear W20761406352018 @default.
- W2076140635 countsByYear W20761406352019 @default.
- W2076140635 countsByYear W20761406352020 @default.
- W2076140635 countsByYear W20761406352021 @default.
- W2076140635 countsByYear W20761406352022 @default.
- W2076140635 countsByYear W20761406352023 @default.
- W2076140635 crossrefType "journal-article" @default.
- W2076140635 hasAuthorship W2076140635A5042661951 @default.
- W2076140635 hasAuthorship W2076140635A5050714291 @default.
- W2076140635 hasAuthorship W2076140635A5060129075 @default.
- W2076140635 hasAuthorship W2076140635A5063778577 @default.
- W2076140635 hasBestOaLocation W20761406351 @default.
- W2076140635 hasConcept C127413603 @default.
- W2076140635 hasConcept C137637335 @default.
- W2076140635 hasConcept C13965031 @default.
- W2076140635 hasConcept C159985019 @default.
- W2076140635 hasConcept C185592680 @default.
- W2076140635 hasConcept C191897082 @default.
- W2076140635 hasConcept C192562407 @default.
- W2076140635 hasConcept C26771246 @default.
- W2076140635 hasConcept C42360764 @default.
- W2076140635 hasConcept C544778455 @default.
- W2076140635 hasConcept C87976508 @default.
- W2076140635 hasConcept C92880739 @default.
- W2076140635 hasConceptScore W2076140635C127413603 @default.
- W2076140635 hasConceptScore W2076140635C137637335 @default.
- W2076140635 hasConceptScore W2076140635C13965031 @default.
- W2076140635 hasConceptScore W2076140635C159985019 @default.
- W2076140635 hasConceptScore W2076140635C185592680 @default.
- W2076140635 hasConceptScore W2076140635C191897082 @default.
- W2076140635 hasConceptScore W2076140635C192562407 @default.
- W2076140635 hasConceptScore W2076140635C26771246 @default.
- W2076140635 hasConceptScore W2076140635C42360764 @default.
- W2076140635 hasConceptScore W2076140635C544778455 @default.
- W2076140635 hasConceptScore W2076140635C87976508 @default.
- W2076140635 hasConceptScore W2076140635C92880739 @default.
- W2076140635 hasIssue "02" @default.
- W2076140635 hasLocation W20761406351 @default.
- W2076140635 hasOpenAccess W2076140635 @default.
- W2076140635 hasPrimaryLocation W20761406351 @default.
- W2076140635 hasRelatedWork W1483110363 @default.
- W2076140635 hasRelatedWork W2049757704 @default.
- W2076140635 hasRelatedWork W2058940780 @default.
- W2076140635 hasRelatedWork W2090404944 @default.
- W2076140635 hasRelatedWork W2326185588 @default.
- W2076140635 hasRelatedWork W2327828343 @default.
- W2076140635 hasRelatedWork W2355862987 @default.
- W2076140635 hasRelatedWork W2389009860 @default.
- W2076140635 hasRelatedWork W2468563442 @default.
- W2076140635 hasRelatedWork W3144433931 @default.
- W2076140635 hasVolume "01" @default.
- W2076140635 isParatext "false" @default.
- W2076140635 isRetracted "false" @default.
- W2076140635 magId "2076140635" @default.
- W2076140635 workType "article" @default.